Solidification mechanisms of unmodified and strontium-modified hypereutectic aluminium-silicon alloys

The effects of strontium on the solidi. cation mode of hypereutectic aluminium-silicon alloys have been studied. Samples were prepared from an aluminium-17wt% silicon-based alloy and strontium was added at several different concentrations. The development of the microstructure was investigated by cooling curve analysis, interrupted solidi. cation experiments and optical and scanning electron microscopy. It was found that nucleation of primary silicon is suppressed by additions of strontium. The suppressed nucleation results in supersaturation of the liquid prior to nucleation, and an increased growth rate after nucleation. As a result, the silicon crystals become less faceted and more dendritic with increasing strontium additions. Increasing the strontium concentration slightly refined the eutectic spacing and introduced a small amount of fibrous silicon. Electron back-scatter diffraction measurements were performed to determine the crystallographic relation between the primary and eutectic silicon phases. The eutectic silicon in the unmodified alloy does not have any crystallographic relationship with the primary silicon crystals. In contrast, the eutectic silicon crystals in the strontium-modified alloys often share an identical or twin relationship with nearby primary silicon crystals. The incidence of twinning within primary silicon crystals was relatively low and did not appear to increase with strontium additions.

Eutectic grains in unmodified and strontium-modified hypoeutectic aluminum-silicon alloys

Additions of strontium to hypoeutectic aluminum-silicon alloys modify the morphology of the eutectic silicon phase from a coarse platelike structure to a fine fibrous structure. Thermal analysis, interrupted solidification, and microstructural examination of sand castings in this work revealed that, in addition to a change in silicon morphology, modification with strontium also causes an increase in the size of eutectic grains. The eutectic grain size increases because fewer grains nucleate, possibly due to poisoning of the phosphorus-based nucleants, that are active in the unmodified alloy. A simple growth model is developed to estimate the interface velocity during solidification of a eutectic grain. The model confirms, independent of microstructural observations, that the addition of 100 ppm strontium increases the eutectic grain size by at least an order of magnitude compared with the equivalent unmodified alloy. The model predicts that the growth velocity varies significantly during eutectic growth. At low strontium levels, these variations may be sufficient to cause transitions between flake and fibrous silicon morphologies depending on the casting conditions. The model can be used to rationally interpret the eutectic grain structure and silicon morphology of fully solidified aluminum-silicon castings and, when coupled with reliable thermal data, can be used to estimate the eutectic grain size.

Native grain refinement of magnesium alloys

High purity Mg-Al type alloys have a naturally fine grain size compared to commercial purity alloys with the same basic composition. This is referred to as native grain refinement. It is shown that native grain refinement occurs only in magnesium alloys containing aluminium. The mechanism is attributed to the Al4C3 particles existing in these alloys. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Influence of calcium on the microstructure and properties of an Al-7Si-0.3Mg-xFe alloy

The effect of Ca addition on the microstructure, physical characteristics (density/porosity), and mechanical properties (tensile and impact strength) has been investigated in an Al-7Si-0.3Mg-xFe (x = 0.2, 0.4, and 0.7) alloy. The size of Al-Fe intermetallic platelets (beta-Al5FeSi) increased with increasing Fe content. The addition of Ca modified the eutectic microstructure and also reduced the size of intermetallic Fe-platelets, causing improved elongation and impact strengths. A low level of Ca addition (39 ppm) reduced the porosity of the alloys. The tensile strength was decreased marginally with Ca addition. However, Ca addition improved the ductility of the alloy by 18.3, 16.7, and 44 pet and the impact strength by 44, 48, and 15.8 pct for Fe contents of 0.2, 0.4, and 0.7 pct, respectively.

Light alloy castings for automotive applications: The case of Al vs Mg

The economical and environmental effects of mass reduction through Al and Mg primary alloys substitutions for cast iron and steel in automotive components are discussed using MF. Ashby's penalty functions method The viability of Mg alloy substitutions for existing Al alloy cast components is also considered. The cost analysis shows that direct, equal-volume, Al alloy substitutions for cast iron and steel are the most feasible in terms of the CAFE liability, followed by substitutions involving flat panels of prescribed stiffness. When the creation of CO2 associated to the production of Al and Mg is considered, the potential gasoline savings over the lifespan of the car compensate for the intrinsic environmental burden of Al in all applications, while electrolytic Mg substitutions for cast iron and steel are feasible for equal volume and panels only. Magnesium produced by the Pidgeon thermal process appears to be too primary energy intensive to be competitive in structural applications. Magnesium substitutions for existing Al alloy beams and panels are generally unviable. The current higher recycling efficiency of Al casting alloys confers Al a significant advantage over Mg alloys.

Eutectic solidification and its role in casting porosity formation

Understanding and controlling the eutectic solidification process in Al-Si alloys permits prediction of the formation of casting porosity, eventually leading to methods for its control and elimination. In addition, it enables control of eutectic structure, silicon morphology, and eutectic grain size to further improve the alloy properties. This paper presents the current understanding of eutectic solidification in hypoeutectic Al-Si foundry alloys and the relationship between eutectic solidification and porosity formation. New concepts in engineering eutectic solidification are also explored.

Service performance of engineering materials

Corrosion research by Atrens and co-workers has made significant contributions to the understanding of the service performance of engineering materials. This includes: (1) elucidated corrosion mechanisms of Mg alloys, stainless steels and Cu alloys, (2) developed an improved understanding of passivity in stainless steels and binary alloys such as Fe-Cr, Ni-Cr, Co-Cr, Fe-Ti, and Fe-Si, (3) developed an improved understanding of the melt spinning of Cu alloys, and (4) elucidated mechanisms of environment assisted fracture (EAF) of steels and Zr alloys. This paper summarises contributions in the following: (1) intergranular stress corrosion cracking of pipeline steels, (2) atmospheric corrosion and patination of Cu, (3) corrosion of Mg alloys, and (4) transgranular stress corrosion cracking of rock bolts.

Semisolid structure formation and semisolid casting

Semisolid metal forming has now been accepted as a viable technology for production of components with complex shape and high integrity. The advantages of semisolid metal forming can only be achieved when the feedstock material has a non-dendritic semisolid structure. A controlled nucleation method has been developed to produce such structures for semisolid forming. By controlling grain nucleation and growth, fine-grained and non-dendritic microstructures that are suitable for semisolid casting can be generated. The method was applied to hypoeutectic and hypereutectic Al-Si casting alloys, Al wrought alloys and a Mg alloy. Parameters such as pouring temperature, cooling rate and grain refiner addition were controlled to achieve copious nucleation, nuclei survival and dendritic growth suppression during solidification. The influences of the controlling parameters on the formation of semisolid structure were different for each of these alloy groups. The as-cast structures were then partially remelted and isothermally held. Semisolid structures were developed and followed by semisolid casting into a stepped die.

Strength-ductility behaviour of Al-Si-Cu-Mg casting alloys in T6 temper

A comparative study of the mechanical properties of 20 experimental alloys has been carried out. The effect of different contents of Si, Cu, Mg, Fe and Mn, as well as solidification rate, has been assessed using a strength-ductility chart and a quality index-strength chart developed for the alloys. The charts show that the strength generally increases and the ductility decreases with an increasing content of Cu and Mg. Increased Fe (at Fe/Mn ratio 0.5) dramatically lowers the ductility and strength of low Si alloys. Increased Si content generally increases the strength and the ductility. The increase in ductility with increased Si is particularly significant when the Fe content is high. The charts are used to show that the cracking of second phase particles imposes a limit to the maximum achievable strength by limiting the ductility of strong alloys. The (Cu + Mg) content (at.%), which determines the precipitation strengthening and the volume fraction of Cu-rich and Mg-rich intermetallics, can be used to select the alloys for given strength and ductility, provided the Fe content stays below the Si-dependent critical level for the formation of pre-eutectic alpha-phase particles or beta-phase plates.

Effect of iron on grain refinement of high-purity MG-Al alloys

The effect of iron on the grain refinement of high-purity Mg-3%Al and Mg-91%Al alloys has been investigated using anhydrous FeCl3 as an iron additive at 750degreesC in carbon-free aluminium titanite crucibles. It was shown that grain refinement was readily achievable for both alloys. Fe- and Al-rich intermetallic particles were observed in many magnesium grains. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.