Improving the ionic conductivity of yttria-stabilised zirconia electrolyte materials

Low-temperature anneals (1200 degreesC for 40 h) of 8 mol% yttria-stabilised zirconia, prior to the samples being sintered at 1500 degreesC, had the effect of improving the ionic conductivity of the specimens. The presence Of SiO2 in the specimens was shown to be detrimental, however. Irrespective of the SiO2 content, this type of heat treatment also leads to improvements in conductivity. Extensive microstructural analysis provided indication of the mechanism of this phenomenon. This included selective formation of zircon, relief of sintering strain leading to the formation of coherent grain boundaries and segregation effects. (C) 2002 Elsevier Science B.V All rights reserved.

Characterization of the acidic properties of mesoporous aluminosilicates synthesized from leached saponite with additional aluminum incorporation

The acidic properties of hexagonal mesoporous aluminosilicates synthesized via a new successful short time synthesis route using leached saponite and a low concentration of surfactant are thoroughly investigated. The resulting aluminosilicate mesoporous materials with high Si/Al ratios of around 11 have a maximal surface area of 1130 m(2)/g, a pore volume of 0.92 cm(3)/g, and a narrow pore size distribution at around 3 nm. The replacement of the sodium ions, present as counterions in the synthesized aluminosilicates, with protons imparts useful catalytic acidity. This acidity is extensively studied with FTIR spectroscopy after adsorption of ammonia and cyclohexylamine, while deuterated acetonitrile differentiates between Bronsted and Lewis acidity. Al-27 NMR spectroscopy determined the coordination of the aluminum in the FSM materials. Simultaneously the effect of an additional Al incorporation, utilizing sodium aluminate, aluminum nitrate, and aluminum isopropoxide is studied. From an acidic point of view, the incorporation with Al(NO3)(3) appears to be the most optimal, as the sample has a very high amount of acid sites (1.3 mmol/g). Investigating the nature of the acid sites it is found that in all samples except the one incorporated with Al(NO3)(3), more Bronsted than Lewis sites are present, both sites being quite acidic as they resist desorption temperatures up to 300 degreesC. Probing the coordination and location of the Al atoms, all the catalysts appeared to have mostly tetrahedral aluminum, up to 95% of the total Al amount for the proton exchanged AI(NO3)(3) incorporated sample.