New structure formation on gamma-irradiation of poly(chlorotrifluoroethylene)

The radiation chemistry of PCTFE at different temperatures has been studied. The polymer was irradiated under vacuum to absorbed doses of up to 1500 kGy. Three irradiation temperatures were chosen. These included ambient temperature, a temperature well above the T, and a temperature above the crystalline melting temperature. These were 298, 423 and 493 K, respectively. The formation of new structures was identified by solid-state FTIR and F-19 NMR. No branching was observed below the melting temperature, but branches were observed above the melting temperature. G-values for chain-end formation were 1.5 and 2.4 at room temperature and 423 K, respectively and the G-value for the formation of double bonds was found to be < 0.1. For the irradiations at 493 K, the G-values for the formation of chain ends, double bonds and branching points were 3.6, 0.2 and 0.5, respectively. The presence of long-chain branches within the polymer structure could not be proven for radiolysis at 493 K, but scission predominates and network formation does not occur upon irradiation. DSC studies of the polymers irradiated at ambient temperature were consistent with chain scission leading to an increase in the percentage crystallinity, as observed for other fluoropolymers. (C) 2003 Elsevier Science Ltd. All rights reserved.

Cross-linking of PFA by electron beam irradiation

The effect of electron beam radiation on a perfluoroalkoxy (PFA) resin was examined using solid-state high-speed magic angle spinning F-19 NMR spectroscopy and FT-IR spectroscopy. Samples were prepared for analysis by subjecting them to electron beam radiation in the dose range 0.5-2.0 MGy at 633 K, which is above the crystalline melting temperature. The new structures were identified and include new saturated chain ends, short and long branches, unsaturated groups, and cross-links. The radiation chemical yield (G value) of new long branch points was greater than the G value of new chain ends, suggesting that cross-linking is the net radiolytic process. This conclusion was supported by an observed decrease in the crystallinity and an increase in the optical clarity of the polymer.