Radical formation on gamma-radiolysis of poly [(methacrylic acid)-co-acrylonitri

The radicals formed on gamma-radiolysis of a series of copolymers of methacrylic acid and acrylonitrile have been investigated by ESR spectroscopy. This series of copolymers spanned the full composition range and the study was carried out at 77 K and ambient temperature. The radicals formed in the copolymers at 77 and 303 K were found to be similar to those found in the two homopolymers, but in the intermediate composition range the presence of acrylonitrile propagation radicals was also detected. These radicals were not observed to be formed in significant quantities on the radiolysis of polyacrylonitrile. They are believed to result from a scission of the main chain at methacrylic acid/acrylonitrile diad sequences following loss of the methacrylic acid carboxyl group. At 77 K, the copolymers with high methacrylic acid contents were found to be more sensitive to radical formation than the methacrylic acid homopolymer, but this enhanced sensitivity was not evident at ambient temperature, where the G-values for radical formation for the copolymers were slightly less than the values for the homopolymers. (C) 2003 Society of Chemical Industry.

G-values for scission and crosslinking on γ-radiolysis of Ultem at 303 K

The radiation chemical yields G(S) and G(X) for H-linking and Y-linking models for Ultem have been calculated from molecular weight analysis by gel permeation chromatography. These G-values have been compared with the G-values obtained from analysis of soluble fractions above the gel dose, Which have been reported in previous works. An analysis of the molecular weight data in terms of H-linking and Y-linking mechanisms yielded values of G(S-H) = 1.0 x 10(-3) and G(H) = 6.0 x 10(-3) and G(S-Y) = 1.3 x 10(-2) and G(Y) = 1.8 x 10(-2). The corresponding values obtained from the solubility data were G(SH) = 0.53 x 10(-2), G(H) = 1.39 x 10(-2), G(S-Y) = 4.2 x 10(-2) and G(Y) - 4.6 x 10(-2). The origin of the disagreement between the molecular weight and solubility values is not clear, but it could arise as a result of observed microgel formation below the reported gel dose of 0.13 MGy. Whether the crosslink mechanism proceeds by an H-linking or Y-linking process is also unclear and will require direct observation of the crosslinking structures.

Isomers of 1,4,8,11-tetraazacyclotetradecane-6,13-dicarboxylate characterized as cobalt(III) complexes

The major trans (1) and minor cis (2) isomers of 1,4,8,11-tetraazacyclotetradecane-6,13-dicarboxylate have been characterized as the complexes [Co(1)](ClO4) and [Co(H-2)(OH2)]Cl(ClO4).H2O. The former crystallized in the C-2/c space group and the latter in the P2(1)/c space group, with cell parameters a 16.258(7), b 9.050(3), c 15.413(6) Angstrom, beta133.29(3)degrees, and a 9.694(4), b 16.135(1), c 12.973(5) Angstrom, beta 93.00(2)degrees, respectively. Their characterization completes identification of the respective trans and cis isomers for the series of C-pendant macrocycles also including 1,4,8,11-tetraazacyclotetradecane-6-amine-13-carboxylate ((3), (4)) and 1,4,8,11-tetraazacyclotetradecane-6,13-diamine ((5), (6)). The complexes show limited distortion from octahedral geometry with the strain in the presence of the coordinated C-pendant carboxylate significantly reduced compared with that for the C-pendant amine in analogues, a consequence mainly of six-membered as opposed to five-membered chelate rings involving the pendant donor. A comparison of the physical properties for the trans isomers of the octahedral complexes of (1), (3), and (5), which reflect progressively increasing strain, is presented.