The crystallography and morphology of Mo2C in ferrite

The orientation relationships between hexagonal Mo2C precipitates (H) in ferrite (B) have been determined by electron diffraction to an accuracy of +/-2degrees. With one exception, the 19 results are consistent with the previously reported Pitsch and Schrader (P/S) orientation relationship. However, these more accurate determinations show clearly that there is a systematic deviation of up to 5.5degrees from the exact P/S relationship and that this deviation consists of a small rotation about the parallel close packed directions-[100](B)//[2 (1) over bar(1) over bar0](H). The long direction of the Mo2C needles has been determined unequivocally in terms of the orientation relationship to be [100](B)//[2 (1) over bar(1) over bar0](H). Moire fringes between precipitate and matrix have been used to improve the accuracy of the orientation relationship results and to determine the lattice parameters of the carbide precipitates investigated. The Moire fringe analysis has shown small systematic departures from the exact parallelism between [100](B) and [2 (1) over bar(1) over bar0](H) along the length of Mo2C needles and a lowering of the carbide lattice parameter that is consistent with the replacement of Mo by Fe in the carbide. The orientation relationship results, including the observed systematic deviation from the exact P/S relationship, are shown to be consistent with the edge-to-edge model. (C) 2002 Kluwer Academic Publishers.

Structural changes in mixed Langmuir-Blodgett films upon nanoparticle formation

The formation of CdS nanoparticles by reacting mixed Langmuir-Blodgett films of arachidic acid and either octadecylamine or dimethyldioctadecylammonium nitrate on a cadmium-containing subphase with hydrogen sulfide gas has resulted in the identification of a number of structural changes, observed using grazing incidence X-ray diffraction. In the case of octadecylamine, the structure after reaction is a hexagonal close-packed array of surfactant-stabilized nanoclusters, with a lattice constant of a = 17.65 Angstrom. In both octadecylamine and dimethyldioctadecylammonium nitrate films, the presence of a unit cell tilted at 38degrees to the plane of the substrate was found. Despite these changes, the average nanoparticle size was unaffected by the addition of either second component to the film.

Characterization of the acidic properties of mesoporous aluminosilicates synthesized from leached saponite with additional aluminum incorporation

The acidic properties of hexagonal mesoporous aluminosilicates synthesized via a new successful short time synthesis route using leached saponite and a low concentration of surfactant are thoroughly investigated. The resulting aluminosilicate mesoporous materials with high Si/Al ratios of around 11 have a maximal surface area of 1130 m(2)/g, a pore volume of 0.92 cm(3)/g, and a narrow pore size distribution at around 3 nm. The replacement of the sodium ions, present as counterions in the synthesized aluminosilicates, with protons imparts useful catalytic acidity. This acidity is extensively studied with FTIR spectroscopy after adsorption of ammonia and cyclohexylamine, while deuterated acetonitrile differentiates between Bronsted and Lewis acidity. Al-27 NMR spectroscopy determined the coordination of the aluminum in the FSM materials. Simultaneously the effect of an additional Al incorporation, utilizing sodium aluminate, aluminum nitrate, and aluminum isopropoxide is studied. From an acidic point of view, the incorporation with Al(NO3)(3) appears to be the most optimal, as the sample has a very high amount of acid sites (1.3 mmol/g). Investigating the nature of the acid sites it is found that in all samples except the one incorporated with Al(NO3)(3), more Bronsted than Lewis sites are present, both sites being quite acidic as they resist desorption temperatures up to 300 degreesC. Probing the coordination and location of the Al atoms, all the catalysts appeared to have mostly tetrahedral aluminum, up to 95% of the total Al amount for the proton exchanged AI(NO3)(3) incorporated sample.