Effect of Co addition on the lattice parameter, electrical conductivity and sintering of gadolinia-doped ceria

Co-sintering aid has been added to Ce1.9Gd0.1O1.95 (CGO) by treating a commercial powder with Co(NO3)(2) (COCGO), X-ray diffraction (XRD) measurements of lattice parameter indicated that the Co was located on the CGO particle surface after calcination at 650 degreesC. After heat treatment at temperatures above 650 degreesC, the room temperature lattice parameter of CGO was found to increase, indicating redistribution of the Gd. Compared to CGO, the lattice parameter of CGO + 2 cation% Co (2CoCGO) was lower for a given temperature (650-1100 degreesC), A.C. impedance revealed that the lattice conductivity of 2CoCGO was enhanced when densified at lower temperatures, Transmission electron microscopy (TEM) showed that, even after sintering for 4 h at 980 degreesC, most of the Co was located at grain boundaries. (C) 2002 Published by Elsevier Science B.V.

Oxide ionic conductivity and microstructures of Sm- or La-doped CeO2-based systems

The concept of crystallographic index termed the effective index is suggested and applied to the design of ceria (CeO2)-based electrolytes to maximize oxide ionic conductivity. The suggested index considers the fluorite structure, and combines the expected oxygen vacancy level with the ionic radius mismatch between host and dopant cations. Using this approach, oxide ionic conductivity of Sm- or La-doped CeO2-based system has been optimized and tested under operating conditions of a solid oxide fuel cell. In the observation of microstructure in atomic scale, both Sm-doped CeO2 and La-doped CeO2 electrolytes had large micro-domains over 10 nm in the lattice. On the other hand, Sm or La and alkaline earth co-doped CeO2-based electrolytes with high effective index had small micro-domains around 1-3 nm in the microstructure. The large micro-domain would prevent oxide ion from passing through the lattice. Therefore, it is concluded that the improvement of ionic conductivity is reflected in changes of microstructure in atomic scale. (C) 2002 Elsevier Science B.V. All rights reserved.