The effect of Cu addition and milling contaminations on the microstructure evolution of ball milled Al-Pb alloy during sintering

Al-10 wt.%Pb and Al-10 wt.%Pb-x wt.%Cu (x = 0-7.0) bulk alloys were prepared by sintering the mechanically alloyed powders at various temperatures. The microstructure changes of the as consolidated powders in the course of sintering were analyzed by differential scanning calorimetry, scanning electron microscopy, X-ray diffraction analysis and transmission electron microscopy. It has been found that, with respect to the Al-10 wt.%Pb-x wt.%Cu alloy, CuAl2 and Cu9Al4 phases formed in the milling process, and the amount of CuAl2 phase increased while the Cu9Al4 phase disappeared gradually in the sintering process. In both Al-10 wt.%Pb and Al-10 wt.%Pb-x wt.%Cu alloys, the sintering process results in the coarsening of Pb phase and the growth rate of Pb phase fulfills the Lifshitz-Slyozov-Wagner equation even though the size of the Pb phase was in nanometer range. The Pb particle exhibits cuboctahedral morphology and has a cubic to cubic orientation relationship with the Al matrix. The addition of Cu strongly depressed the growth rate of Pb. Contamination induced by milling has apparent influence on the microstructure of the sintered alloys. Al7Cu2Fe and aluminium oxide phases were identified in the sintered alloys. The cuboctahedral morphology of Pb particles was broken up by the presence of the oxide phase. (c) 2006 Elsevier B.V. All rights reserved.

Modification-related porosity formation in hypoeutectic aluminum-silicon alloys

A series of aluminum-10 wt pet silicon castings were produced in sand molds to investigate the effect of modification on porosity formation. Modification with individual additions of either strontium or sodium resulted in a statistically significant increase in the level of porosity compared to unmodified castings. The increase in porosity with modification is due to the presence of numerous dispersed pores, which were absent in the unmodified casting. It is proposed that these pores form as a result of differences in size of the aluminum-silicon eutectic grains between unmodified and modified alloys. A geometric model is developed to show how the size of eutectic grains can influence the amount and distribution of porosity. Unlike traditional feeding-based models, which incorporate the effect: of microstructure on permeability, this model considers what happens when liquid is isolated from the riser and can no longer flow. This simple isolation model complements rather than contradicts existing theories on modification-related porosity formation and should be considered in the development of future comprehensive models.

Eutectic grains in unmodified and strontium-modified hypoeutectic aluminum-silicon alloys

Additions of strontium to hypoeutectic aluminum-silicon alloys modify the morphology of the eutectic silicon phase from a coarse platelike structure to a fine fibrous structure. Thermal analysis, interrupted solidification, and microstructural examination of sand castings in this work revealed that, in addition to a change in silicon morphology, modification with strontium also causes an increase in the size of eutectic grains. The eutectic grain size increases because fewer grains nucleate, possibly due to poisoning of the phosphorus-based nucleants, that are active in the unmodified alloy. A simple growth model is developed to estimate the interface velocity during solidification of a eutectic grain. The model confirms, independent of microstructural observations, that the addition of 100 ppm strontium increases the eutectic grain size by at least an order of magnitude compared with the equivalent unmodified alloy. The model predicts that the growth velocity varies significantly during eutectic growth. At low strontium levels, these variations may be sufficient to cause transitions between flake and fibrous silicon morphologies depending on the casting conditions. The model can be used to rationally interpret the eutectic grain structure and silicon morphology of fully solidified aluminum-silicon castings and, when coupled with reliable thermal data, can be used to estimate the eutectic grain size.

Surface oxide and the role of magnesium during the sintering of aluminum

The effect of trace additions of magnesium on the sintering of aluminum and its alloys is examined. Magnesium, especially at low concentrations, has a disproportionate effect on sintering because it disrupts the passivating Al2O3 layer through the formation of a spinel phase. Magnesium penetrates the sintering compact by solid-state diffusion, and the oxide is reduced at the metal-oxide interface. This facilitates solid-state sintering, as well as wetting of the underlying metal by sintering liquids, when these are present. The optimum magnesium concentration is approximately 0.1 to 1.0 wt pet, but this is dependent on the volume of oxide and, hence, the particle size, as well as the sintering conditions. Small particle-size fractions require proportionally more magnesium than large-size fractions do.

Influence of Mg content on the microstructure and solid solution chemistry of Al-7%Si-Mg casting alloys during solution treatment

The solution treatment stage of the T6 heat-treatment of Al-7%Si-Mg foundry alloys influences microstructural features such as Mg2Si dissolution, and eutectic silicon spheroidisation and coarsening. Microstructural and microanalytical studies have been conducted across a range of Sr-modified Al-7%Si alloys, with an Fe content of 0.12% and Mg contents ranging from 0.3-0.7wt%. Qualitative and quantitative metallography have shown that, in addition to the above changes, solution treatment also results in changes to the relative proportions of iron-containing intermetallic particles and that these changes are composition-dependent. While solution treatment causes a substantial transformation of pi phase to beta phase in low Mg alloys (0.3-0.4%), this change is not readily apparent at higher Mg levels (0.6-0.7%). The pi to beta transformation is accompanied by a release of Mg into the aluminum matrix over and above that which arises from the rapid dissolution of Mg2Si. Since the level of matrix Mg retained after quenching controls an alloy's subsequent precipitation hardening response, a proper understanding of this phase transformation is crucial if tensile properties are to be maximised.

Eutectic nucleation and growth in hypoeutectic Al-SI alloys at different strontium levels

The effects of different levels of strontium on nucleation and growth of the eutectic in a commercial hypoeutectic Al-Si foundry alloy have been investigated by optical microscopy and electron backscattering diffraction (EBSD) mapping by scanning electron microscopy (SEM). The microstructural evolution of each specimen during solidification was studied by a quenching technique at different temperatures and Sr contents. By comparing the orientation of the aluminum in the eutectic to that of the surrounding primary aluminum dendrites by EBSD, the eutectic formation mechanism could be determined. The results of these studies show that the eutectic nucleation mode, and subsequent growth mode, is strongly dependent on Sr level. Three distinctly different eutectic growth modes were found, in isolation or sometimes together, but different for each Sr content. At very low Sr contents, the eutectic nucleated and grew from the primary phase. Increasing the Sr level to between 70 and 110 ppm resulted in nucleation of independent eutectic grains with no relation to the primary dendrites. At a Sr level of 500 ppm, the eutectic again nucleated on and grew from the primary phase while a well-modified eutectic structure was still present. A slight dependency of eutectic growth radially from the mold wall opposite the thermal gradient was observed in all specimens in the early stages of eutectic solidification.

The influence of the atmosphere on the sintering of aluminum

Alloys of Al, Al-0.15Mg, and Al-12Sn made using air atomized aluminum powder and pressed to green densities of 75 to 98 pet were sintered under argon or nitrogen. Sintering in argon is only effective at high green densities when magnesium is present. In contrast, highly porous aluminum can be sintered in nitrogen without the need for magnesium. The oxygen concentration in the gas is reduced by the aluminum through a self-gettering process. The outer layers of the porous powder compact serve as a getter for the inner layers such that the oxygen partial pressure is reduced deep within the pore network. Aluminum nitride then forms, either by direct reaction with the metal or by reduction of the oxide layer, and sintering follows.

Eutectic modification and microstructure development in Al-Si alloys

Recent increasing applications for cast Al-Si alloys are particularly driven by the need for lightweighting components in the automotive sector. To improve mechanical properties, elements such as strontium, sodium and antimony can be added to modify the eutectic silicon from coarse and plate-like to fine and fibrous morphology. It is only recently being noticed that the morphological transformation resulting from eutectic modification is also accompanied by other, equally significant, but often unexpected changes. These changes can include a 10-fold increase in the eutectic grain size, redistribution of low-melting point phases and porosity as well as surface finish, consequently leading to variations in casting quality. This paper shows the state-of-the-art in understanding the mechanism of eutectic nucleation and growth in Al-Si alloys, inspecting samples, both quenched and uninterrupted, on the macro, micro and nano-scale. It shows that significant variations in eutectic nucleation and growth dynamics occur in AI-Si alloys as a function of the type and amount of modifier elements added. The key role of AIP particles in nucleating silicon is demonstrated. (c) 2005 Elsevier B.V. All rights reserved.

Eutectic solidification in hypoeutectic Al-Si alloys: electron backscatter diffraction analysis

Nucleation and growth of the eutectic, in hypoeutectic Al-Si foundry alloys has been investigated by the electron backscatter diffraction (EBSD) mapping technique using a scanning electron microscope (SEM). Sample preparation procedures for optimizing mapping have been developed. To obtain a sufficiently smooth surface from a cast Al-Si eutectic microstructure for EBSD mapping, an appropriate preparation technique by ion milling was developed and applied instead of conventional electropolishing. By comparing the orientation of the aluminum in the eutectic to that of the surrounding primary aluminum dendrites, the growth mechanism of the eutectic can be determined. Two different results were found, in isolation or sometimes together, but distinct for different strontium contents: (1) crystallographic orientations of aluminum in eutectic and surrounding primary dendrites are identical, and (2) wide variation in orientations of the aluminum in the eutectic. (C) 2001 Elsevier Science Inc. All rights reserved.

An age hardening model for Al-7Si-Mg casting alloys

Yield strength (YS) ageing curves have been modelled for A356 and A357 aluminium casting alloys below the solvus temperature of the main hardening precipitate. Predictions are based on the Shercliff and Ashby methodology (Acta MetaH. Mater. 38 (1990) 1789) for wrought alloys. Differences between strengthening in wrought and cast Al-Si-Mg alloys are considered. A Brinell hardness to YS conversion incorporating strain hardening has been established to enable YS ageing curves to be predicted with reduced experimental effort. (C) 2002 Elsevier Science B.V. All rights reserved.

Rapid manufacturing of aluminum components

A manufacturing technique for the production of aluminum components is described. A resin-bonded part is formed by a rapid prototyping technique and then debound and infiltrated by a second aluminum alloy under a nitrogen atmosphere. During thermal processing, the aluminum reacts with the nitrogen and is partially transformed into a rigid aluminum nitride skeleton, which provides the structural rigidity during infiltration. The simplicity and rapidity of this process in comparison to conventional production routes, combined with the ability to fabricate complicated parts of almost any geometry and with high dimensional precision, provide an additional means to manufacture aluminum components.