Characterisation of xerogels derived from sucrose templated sol-gel synthesis

This work presents the results of the nanostructural characterisation of the effect of sucrose as a template added to a sol derived from a tetraethoxysilane acid catalysed process. By increasing the sucrose template ratio, N-2 adsorption isotherms showed that the xerogel samples changed from a micropore to a mesopore nanostructure as evidenced by the formation of hysteresis at 0.5 partial pressure. In turn, this led to a direct increase in surface areas, pore volumes and average pore sizes. Sucrose has two molecular components of the same molecular weight: D-fructose and D-glucose. D-fructose resulted in the formation of higher pore volumes and pore sizes, while D-glucose formed higher surface area xerogels. Depending of the template ratio employed in the xerogel synthesis, average pore radius ranged from 8.8 to 26 Angstrom, while surface areas increased by over two fold up to 750 m(2) . g(-1). However, pore volumes increased by as much as six fold, from 0.15 to almost 1 cm(3) . g(-1).

Postsynthesis stabilization of free-standing mesoporous silica films

Mixed ammonia-water vapor postsynthesis treatment provides a simple and convenient method for stabilizing mesostructured silica films. X-ray diffraction, transmission electron microscopy, nitrogen adsorption/desorption, and solid-state NMR (C-13, Si-29) were applied to study the effects of mixed ammonia-water vapor at 90 degreesC on the mesostructure of the films. An increased cross-linking of the silica network was observed. Subsequent calcination of the silica films was seen to cause a bimodal pore-size distribution, with an accompanying increase in the volume and surface area ratios of the primary (d = 3 nm) to secondary (d = 5-30 nm) pores. Additionally, mixed ammonia-water treatment was observed to cause a narrowing of the primary pore-size distribution. These findings have implications for thin film based applications and devices, such as sensors, membranes, or surfaces for heterogeneous catalysis.

Biomolecular screening with novel organosilica microspheres

Organosilica microspheres synthesised via a novel surfactant-free emulsion-based method show applicability towards optical encoding, solid-phase synthesis and high-throughput screening of bound oligonucleotide and peptide sequences.