Preparation and characterisation of biodegradable starch-based nanocomposite materials

Different formulations of biodegradable starch-polyester blend nanocomposite materials have been film blown on a pilot scale film blowing tower. The physical properties of different films have been examined by thermal and mechanical analysis and X-ray diffraction. The results show that the addition of an organoclay (from 0 to 5 wt%) significantly improves both the processing and tensile properties over the original starch blends. Wide angle X-ray diffraction (WAXD) results indicate that the best results were obtained for 30wt% starch blends, and the level of delamination depends on the ratio of starch to polyester and amount of organoclay added. The crystallisation temperature of the nanocomposite blends is significantly lower than the base blend. This is probably due to the platelets inhibiting order, and hence crystallisation, of the starch and polyester. The mechanical and thermal properties of the blends are also sensitive to the way the clay particles are dispersed. (C) 2003 Society of Chemical Industry.

Biodegradation and ecotoxicity evaluation of a bionolle and starch blend and its degradation products in compost

A polymer based on a blend of starch and Bionolle(TM) has been prepared and tested for biodegradation in compost. The polymer was completely mineralised to carbon dioxide in 45 days. The potential toxicity of the polymer was tested against the earthworm Eisenia fetida using a modification of the American Standard for Testing Materials E1976-97. The earthworms were exposed to 30 g of the polymer for 28 days and changes in weight recorded. In addition, the polymer was firstly degraded by the compost and the worms exposed to the breakdown products for 28 days. Differences in weight were also recorded. In each case the production of juveniles was noted and all earthworms were examined for pathology. The results obtained were processed statistically using a t-test. The number of juveniles, produced from the breakdown products, was highly significant (P < 0.001) when compared to the earthworms added to the intact polymer. There was a definitely significant difference (P < 0.01, t = 3.25) in change in weight between the earthworms that were exposed to the polymer directly and those that were exposed to the breakdown products. There was no indication of any pathology of any earthworms. The polymer is considered safe for this species. (C) 2002 Elsevier Science Ltd. All rights reserved.

Radical formation on gamma-radiolysis of poly [(methacrylic acid)-co-acrylonitri

The radicals formed on gamma-radiolysis of a series of copolymers of methacrylic acid and acrylonitrile have been investigated by ESR spectroscopy. This series of copolymers spanned the full composition range and the study was carried out at 77 K and ambient temperature. The radicals formed in the copolymers at 77 and 303 K were found to be similar to those found in the two homopolymers, but in the intermediate composition range the presence of acrylonitrile propagation radicals was also detected. These radicals were not observed to be formed in significant quantities on the radiolysis of polyacrylonitrile. They are believed to result from a scission of the main chain at methacrylic acid/acrylonitrile diad sequences following loss of the methacrylic acid carboxyl group. At 77 K, the copolymers with high methacrylic acid contents were found to be more sensitive to radical formation than the methacrylic acid homopolymer, but this enhanced sensitivity was not evident at ambient temperature, where the G-values for radical formation for the copolymers were slightly less than the values for the homopolymers. (C) 2003 Society of Chemical Industry.