Water sorption into poly[(2-hydroxyethyl methacrylate)-co-(1-vinyl-2-pyrrolidone]at 310 K

Poly(2-hydroxyethyl methacrylate) and copolymers of 2-hydroxyethyl methacrylate (HEMA) and 1-vinyl-2-pyrrolidone (VP) in the form of cylindrical samples (approximate to8mm x 20mm) have been prepared and the sorption of water into these cylinders has been studied by the mass-uptake methods and by magnetic-resonance imaging. The equilibrium water contents for the cylinders were found to vary systematically with the copolymer composition. Diffusion of water into the cylinders was found to follow Fickian behaviour for cylinders with high HEMA contents, with the diffusion coefficients obtained from mass-uptake studies dependent on the copolymer composition, varying from 1.7 x 10(-11) m(2) s(-1) for poly(HEMA) to 2.0 x 10(-11) m(2) s(-1) for poly(HEMA-co-VP) with a composition of 1:1. However, NMR-imaging studies showed that, while the profiles of the water diffusion fronts for cylinders with high HEMA contents were Fickian, that for the 1:1 copolymer was not and indicated that the mechanism was Case III. The polymers which were rich in VP were characterized by a water-sorption process which follows Case-III behaviour. (C) 2003 Society of Chemical Industry.

G-values for scission and crosslinking on γ-radiolysis of Ultem at 303 K

The radiation chemical yields G(S) and G(X) for H-linking and Y-linking models for Ultem have been calculated from molecular weight analysis by gel permeation chromatography. These G-values have been compared with the G-values obtained from analysis of soluble fractions above the gel dose, Which have been reported in previous works. An analysis of the molecular weight data in terms of H-linking and Y-linking mechanisms yielded values of G(S-H) = 1.0 x 10(-3) and G(H) = 6.0 x 10(-3) and G(S-Y) = 1.3 x 10(-2) and G(Y) = 1.8 x 10(-2). The corresponding values obtained from the solubility data were G(SH) = 0.53 x 10(-2), G(H) = 1.39 x 10(-2), G(S-Y) = 4.2 x 10(-2) and G(Y) - 4.6 x 10(-2). The origin of the disagreement between the molecular weight and solubility values is not clear, but it could arise as a result of observed microgel formation below the reported gel dose of 0.13 MGy. Whether the crosslink mechanism proceeds by an H-linking or Y-linking process is also unclear and will require direct observation of the crosslinking structures.