New HDPE/MCM41 nanocomposites with improved mechanical performance: synthesis and characterizatio

Ordered mesoporous silicas with a channel structure of well-defined geometries and dimensions at nanometer scale are excellent candidates to host intercalation reactions. In recent years, our research group has shown that mesoporous silicas of the M41S class combined with metallocene complexes give rise to excellent supported catalysts for ethylene polymerisation. Due to the support characteristics, the reaction is allowed to occur in the channels and in this way hybrid organic-inorganic materials can be prepared within a large range of nanofiller concentration. These HDPE/MCM-41 nanocomposites exhibit an improved mechanical performance and an easier degradability due to the additional role of MCM-41 as a promoter for PE degradation.

Hybrid materials based on polyethylene and MCM-41 microparticles functionalized with silanes: catalytic aspects of in situ polymerization, crystalline features and mechanical properties

New nanocomposites based on polyethylene have been prepared by in situ polymerization of ethylene in presence of mesoporous MCM-41. The polymerization reactions were performed using a zirconocene catalyst either under homogenous conditions or supported onto mesoporous MCM-41 particles, which are synthesized and decorated post-synthesis with two silanes before polymerization in order to promote an enhanced interfacial adhesion. The existence of polyethylene chains able to crystallize within the mesoporous channels in the resulting nanocomposites is figured out from the small endothermic process, located at around 80 C, on heating calorimetric experiments, in addition to the main melting endotherm. These results indicate that polyethylene macrochains can grow up during polymerization either outside or inside the MCM-41 channels, these keeping their regular hexagonal arrangements. Mechanical response is observed to be dependent on the content in mesoporous MCM-41 and on the crystalline features of polyethylene. Accordingly, stiffness increases and deformability decreases in the nanocomposites as much as MCM-41 content is enlarged and polyethylene amount within channels is raised. Ultimate mechanical performance improves with MCM-41 incorporation without varying the final processing temperature.