The development of a compact gamma camera with high spatial resolution is of great interest in Nuclear Medicine as a means to increase the sensitivity of scintigraphy exams and thus allow the early detection of small tumours. Following the introduction of the wavelength-shifting fibre (WSF) gamma camera by Soares et al. and evolution of photodiodes into highly sensitive silicon photomultipliers (SiPMs), this thesis explores the development of a WSF gamma camera using SiPMs to obtain the position information of scintillation events in a continuous CsI(Na) crystal. The design is highly flexible, allowing the coverage of different areas and the development of compact cameras, with very small dead areas at the edges. After initial studies which confirmed the feasibility of applying SiPMs, a prototype with 5 5 cm2 was assembled and tested at room temperature, in an active field-of-view of 10 10 mm2. Calibration and characterisation of intrinsic properties of this prototype were done using 57Co, while extrinsic measurements were performed using a high-resolution parallel-hole collimator and 99mTc. In addition, a small mouse injected with a radiopharmaceutical was imaged with the developed prototype. Results confirm the great potential of SiPMs when applied in a WSF gamma camera, achieving spatial resolution performance superior to the traditional Anger camera. Furthermore, performance can be improved by an optimisation of experimental conditions, in order to minimise and control the undesirable effects of thermal noise and non-uniformity of response of multiple SiPMs. The development and partial characterisation of a larger SiPM WSF gamma camera with 10 10 cm2 for clinical application are also presented.

The influence of photon excitation and proton irradiation on the luminescence properties of yttria stabilized zirconia doped with praseodymium ions

Lanthanide doped zirconia based materials are promising phosphors for lighting applications. Transparent yttria stabilized zirconia fibres, in situ doped with Pr3+ ions, were grown by the laser floating zone method. The single crystalline doped fibres were found to be homogeneous in composition and provide an intense red luminescence at room temperature. The stability of this luminescence due to transitions between the 1D2 → 3H4 multiplets of the Pr3+ ions (intra-4f2 configuration) was studied by photo- and iono-luminescence. The evolution of the red integrated photoluminescence intensity with temperature indicates that the overall luminescence decreases to ca. 40% of the initial intensity at 14 K when heated to room temperature (RT). RT analysis of the iono-luminescence dependence on irradiation fluence reveals a decrease of the intensity (to slightly more than ∼60% of the initial intensity after 25 min of proton irradiation exposure). Nevertheless the luminescence intensity saturates at non-zero values for higher irradiation fluences revealing good potential for the use of this material in radiation environments.