PMMA-co-EHA cements for osteoprotheses

The main purpose of this thesis was to produce new formulations of PMMA-co- EHA and study its feasibility as being an alternative to traditional PMMA bone cements. Thus, were originally produced several co-polymers of PMMA-co-EHA and its mechanical properties and in vitro behaviour were evaluated. The copolymers were obtained by radical polymerization and several formulations were produced by partial replacement of MMA (up to about 50%) for EHA. Overall, the results suggest that the partial replacement of MMA by EHA decreased the modulus of the materials and, consequently, increased its flexibility. Then, PMMA commercial beads were added to PMMA-co-EHA formulations (to get bone cement) and the general properties of the resulting bone cements were evaluated. In general, the results revealed that the partial replacement of MMA by EHA led to beneficial changes in curing parameters (there was a reduction of the peak temperature and an increase of curing/setting time), in the in vitro behaviour (the water capacity increased) and in the mechanical properties (the bending strength increased) of new cements. The in vitro cellular response of new formulations of PMMA-co-EHA was compared with that of traditional PMMA bone cement. To this end, we tested the cell adhesion and proliferation of osteoblast-like MG63 cells and human cells from bone marrow. The results revealed that both types of cells were able to attach and proliferate in both formulations. The only exception was observed for the formulation prepared with the highest percentage of EHA, where a few cells that adhere failed to proliferate. Moreover, it was found that increasing the amount of EHA in cement led to an increasing inhibition of cell growth, especially during the first week of culture. This was related to increased water uptake capacity by the new formulations and consequent release of some of its toxic components. Finally, PMMA commercial beads were partially replaced by HA particles and the influence of this substitution on the curing parameters, the mechanical properties and in vitro behaviour of the resulting composites was also evaluated. Incorporation of HA into the bone cements induced a number of significant changes in its final properties: 1) decrease the peak temperature; 2) increase of curing time, 3) increasing the value of elastic modulus accompanied by decrease of the strength/tension. This last finding was related to poor interfacial adhesion between the various components of the bone cements and a heterogeneous distribution (possible agglomeration) of HA particles.

Inactivation of Pseudomonas spp. biofilms with natural and synthetic photossensitizers

Cationic porphyrins have been widely used as photosensitizers (PSs) in the inactivation of microorganisms, both in biofilms and in planktonic forms. However, the application of curcumin, a natural PS, in the inactivation of biofilms, is poorly studied. The objectives of this study were (1) to evaluate and compare the efficiency of a cationic porphyrin tetra (Tetra-Py+-Me) and curcumin in the photodynamic inactivation of biofilms of Pseudomonas spp and the corresponding planktonic form; (2) to evaluate the effect of these PSs in cell adhesion and biofilm maturation. In eradication assays, biofilms of Pseudomonas spp adherent to silicone tubes were subjected to irradiation with white light (180 J cm-2) in presence of different concentrations (5 and 10 μM) of PS. In colonization experiments, solid supports were immersed in cell suspensions, PS was added and the mixture experimental setup was irradiated (864 J cm-2) during the adhesion phase. After transference solid supports to new PS-containing medium, irradiation (2592 J cm-2) was resumed during biofilm maturation. The assays of inactivation of planktonic cells were conducted in cell suspensions added of PS concentrations equivalent to those used in experiments with biofilms. The inactivation of planktonic cells and biofilms (eradication and colonization assays) was assessed by quantification of viable cells after plating in solid medium, at the beginning and at the end of the experiments. The results show that porphyrin Tetra-Py+-Me effectively inactivated planktonic cells (3.7 and 3.0 log) and biofilms of Pseudomonas spp (3.2 and 3.6 log). In colonization assays, the adhesion of cells was attenuated in 2.2 log, and during the maturation phase, a 5.2 log reduction in the concentration of viable cells was observed. Curcumin failed to cause significant inactivation in planktonic cells (0.7 and 0.9 log) and for that reason it was not tested in biofilm eradication assays. In colonization assays, curcumin did not affect the adhesion of cells to the solid support and caused a very modest reduction (1.0 log) in the concentration of viable cells during the maturation phase. The results confirm that the photodynamic inactivation is a promising strategy to control installed biofilms and in preventing colonization. Curcumin, however, does not represent an advantageous alternative to porphyrins in the case of biofilms of Pseudomonas spp.