Electrolytic cells for plastic waste recycling

The current project assesses potential molten alloy anodes for Solid Oxide Fuel Cells (SOFC) running on solid waste. A detailed phase diagram study was performed to locate probable anode systems. The molten metal oxide system PbO-Sb2O3 was selected as a possible molten alloy anode for this application. A detailed vapour pressure study of this system was performed. Several cells were fabricated to experimentally assess the electrochemical properties of this system. The work reveals several unexpected limiting features such as the incompatibility between the platinum and the chosen alloy. A second cell was built, this time using rhenium wires instead, preventing such reaction. However, the rhenium wire sublimes under oxidizing conditions (air) and the sealing glass and the chosen alloy system react with each other under long term use. Considering all these issues, a third cell design was conceived, surpassing some obstacles and providing some initial information regarding the electrochemical behaviour. The current project shows that many parameters need to be taken into account to ensure materials compatibility. For the PbOSb2O3 system, the high volatility of Sb2O3 was a serious limitation that can only be addressed through the application of new contact wires or sealing materials and conditions. Nonetheless, the project highlights several other potential systems that can be considered, such as Pb11Ge3O17, Pb3GeO5, Pb5Ge3O11, Bi2CuO4, Bi2PdO4, Bi12GeO20.

Photodynamic inactivation of bacteria by cationic porphyrins : their cellular targets and potential environmental applications

Photodynamic inactivation (PDI) is defined as the process of cell destruction by oxidative stress resulting from the interaction between light and a photosensitizer (PS), in the presence of molecular oxygen. PDI of bacteria has been extensively studied in recent years, proving to be a promising alternative to conventional antimicrobial agents for the treatment of superficial and localized infections. Moreover, the applicability of PDI goes far beyond the clinical field, as its potential use in water disinfection, using PS immobilized on solid supports, is currently under study. The aim of the first part of this work was to study the oxidative modifications in phospholipids, nucleic acids and proteins of Escherichia coli and Staphylococcus warneri, subjected to photodynamic treatment with cationic porphyrins. The aims of the second part of the work were to study the efficiency of PDI in aquaculture water and the influence of different physicalchemical parameters in this process, using the Gram-negative bioluminescent bacterium Vibrio fischeri, and to evaluate the possibility of recycling cationic PS immobilized on magnetic nanoparticles. To study the oxidative changes in membrane phospholipids, a lipidomic approach has been used, combining chromatographic techniques and mass spectrometry. The FOX2 assay was used to determine the concentration of lipid hydroperoxides generated after treatment. The oxidative modifications in the proteins were analyzed by one-dimensional polyacrylamide gel electrophoresis (SDS-PAGE). Changes in the intracellular nucleic acids were analyzed by agarose gel electrophoresis and the concentration of doublestranded DNA was determined by fluorimetry. The oxidative changes of bacterial PDI at the molecular level were analyzed by infrared spectroscopy. In laboratory tests, bacteria (108 CFU mL-1) were irradiated with white light (4.0 mW cm-2) after incubation with the PS (Tri-Py+-Me-PF or Tetra-Py+-Me) at concentrations of 0.5 and 5.0 μM for S. warneri and E. coli, respectively. Bacteria were irradiated with different light doses (up to 9.6 J cm-2 for S. warneri and up to 64.8 J cm-2 for E. coli) and the changes were evaluated throughout the irradiation time. In the study of phospholipids, only the porphyrin Tri-Py+-Me-PF and a light dose of 64.8 J cm-2 were tested. The efficiency of PDI in aquaculture has been evaluated in two different conditions: in buffer solution, varying temperature, pH, salinity and oxygen concentration, and in aquaculture water samples, to reproduce the conditions of PDI in situ. The kinetics of the process was determined in realtime during the experiments by measuring the bioluminescence of V. fischeri (107 CFU mL-1, corresponding to a level of bioluminescence of 105 relative light units). A concentration of 5.0 μM of Tri-Py+-Me-PF was used in the experiments with buffer solution, and 10 to 50 μM in the experiments with aquaculture water. Artificial white light (4.0 mW cm-2) and solar irradiation (40 mW cm-2) were used as light sources.

Propriedades intrínsecas e de processamento de termoplásticos elastoméricos incorporando borracha de pneu reciclada

O trabalho apresentado tem por objetivo contribuir para a valorização da borracha proveniente de pneus em fim de vida, assente em princípios de sustentabilidade ambiental. A abordagem adotada para a concretização deste objetivo consiste na incorporação de borracha de pneus em formulações de base termoplástica e elastomérica (TPE), adequadas ao processo de moldação por injeção. São desenvolvidos estudos sobre a morfologia, propriedades mecânicas, térmicas e reológicas das ligas poliméricas à base de granulado de borracha de pneu (GTR). A falta de adesão entre o GTR e a matriz polimérica leva à degradação das propriedades mecânicas dos materiais obtidos. A estratégia explorada passa pela utilização de um elastómero para promover o encapsulamento do GTR e, desta forma, procurar obter ligas com propriedades mecânicas características de um TPE. São analisadas ligas ternárias (TPEGTR) compostas por polipropileno (PP) de elevada fluidez, GTR e elastómero virgem. O efeito da presença de diferentes elastómeros nas ligas é analisado neste trabalho: um elastómero de etilenopropileno- dieno (EPDM), e um novo elastómero de etileno-propileno (EPR) obtido por catálise metalocénica. O estudo da morfologia das ligas obtidas mostra haver interação entre os materiais, sendo possível inferir a viabilidade da estratégia adotada para promover a adesão do GTR. A incorporação de elastómero promove o aumento da resistência ao impacto e da extensão na rotura nas ligas, o que é atribuído, fundamentalmente, ao encapsulamento do GTR e ao aumento da tenacidade da matriz termoplástica. Com o objetivo de avaliar a influência da estrutura cristalina das ligas TPEGTR no seu comportamento mecânico, procede-se à análise do processo de cristalização sob condições isotérmicas e não isotérmicas. Neste estudo, é avaliado o efeito da presença dos materiais que constituem a fase elastomérica na cinética de cristalização. Para cada uma das ligas desenvolvidas, recorre-se ao modelo de Avrami para avaliar o efeito da temperatura no mecanismo de nucleação, na morfologia das estruturas cristalinas e na taxa de cristalização. Recorre-se à reometria capilar para estudar, sob condições estacionárias, o comportamento reológico das ligas TPEGTR. O modelo de Cross-WLF é utilizado para avaliar o comportamento reológico de todos os materiais, obtendo-se resultados similares àqueles obtidos experimentalmente. O comportamento reológico dos polímeros PP, EPR e EPDM é do tipo reofluidificante, tendo o EPR um comportamento reológico similar ao do PP e o EPDM um comportamento reo-fluidificante mais pronunciado. Em todas as ligas analisadas o comportamento reológico revela-se do tipo reo-fluidificante, sendo que a presença de GTR promove o aumento da viscosidade. Os parâmetros obtidos do modelo de Cross-WLF são utilizados para realizar a simulação da etapa de injeção recorrendo a um software comercial. Os resultados obtidos são validados experimentalmente pelo processo de moldação por injeção, evidenciando uma boa adequabilidade da aplicação deste modelo a estas ligas. O trabalho desenvolvido sobre ligas TPEGTR, constitui um contributo para a valorização da borracha proveniente de pneus em fim de vida, assente em princípios de sustentabilidade ambiental.