Fabrication and evaluation of NiO/Y2O3-stabilized-ZrO2 hollow fibers for anode-supported micro-tubular solid oxide fuel cells

In this work NiO/3mol% Y₂O₃-ZrO₂ (3YSZ) and NiO/8mol% Y₂O₃-ZrO₂ (8YSZ) hollow fibers were prepared by phase-inversion. The effect of different kinds of YSZ (3YSZ and 8YSZ) on the porosity, electrical conductivity, shrinkage and flexural strength of the hollow fibers were systematically evaluated. When compared with Ni-8YSZ the porosity and shrinkage of Ni-3YSZ hollow fibers increases while the electrical conductivity decreases, while at the same time also exhibiting enhanced flexural strength. Single cells with Ni-3YSZ and Ni-8YSZ hollow fibers as the supported anode were successfully fabricated showing maximum power densities of 0.53 and 0.67Wcm^-2 at 800°C, respectively. Furthermore, in order to improve the cell performance, a Ni-8YSZ anode functional layer was added between the electrolyte and Ni-YSZ hollow fiber. Here enhanced peak power densities of 0.79 and 0.73Wcm^-2 were achieved at 800°C for single cells with Ni-3YSZ and Ni-8YSZ hollow fibers, respectively.

Fabrication and characterization of SSZ tape cast electrolyte-supported solid oxide fuel cells

A 10 mol%Sc₂O₃, 1 mol%CeO₂ stabilized-ZrO₂ (SSZ) powder was successfully prepared using the sol-gel method. Subsequent SSZ electrolyte pellets were prepared by tape casting technique and sintered at 1400 °C, 1450 °C, 1500 °C, 1550 °C and 1600 °C. These were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS). SSZ showed a pure cubic phase after sintering, the grain size of SSZ increased with the increase of sintering temperature. The SSZ sintered at 1550 °C showed the highest ion conductivity. The maximum power densities of Ni-SSZ/SSZ/La_0.8Sr_0.2MnO_3-δ (LSM)-SSZ single cells sintered at 1550 °C were 0.18, 0.36, 0.51 and 0.72 W cm^-2 at 650, 700, 750 and 800 °C, respectively. The polarization resistance (R_p) of the single cell attained 0.201 Ω cm² at 800 °C.

Evaluation of strontium-site-deficient Sr2Fe1.4Co0.1Mo0.5O6-δ-based perovskite oxides as intermediate temperature solid oxide fuel cell cathodes

In this paper strontium-site-deficient Sr₂Fe_1.4Co_0.1Mo_0.5O_6-δ-based perovskite oxides (S_xFCM) were prepared and evaluated as the cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFCs). All samples exhibited a cubic phase structure and the lattice shrinked with increasing the Sr-deficiency as shown in XRD patterns. XPS results determined that the transition elements (Co/Fe/Mo) in S_xFCM oxides were in a mixed valence state, demonstrating the small polaron hopping conductivity mechanism existed. Among the samples, S_1.950FCM presented the lowest coefficient of thermal expansion of 15.62 × 10^-6 K^-1, the highest conductivity value of 28 S cm^-1 at 500 °C, and the lowest interfacial polarization resistance of 0.093 Ω cm² at 800 °C, respectively. Furthermore, an anode-supported single cell with a S_1.950FCM cathode was prepared, demonstrating a maximum power density of 1.16 W cm^-2 at 800 °C by using wet H₂ (3% H₂O) as the fuel and ambient air as the oxidant. These results indicate that the introduction of Sr-deficiency can dramatically improve the electrochemical performance of Sr₂Fe_1.4Co_0.1Mo_0.5O_6-δ, showing great promise as a novel cathode candidate material for IT-SOFCs.