5 resultados para materials science and engineering
Resumo:
Two ferritic/martensitic steels, T91 steel and newly developed SIMP steel, were subject to tensile test after being oxidized in the liquid lead-bismuth eutectic (LBE) at 873 K for 500 h, 1000 h and 2000 h. Tensile tests were also carried out on the steels only thermally aged at 873 K. The result shows that thermal aging has no effect. Exposure to LBE at 873 K leads to a slight decrease in strength, but a large decrease in elongation when tested at 873 K. When tested at 873 K after 2000 h exposure, the tensile strength of T91 decreases slightly, and elongation from 39% to 21%. For SIMP, the decreases are slightly and from 44% to 28%, for tensile strength and elongation, respectively. The room temperature strength has slightly larger percentage reductions after the LBE exposure, but the elongation changes little.
Resumo:
Green composites are important class of biocomposites widely explored due to their enhanced properties. The biodegradable polymeric material is reinforced with natural fibers to form a composite that is eco-friendly and environment sustainable. The green composites have potential to attract the traditional petroleum-based composites which are toxic and nonbiodegradable. The green composites eliminate the traditional materials such as steel and wood with biodegradable polymer composites. The degradable and environment-friendly green composites were prepared by various fabrication techniques. The various properties of different fiber composite were studied as reinforcement for fully biodegradable and environmental-friendly green composites.
Resumo:
Botanically, green composites belong to an economically important seed plant family that includes maize, wheat, rice, and sorghum known as Saccharum offi cinarum. There are so many natural fibers available in the environment such as rice husk, hemp fibers, flax fibers, bamboo fibers, coconut fiber, coconut coir, grawia optiva and many others also. Life Cycle Assessment (LCA) is a process to estimate the environmental feature and potential impacts related to a product, by organizing a directory of pertinent inputs and outputs of a product system, assessing the potential environmental impacts related with the said inputs and outputs, explaining the results of the inventory analysis and impact evaluation phases in connection to the objectives of the study. Particularly Bagasse, an agricultural residue not only becomes a problem from the environmental point of view, but also affects the profitability of the sugarcane industries. This chapter discusses the properties, processing methods and various other aspects including economic and environmental aspects related to green composites.
Resumo:
Development of green composite from natural fibers has gained increasing interests due to the environmental and sustainable benefits when compared with petroleum based non-degradable materials. However, a big challenge of green composites is the diversity of fiber sources, because of the large variation in the properties and characteristics of the lignocellulosic renewable resource. The lignocellulosic fibers/natural fibers used to reinforce green composites are reviewed in this chapter. A classification of fiber types and sources, the properties of various natural fibers, including structure, composition, physical and chemical properties are focused; followed by the impacts of natural fibers on composite properties, with identification of the main pathways from the natural fibers to the green composite. Furthermore, the main challenges and future trend of natural fibers are highlighted.
Resumo:
Composite NiFe2O4–TiO2 magnetic catalysts were prepared by mechanochemical synthesis from a mixture of titania supported nickel ferrite nanoparticles and P25 titania (Evonic). The former provides fast and efficient heating under radiofrequency field, while the latter serves as an active catalyst or catalyst support. The highest heating rate was observed over a catalyst prepared for a milling time of 30 min. The catalytic activity was measured over the sulfated composite catalysts in the condensation of aniline and 3-phenylbutyric acid in a stirred tank reactor and in a continuous RF heated flow reactor in the 140–170 °C range. The product yield of 47% was obtained over the sulfated P25 titania catalyst in the flow reactor.