An investigation into the effect of thickness of titanium dioxide and gold-silver nanoparticle titanium dioxide composite thin-films on photocatalytic activity and photo-induced oxygen production in a sacrificial system

Thin films of titanium dioxide and titanium dioxide with incorporated gold and silver nanoparticles were deposited onto glass microscope slides, steel and titanium foil coupons by two sol-gel dip-coating methods. The film's photocatalytic activity and ability to evolve oxygen in a sacrificial solution were assessed. It was found that photocatalytic activity increased with film thickness (from 50 to 500 nm thick samples) for the photocatalytic degradation of methylene blue in solution and resazurin redox dye in an intelligent ink dye deposited on the surface. Contrastingly, an optimum film thickness of similar to 200 nm for both composite and pure films of titanium dioxide was found for water oxidation, using persulfate (S2O82-) as a sacrificial electron acceptor. The nanoparticle composite films showed significantly higher activity in oxygen evolution studies compared with plain TiO2 films.

An Experimental and Numerical Study of the Static and Fatigue Performance of a Composite Adhesive Repair

Experimental static and fatigue tension-tension tests were carried out on 5HS/RTM6 composite intact coupons and coupons incorporating adhesively-bonded (FM300-2) stepped flush joints. The results show that the adhesive joint, which is widely used in repairs, significantly reduces the static strength as well as the fatigue life of the composite. Both, the static and the fatigue failure of the ‘repaired’ coupons occur at the adhesive joint and involve crack initiation and propagation. The latter is modelled using interface finite elements based on the decohezive zone approach. The material degradation in the interface constitutive law is described by a damage variable, which can evolve due to the applied loads as well as the number of fatigue cycles. The fatigue formulation, based on a published model, is adapted to fit the framework of the pseudotransient formulation that is used as a numerical tool to overcome convergence difficulties. The fatigue model requires three material parameters. Numerical tests show that a single set of these parameters can be used to recover, very accurately, the experimental S-N relationship. Sensitivity studies show that the results are not mesh dependent.

Fatigue Life Assessment and Static Testing of Structural GFRP Tubes Based on Coupon Tests

Fiber-reinforced polymer (FRP) hollow tubes are used in structural applications, such as utility poles and pipelines. Concrete-filled FRP tubes (CFFTs) are also used as piles and bridge piers. Applications such as poles and marine piles are typically governed by cyclic bending. In this paper, the fatigue behavior of glass-FRP filament-wound tubes is studied using coupons cut from the tubes. Several coupon configurations were first examined in 24 tension and five compression monotonic loading tests. Fatigue tests were then conducted on 81 coupons to examine several parameters; namely, loading frequency as well as maximum-to-ultimate (max ult) and minimum-to-maximum (min max) stress ratios, including tension tension and tension compression, to simulate reversed bending. The study demonstrated the sensitivity of test results and failure mode to coupon configuration. The presence of compression loads reduced fatigue life, while increasing load frequency increased fatigue life. Stiffness degradation behavior was also established. To achieve at least one million cycles, it is recommended to limit (max ult) to 0.25. Models were used to simulate stiffness degradation and fatigue life curve of the tube. Fatigue life predictions of large CFFT beams showed good correlation with experimental results. © 2008 ASCE.

Microscopic Examination of Biofilm Destruction by Atmospheric Pressure Plasma

Objective: The aim of this study is to examine microscopically the destruction of bacterial biofilms mediated by atmospheric pressure non-thermal plasma (APNTP) at cellular level as well as at the level of biofilm structure as a whole. Methods: 3-day old bacterial biofilms were grown on polycarbonate coupons in a dual channel flow cell and were treated with an in-housed designed atmospheric pressure non-thermal plasma jet for up to 4 minutes of exposure before being examined by both confocal laser scanning microscopy (CLSM), preceded by Live/Dead bacterial viability staining, and scanning electron microscopy (SEM). Results: Differential live/dead staining followed by confocal microscopy examination revealed that biofilm eradication by APNTP was mediated by varying levels of both cell killing and physical removal. Relative extent of each mechanism was dependent on plasma operating conditions, bacterial species, growth conditions and biofilm thickness. On the other hand, SEM examination of plasma-exposed biofilms revealed a series of morphological changes exhibited by biofilm cells ranging from increased roughness of cell surface to complete cell lysis. Conclusions: Interesting mechanistic insights have been revealed by microscopic examination of plasma-treated bacterial biofilms that, when coupled with more specific biochemical studies, will not only contribute significantly to our understanding of the mechanism of plasma mediated biofilm destruction but also will help in better application-guided development of this novel anti-biofilm approach.

Interpretation of flat FRP coupon test results

The tensile strength obtained from existing testing methods such as ASTM D3039, based on flat coupons, usually has a large scatter for fibre reinforced polymer (FRP) composites. This means that the measured strength may not represent the actual strength of the material, leading to under or over design. This paper develops a new interpretation method which requires fewer tests, saving money and time. Moreover the results are more consistent and more closely represent the actual strength which can lead to a safer and more economical design.