Performance of calcium deficient hydroxyapatite-polyglycolic acid composites: An in vitro study

The strategic incorporation of bioresorbable polymeric additives to calcium-deficient hydroxyapatite cement may provide short-term structural reinforcement and modify the modulus to closer match bone. The longer-term resorption properties may also be improved, creating pathways for bone in-growth. The aim of this study was to investigate the resorption process of a calcium phosphate cement system containing either in polyglycolic acid tri-methylene carbonate particles or polyglycolic acid fibres. This was achieved by in vitro aging in physiological conditions (phosphate buffered solution at 37°C) over 12 weeks. The unreinforced CPC exhibited an increase in compressive strength at 12 weeks, however catastrophic failure was observed above a critical loading. The fracture behaviour of cement was improved by the incorporation of PGA fibres; the cement retained its cohesive structure after critical loading. Gravimetric analysis and scanning electron microscopy showed a large proportion of the fibres had resorbed after 12 weeks allowing for the increased cement porosity, which could facilitate cell infiltration and faster integration of natural bone. Incorporating the particulate additives in the cement did not provide any mechanism for mechanical property augmentation or did not demonstrate any appreciable level of resorption after 12 weeks.

Fracture Mechanics Analysis of the Dentine-Luting Cement Interface.

The objectives of this study were to determine the fracture toughness of adhesive interfaces between dentine and clinically relevant, thin layers of dental luting cements. Cements tested included a conventional glass-ionomer, F (Fuji I), a resin-modified glass-ionomer, FP (Fuji Plus) and a compomer cement, D (DyractCem). Ten miniature short-bar chevron notch specimens were manufactured for each cement, each comprising a 40 µm thick chevron of lute, between two 1.5 mm thick blocks of bovine dentine, encased in resin composite. The interfacial KIC results (MN/m3/2) were median (range): F; 0.152 (0.14-0.16), FP; 0.306 (0.27-0.37), D; 0.351 (0.31-0.37). Non-parametric statistical analysis showed that the fracture toughness of F was significantly lower (p