Dynamically mechanical and nano-impact (fatigue) analysis of touch screen thin films deposited on polyethylene terephthalate substrate

Nano-scale touch screen thin film have not been thoroughly investigated in terms of dynamic impact analysis under various strain rates. This research is focused on two different thin films, Zinc Oxide (ZnO) film and Indium Tin Oxide (ITO) film, deposited on Polyethylene Terephthalate (PET) substrate for the standard touch screen panels. Dynamic Mechanical Analysis (DMA) was performed on the ZnO film coated PET substrates. Nano-impact (fatigue) testing was performed on ITO film coated PET substrates. Other analysis includes hardness and the elastic modulus measurements, atomic force microscopy (AFM), Fourier Transform Infrared Spectroscopy (FTIR) and the Scanning Electron Microscopy (SEM) of the film surface.
Ten delta of DMA is described as the ratio of loss modulus (viscous properties) and storage modulus (elastic properties) of the material and its peak against time identifies the glass transition temperature (Tg). Thus, in essence the Tg recognizes changes from glassy to rubber state of the material and for our sample ZnO film, Tg was found as 388.3 K. The DMA results also showed that the Ten delta curve for Tg increases monotonically in the viscoelastic state (before Tg) and decreases sharply in the rubber state (after Tg) until recrystallization of ZnO takes place. This led to an interpretation that enhanced ductility can be achieved by negating the strength of the material.
For the nano-impact testing using the ITO coated PET, the damage started with the crack initiation and propagation. The interpretation of the nano-impact results depended on the characteristics of the loading history. Under the nano-impact loading, the surface structure of ITO film suffered from several forms of failure damages that range from deformation to catastrophic failures. It is concluded that in such type of application, the films should have low residual stress to prevent deformation, good adhesive strength, durable and good resistance to wear.

Informal strategies of power in the local planning system

Existing studies that question the role of planning as a state institution, whose interests it serves together with those disputing the merits of collaborative planning are all essentially concerned with the broader issue of power in society. Although there have been various attempts to highlight the distorting effects of power, the research emphasis to date has been focused on the operation of power within the formal structures that constitute the planning system. As a result, relatively little attention has been attributed to the informal strategies or tactics that can be utilised by powerful actors to further their own interests. This article seeks to address this gap by identifying the informal strategies used by the holders of power to bypass the formal structures of the planning system and highlight how these procedures are to a large extent systematic and (almost) institutionalised in a shadow planning system. The methodology consists of a series of semi-structured qualitative interviews with 20 urban planners working across four planning authorities within the Greater Dublin Area, Ireland. Empirical findings are offered that highlight the importance of economic power in the emergence of what essentially constitutes a shadow planning system. More broadly, the findings suggest that much more cognisance of the structural relations that govern how power is distributed in society is required and that ‘light touch’ approaches that focus exclusively on participation and deliberation need to be replaced with more radical solutions that look towards the redistribution of economic power between stakeholders.