An investigation into the behaviour of concrete containing seawater-neutralised bauxite refinery residues in silage effluent

The farm production of silage as a winter-feed supplement is widespread. However, the bins in which silage is produced are subject to acidic and microbial attacks. Both these types of attack can lead to a weakening and failure of the concretes, especially on the outer lip of the open side of the silage pit. Consequently, the development of an acid-resistant concrete that can extend the life span of silage bins on farms could lead to considerable cost savings for farmers and, hence, can improve farm productivity. This paper reports on test results of an investigation into the behaviour of concrete containing seawater-neutralised bauxite refinery residues (Bauxsol™) exposed to sulphuric acid environments in the laboratory and to silage effluents. The concrete manufactured had a fixed water–cement ratio of 0.55 and natural sand was replaced with the Bauxsol™ at 0%, 5%, 10%, 15% and 20% by cement mass. Results indicated that the use of Bauxsol™ as a sand replacement material improved the behaviour of concrete both in sulphuric acid in the laboratory as well as in the silage effluent. Consequently, it is concluded that the Bauxsol™ can be used to replace 10% of natural sand to produce concrete that is resistant to silage effluents, providing an extended service life over conventional concretes used in silage pits.

Preparation and characterisation of cellulose nanofibres

Two different procedures were compared for the preparation of cellulose nanofibres from flax and microcrystalline cellulose (MCC). The first involved a combination of high energy ball milling, acid hydrolysis and ultrasound, whilst the second employed a high pressure homogenisation technique, with and without various pre-treatments of the fibrous feedstock. The geometry and microstructure of the cellulose nanofibres were observed by SEM and TEM and their particle size measured using image analysis and dynamic light scattering. Aspect ratios of nanofibres made by microfluidisation were orders of magnitude greater than those achieved by acid hydrolysis. FTIR, XRD and TGA were used to characterise changes to chemical functionality, cellulose crystallinity and thermal stability resulting from the approaches used for preparing the cellulose nanofibres. Hydrolysis using sulphuric acid gave rise to esterification of the cellulose nanofibres, a decrease in crystallinity with MCC, but an increase with flax, together with an overall reduction in thermal stability. Increased shear history of flax subjected to multiple passes through the microfluidiser, raised both cellulose nanofibril crystallinity and thermal stability, the latter being strongly influenced by acid, alkaline and, most markedly, silane pretreatment.

Biorefining of perennial ryegrass for the production of nano-fibrillated cellulose

This study has demonstrated biorefining steps for ryegrass and silage at a pilot scale to extrude fibre cake for the production of nanofibrillated cellulose (NFC), a potentially green biomaterial for replacing conventional fillers in the manufacture of polymer composites. Further treatments of processed ryegrass fibres with mechanical shearing, microfluidising, hydrochloric acid (HCl)/ sulphuric acid and a four stage {ethylenediaminetetra-acetic acid, sodium hydroxide, sodium hypochlorite and HCl} hydrolysis yielded 43.8, 36.1, 25.6 and 39.8 kg t21 DM of NFCs respectively. The NFCs were characterised using microscopy, X-ray diffraction, dynamic light scattering, spectroscopy and thermogravimetry. The NFC had diameters from 3.0–9.1 nm and length 308 nm– 4.6 mm. NFC-polyvinyl alcohol composites containing NFC (5 wt%) exhibited enhanced Young’s modulus and thermal stability by factors of 2.5 and 2 respectively compared with control. The mass, energy, water and chemical balances of the four process steps were assessed to evaluate technical feasibility and also to provide baseline production data for scaling up. The microfluidised product has been identified as the best NFC product, but production cost needs to be reduced.

In situ FTIR spectroscopic studies of the oxidation of CO adsorbates on Ru(0 0 0 1) electrodes under open circuit conditions

This paper reports the first observation, using in situ FTIR spectroscopy, of the oxidation of CO adsorbates on the Ru(0001) electrode to CO under open circuit (oc) conditions in both perchloric acid and sulphuric acid solution at 20 and 55 °C. While the significant oc oxidation of the adsorbed CO on the Ru(0001) electrode was observed in perchloric acid solution, much less oc oxidation took place in sulfuric acid solution due to the specific adsorption of bisulfate at the Ru surface which inhibits the surface oxidation and reduces the reactivity of the surface towards the oxidation of CO . The oc oxidation of the CO depends strongly on the oxygen concentration in the solution and the temperature. The data so obtained are compared to those observed at the gas|solid interface, as well as to those obtained from the electro-oxidation of CO , and possible new catalytic oxidation reaction mechanisms are discussed. In addition, it is shown that the C-O frequency of the adsorbed CO may be used as an effective probe of the open circuit potential. © 2003 Elsevier B.V. All rights reserved.