Quantification of all-ceramic crown margin surface profile from try-in to 1-week post-cementation

To use profilometry to assess the margin surface profile of all-ceramic crowns (ACC’s) at try-in and 1-week after cementation with dual-cured resin (DC, RelyX ARC, 3 M ESPE, St. Paul, MN, USA), self-adhesive dual-cured resin (SADC, RelyX Unicem, 3 M ESPE), light-cured resin (LC, RelyX Veneer, 3 M ESPE) or chemically cured resin-modified glass ionomer (RMGI, RelyX Luting Plus, 3 M ESPE) luting cement. Methods: Forty, sound, extracted, human, premolar teeth underwent a standardised preparation for ACC’s. IPS Empress (Ivoclar-Vivadent, Liechtenstein) crowns of standard dimensions were fabricated and 10 luted with each cement and stored in water for 7 days. Three groups of serial profiles were taken, the first of the tooth preparation, the second of the crown margins at try-in and lastly of the crown margins after cementation and 7 days water storage. Results: There were no significant differences in the crown margin surface profile between the four cement groups at try-in. The change in crown margin position between try-in and post-cementation was significantly greater for DC than for LC and RMGI. SADC was not significantly different to the other cements. There were no significant differences in the crown margin extensions between the four cement groups, however most of the IPS Empress ACC’s in this study were underextended but this was not statistically significant. Conclusions: IPS Empress ACC’s seated more fully with LC and RMGI than with DC cement

Incorporation of multiwalled carbon nanotubes to acrylic based bone cements: Effects on mechanical and thermal properties

Polymethyl methacrylate (PMMA) bone cement–multiwalled carbon nanotube (MWCNT) nanocomposites with a weight loading of 0.1% were prepared using 3 different methods of MWCNT incorporation. The mechanical and thermal properties of the resultant nanocomposite cements were characterised in accordance with the international standard for acrylic resin cements. The mechanical properties of the resultant nanocomposite cements were influenced by the type of MWCNT and method of incorporation used. The exothermic polymerisation reaction for the PMMA bone cement was significantly reduced when thermally conductive functionalised MWCNTs were added. This reduction in exotherm translated in a decrease in thermal necrosis index value of the respective nanocomposite cements, which potentially could reduce the hyperthermia experienced in vivo. The morphology and degree of dispersion of the MWCNTs in the PMMA matrix at different scales were analysed using scanning electron microscopy. Improvements in mechanical properties were attributed to the MWCNTs arresting/retarding crack propagation through the cement by providing a bridging effect into the wake of the crack, normal to the direction of crack growth. MWCNT agglomerations were evident within the cement microstructure, the degree of these agglomerations was dependent on the method used to incorporate the MWCNTs into the cement.

Influence of multiwall carbon nanotube functionality and loading on mechanical properties of PMMA/MWCNT bone cements

Poly (methyl methacrylate) (PMMA) bone cement—multi walled carbon nanotube (MWCNT) nanocomposites with weight loadings ranging from 0.1 to 1.0 wt% were prepared. The MWCNTs investigated were unfunctionalised, carboxyl and amine functionalised MWCNTs. Mechanical properties of the resultant nanocomposite cements were characterised as per international standards for acrylic resin cements. These mechanical properties were influenced by the type and wt% loading of MWCNT used. The morphology and degree of dispersion of the MWCNTs in the PMMA matrix at different length scales were examined using field emission scanning electron microscopy. Improvements in mechanical properties were attributed to the MWCNTs arresting/retarding crack propagation through the cement by providing a bridging effect and hindering crack propagation. MWCNTs agglomerations were evident within the cement microstructure, the degree of these agglomerations was dependent on the weight fraction and functionality of MWCNTs incorporated into the cement.

Optimisation of a two-liquid component pre-filled acrylic bone cement system: A design of experiments approach to optimise cement final properties

The initial composition of acrylic bone cement along with the mixing and delivery technique used can influence its final properties and therefore its clinical success in vivo. The polymerisation of acrylic bone cement is complex with a number of processes happening simultaneously. Acrylic bone cement mixing and delivery systems have undergone several design changes in their advancement, although the cement constituents themselves have remained unchanged since they were first used. This study was conducted to determine the factors that had the greatest effect on the final properties of acrylic bone cement using a pre-filled bone cement mixing and delivery system. A design of experiments (DoE) approach was used to determine the impact of the factors associated with this mixing and delivery method on the final properties of the cement produced. The DoE illustrated that all factors present within this study had a significant impact on the final properties of the cement. An optimum cement composition was hypothesised and tested. This optimum recipe produced cement with final mechanical and thermal properties within the clinical guidelines and stated by ISO 5833 (International Standard Organisation (ISO), International standard 5833: implants for surgery—acrylic resin cements, 2002), however the low setting times observed would not be clinically viable and could result in complications during the surgical technique. As a result further development would be required to improve the setting time of the cement in order for it to be deemed suitable for use in total joint replacement surgery.

Fracture Mechanics Analysis of the Dentine-Luting Cement Interface.

The objectives of this study were to determine the fracture toughness of adhesive interfaces between dentine and clinically relevant, thin layers of dental luting cements. Cements tested included a conventional glass-ionomer, F (Fuji I), a resin-modified glass-ionomer, FP (Fuji Plus) and a compomer cement, D (DyractCem). Ten miniature short-bar chevron notch specimens were manufactured for each cement, each comprising a 40 µm thick chevron of lute, between two 1.5 mm thick blocks of bovine dentine, encased in resin composite. The interfacial KIC results (MN/m3/2) were median (range): F; 0.152 (0.14-0.16), FP; 0.306 (0.27-0.37), D; 0.351 (0.31-0.37). Non-parametric statistical analysis showed that the fracture toughness of F was significantly lower (p

Smart, Reusable labels for assessing self-cleaning films

Novel, reversible (reusable) photocatalyst activity indicator labels, which undergo a rapid colour change when in contact with a photocatalytic film via the photoreduction of methylene blue contained within the label’s adhesive, are explored as a method for assessing the activity of self-cleaning glass in situ and the laboratory, using digital photography.