Ferroelectricity in epitaxial pulsed laser deposited bismuth-layered perovskite thin films of different crystallographic orientations

Epitaxial thin films Of various bismuth-layered perovskites SrBi(2)Ta(2)O(9), Bi(4)Ti(3)O(12), BaBi(4)Ti(4)O(15), and Ba(2)Bi(4)Ti(5)O(18) were deposited by pulsed laser deposition onto epitaxial conducting LaNiO(3) or SrRuO(3) electrodes on single crystalline SrTiO(3) substrates with different crystallographic orientations or on top of epitaxial buffer layers on (100) silicon. The conductive perovskite electrodes and the epitaxial ferroelectric films are strongly influenced by the nature of the substrate, and bismuth-layered perovskite ferroelectric films with mixed (100), (110)- and (001)-orientations as well as with uniform (001)-, (116)- and (103)- orientations have been obtained. Structure and morphology investigations performed by X-ray diffraction analysis, scanning probe microscopy, and transmission electron microscopy reveal the different epitaxial relationships between films and substrates. A clear correlation of the crystallographic orientation of the epitaxial films with their ferroelectric properties is illustrated by macroscopic and microscopic measurements of epitaxial bismuth-layered perovskite thin films of different crystallographic orientations.

Preparation of La2NiO4+δ powders as a cathode material for SOFC via a PVP-assisted hydrothermal route

Uniform submicron La₂NiO_4+δ (sm-LNO) powders have been synthesized by a facile polyvinylpyrrolidone (PVP)-assisted hydrothermal route. In the presence of PVP, sm-LNO of pure phase has been obtained by calcination at the relatively low temperature of 900 °C for 8 h. Compared micron-sized LNO (m-LNO) particles obtained at 1,000 °C by hydrothermal synthesis route without PVP assisted, the sm-LNO-PVP displays regularly shaped and well-distributed particles in the range of 0.3–0.5 μm. The scanning electron microscopy (SEM) results showed that the sm-LNO sample is submicronic and that the m-LNO sample shows agglomerates with a broad size distribution. The electrochemical performance of m-LNO and sm-LNO-PVP has been investigated by electrochemical impedance spectroscopy. The polarization resistance of the sm-LNO-PVP cathode reaches a value of 0.40 Ω cm² at 750 °C, which is lower than that of m-LNO (0.62 Ω cm²). This result indicates that a fine electrode microstructure with submicron particles can help to increase the active sites, accelerate oxygen diffusion, and reduce polarization resistance. An anode-supported single cell with sm-LNO cathode has been fabricated and tested over a temperature range from 650 to 800 °C. The maximum power density of the cell has achieved 834 mW cm⁻² at 750 °C. These results therefore show that this PVP-assisted hydrothermal method is an effective approach to construct submicron-structured cathode and enhance the performance of intermediate temperature solid oxide fuel cell.