The modification of PLA and PLGA using electron-beam radiation

The degradable polymers polylactide (PLA) and polylactide-co-glycolide (PLGA) have found widespread use in modern medical practice. However, their slow degradation rates and tendency to lose strength before mass have caused problems. The aim of this study was to ascertain whether treatment with e-beam radiation could address these problems. Samples of PLA and PLGA were manufactured and placed in layered stacks, 8.1 mm deep, before exposure to 50 kGy of e-beam radiation from a 1.5 MeV accelerator. Gel permeation chromatography testing showed that the molecular weight of both materials was depth-dependent following irradiation, with samples nearest to the treated surface showing a reduced molecular weight. Samples deeper than 5.4 mm were unaffected. Computer modeling of the transmission of a 1.5 MeV e-beam in these materials corresponded well with these findings. An accelerated mass-loss study of the treated materials found that the samples nearest the irradiated surface initiated mass loss earlier, and at later stages showed an increased percentage mass loss. It was concluded that e-beam radiation could modify the degradation of bioabsorbable polymers to potentially improve their performance in medical devices, specifically for improved orthopedic fixation.

Anatomical study comparing the thickness of the volar and dorsal cortex of cadaveric adult distal radii using digital photography

INTRODUCTION:

Dorsally displaced fractures of the distal radius fractures are one of the commonest in day-to-day practice. There is still no consensus among surgeons regarding the suitability of using volar or the dorsal cortex as basis for internal fixation for dorsally displaced fractures.

BACKGROUND:

We report an anatomical study, which compares the thickness of the volar and dorsal cortices of cadaveric adult radii using digital photography.

RESULTS:

Results of this study show that the volar cortex was statistically, significantly thicker than the dorsal cortex. We believe that the volar cortex may behave as the calcar of the distal radius and hence internal fixation devices applied to the volar cortex may provide a more stable internal fixation compared to those based on the dorsal cortex.

The potential of electron beam irradiation for simultaneous surface modification and bioresorption control of PLLA for medical device applications

Bioresorbable polymers have been widely investigated as materials exhibiting significant potential for successful application in the medical fields of bone fixation devices and drug delivery. Further to the ability to control degradation, surface engineering of polymers has been highlighted as a key method central to their development. Previous work has demonstrated the ability of electron beam (e-beam) technology to control the degradation profiles and bioresorption of a number of commercially relevant bioresorbable polymers (poly-l-lactic acid (PLLA), L-lactide/ DL-lactide co-polymer (PLDL) and poly(lactic-co-glycolic acid) (PLGA). This work investigates the further potential of e-beam technology to impart added biofunctionality through the manipulation of polymer (PLLA) surface properties. A Dynamatron Continuous DC e-beam unit (Synergy Health, UK), with beam energies of 0.5, 0.75, and 1.5 MeV, was used for the irradiation of PLLA samples with delivered surface doses of 150 or 500 kGy at each energy level. The chosen conditions reflect the need to achieve a specific surface modification for the control of surface degradation as demonstrated in previous work. Surface characterization was then performed using contact angle analysis, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and atomic force microscopy.
Results demonstrated a significant increase in surface wettability post e-beam treatment. In correlation with this, XPS data showed the introduction of oxygen-containing functional groups to the surface of PLLA. Raman spectroscopy indicated chain scission in the near surface region of PLLA. E-beam irradiation did not seem to affect the surface roughness of PLLA as a direct consequence of the treatment. In conclusion electron beam surface modification has been found to modify both the surface-to-bulk bioresorption profile and the surface hydrophilicity. Both could provide benefits in relation to the performance of implantable medical devices.

Irradiation of bioresorbable biomaterials for controlled surface degradation

Bioresorbable polymers increasingly are the materials of choice for implantable orthopaedic fixation devices. Controlled degradation of these polymers is vital for preservation of mechanical properties during tissue repair and controlled release of incorporated agents such as osteoconductive or anti-microbial additives. The work outlined in this paper investigates the use of low energy electron beam irradiation to surface modify polyhydroxyacid samples incorporating beta tricalcium phosphate (β-TCP). This work uniquely demonstrates that surface modification of bioresorbable polymers through electron beam irradiation allows for the early release of incorporated agents such as bioactive additives. Samples were e-beam irradiated at an energy of 125 keV and doses of either 150 kGy or 500 kGy. Irradiated and non-irradiated samples were degraded in phosphate buffered saline (PBS), to simulate bioresorption, followed by characterisation. The results show that low energy e-beam irradiation enhances surface hydrolytic degradation in comparison to bulk and furthermore allows for earlier release of incorporated calcium via dissolution into the surrounding medium.