Dry gel conversion of organosilane templated mesoporous silica: from amorphous to crystalline catalysts for benzene oxidation

Mesoporous silica grown using [3-(trimethoxysilyl)propyl]octadecyldimethylammonium chloride as the mesoporogen in the presence of Fe and Al is X-ray amorphous, but contains very small domains with features of MFI zeolite as evidenced by IR and Raman spectroscopy. When applied as a catalyst, this amorphous sample shows good performance in the selective oxidation of benzene using nitrous oxide. Addition of tetrapropylammonium as structure directing agent to the as-synthesized mesoporous silica and subsequent dry gel conversion results in the formation of hierarchical Fe/ZSM-5 zeolite. During dry gel conversion the wormhole mesostructure of the initial material is completely lost. A dominant feature of the texture after crystallization is the high interconnectivity of micropores and mesopores. Substantial redistribution of low-dispersed Fe takes place during dry gel conversion towards highly dispersed isolated Fe species outside the zeolite framework. The catalytic performance in the oxidation of benzene to phenol of these highly mesoporous zeolites is appreciably higher than that of the parent material.

Hierarchical zeolites prepared by organosilane templating: A study of the synthesis mechanism and catalytic activity

The crystallization of hierarchical ZSM-5 in the presence of the organosilane octadecyl-dimethyl-(3-trimethoxysilyl-propyl)-ammonium chloride as the mesoporogen was investigated as a function of time and temperature. The synthesis by this method proceeds in two steps. The rapid formation of a predominantly amorphous disordered mesoporous aluminosilicate precursor phase is followed by the formation of globular highly mesoporous zeolite particles involving dissolution of the precursor phase. It is difficult to completely convert the initial phase into the final hierarchical zeolite. This limits the amount of aluminium built into the MFI network and the resulting Bronsted acidity. In the presence of iron, more crystalline hierarchical zeolite is obtained. These Fe-containing zeolites are excellent catalysts for the selective oxidation of benzene to phenol. Their hierarchical pore structure leads to higher reaction rates due to increased mass transfer and increased catalyst longevity despite more substantial coke formation. (C) 2011 Elsevier B.V. All rights reserved.

Mesoporous SSZ-13 zeolite prepared by a dual-template method with improved performance in the methanol-to-olefins reaction

Hierarchical SSZ-13 zeolites were synthesized by combining N,N,N-trimethyl-1-adamantanammonium hydroxide (TMAdOH) as the structure-directing agent for chabazite formation with mono- and diquaternary ammonium-type and organosilane mesoporogens and extensively characterized for their structural, textural, and catalytic properties. Mesoporous SSZ-13 zeolites can be synthesized in one step by combining TMAdOH and the diquaternary ammonium-type surfactant C22-4-4Br2. The mesopore volume increases with the mesoporogen/SDA ratio. The hierarchical zeolites are highly crystalline and exhibit similar Brønsted acidity as SSZ-13. Hierarchical SSZ-13 zeolites display increased lifetime in packed-bed MTO experiments than conventional SSZ-13 at similar light olefins yield. The increased lifetime is due to better utilization of the micropore space. With increasing mesoporosity, the micropore space is used more efficiently, but also the rate of coke formation at the crystal periphery increases. Accordingly, the most stable zeolite is obtained at a relatively low C22-4-4Br2/SDA ratio. These zeolite catalysts can be regenerated without substantial loss of activity.