Characterising cement-superplasticiser interaction using zeta potential measurements

The zeta potential generated at the interface between cement particle surfaces adsorbed with superplasticisers have been studied using electroacoustic technique, which is capable of measuring zeta potential at high concentrated suspensions. The study has been undertaken to examine the differences in the magnitude of the zeta potential for ordinary Portland cement (OPC) and Portland pozzolanic (fly ash) cement (PPC) pastes along with the differential impacts of different types of superplasticisers on both the varieties of cement pastes. In the latter context, the effects of three different types of superplasticisers namely Ligno Sulphonate (LS), Sulphonated Melamine Formaldehyde (SMF) and Sulphonated Naphthalene Formaldehyde (SNF) have been specifically studied. The results show that the cement pastes with PPC shows better dispersion when compared with the OPC. The paper also endeavors to unfold the relationship and significance of cement interaction with three different superplasticisers.

Mechanism of effluent attack on Portland cement and alkali activated mortars

The alkali activation of waste products has become a widespread topic of research, mainly due to environmental benefits. Portland cement and alkali-activated mortar samples were prepared to compare their resistance to silage effluent which contains lactic acid. The mechanism of attack on each sample has also been investigated.

'PERMIT' ion migration test for measuring the chloride ion transport of concrete on site

The ingress of chlorides into concrete is predominantly by the mechanism of diffusion and the resistance of concrete to the transport of chlorides is generally represented by its coefficient of diffusion. The determination of this coefficient normally requires long test duration (many months). Therefore, rapid test methods based on the electrical migration of ions have widely been used. The current procedure of chloride ion migration tests involves placing a concrete disc between an ion source solution and a neutral solution and accelerating the transport of ions from the source solution to the neutral solution by the application of a potential difference across the concrete disc. This means that, in order to determine the chloride transport resistance of concrete cover, cores should be extracted from the structure and tested in laboratories. In an attempt to facilitate testing of the concrete cover on site, an in situ ion migration test (hereafter referred to as PERMIT ion migration test for the unique identification of the new test) was developed. The PERMIT ion migration test was validated in the lab by carrying out a comparative investigation and correlating the results with the migration coefficient from the one-dimensional chloride migration test, the effective diffusion coefficient from the normal diffusion test and the apparent diffusion coefficient determined from chloride profiles. A range of concrete mixes made with ordinary Portland cement was used for this purpose. In addition, the effects of preferential flow of ions close to the concrete surface and the proximity of reinforcement within the test area on the in situ migration coefficients were investigated. It was observed that the in situ migration index, found in one working day, correlated well with the chloride diffusion coefficients from other tests. The quality of the surface layer of the cover concrete and the location of the reinforcement within the test area were found to affect the flow of ions through the concrete during the test. Based on the data, a procedure to carry out the PERMIT ion migration test was standardised.

Full-Scale Marine Exposure Tests on Treated and Untreated Concretes Initial 7-Year Results

An extensive chloride profiling program was undertaken on concrete pier stems erected in the vicinity of the Dornoch Bridge located at the Dornoch Firth in Northeast Scotland. The pier stems were 2 m (6.562 ft) high and octagonal in plan with 0.66 m (2.165 ft) wide faces. The piers were constructed in sets of three with the lowest of each set in the tidal zone and the highest in the atmospheric zone. The pier stems were placed in such a way that they would represent the exposure conditions of the actual bridge piers of the Dornoch Bridge. In all, six of the pier stems were made using plain ordinary portland cement (OPC) concrete (with three of these having the surface treated with silane); the remaining three pier stems had a concrete containing caltite as an additive. Three exposurezones were studied: the tidal zone, the splash zone, and the atmospheric zone. The tidal zone was further subdivided into two levels defined as low-level and high-level. Chloride profiles were obtained from the different regimes over a period of 7 years for all nine pier stems. This paper describes the nature of chloride ingress and the usefulness of diffusion parameters in classifying each exposure regimes. Furthermore, the effectiveness of silane and caltite in protecting concrete from chloride ingress in different exposure zones was studied.

Assessment of Self-Compacting Concrete Immersed in Acidic Solutions

Ettringite and thaumasite can be found among the deterioration products of cementitious materials exposed to sulfate and hydrochloric attack. The results of a test program to investigate the acid resistance of self-compacting concrete (SCC) and conventional concrete (CC), immersed up to 18 weeks at 20°C in sulfuric and hydrochloric acid solutions, are described. The SCC was prepared with 47% carboniferous limestone powder, as a replacement for cement, and an ordinary portland cement. The CC was prepared with portland cement only. The water-binder ratios of the SCC and CC were 0.36 and 0.46, respectively. The parameter investigated was the time, in weeks, taken to cause 10% mass loss of fully immersed concrete specimens in a 1% solution of sulfuric acid and the same amount of loss in a 1% solution of hydrochloric acid. The investigation indicated that the SCC performed better than the CC in sulfuric solution but was slightly more vulnerable to hydrochloric acid attack compared to CC. The mode of attack between the two solutions was different.

Carbonation and pH in Mortars Manufactured with Supplementary Cementitious Materials

An investigation of carbonation in mortars and methods of measuring the degree of carbonation and pH change is presented. The mortars were manufactured using ordinary portland cement, pulverized fuel ash, ground granulated blast-furnace slag, metakaolin, and microsilica. The mortars were exposed to a carbon dioxide-rich environment 5% CO2 to accelerate carbonation. The resulting carbonation was measured using phenolphthalein indicator and thermogravimetric analysis. The pH of the pore fluid and a powdered sample, extracted from the mortar, was measured to give an accurate indication of the actual pH of the concrete. The pH of the extracted powder mortar sample was found to be similar to the pH of the pore fluid expressed from the mortars. The thermogravimetric analysis suggested two distinct regions of transport of CO2 within mortar, a surface region where convection was prevalent and a deeper region where diffusion was dominant. The use of microsilica has been shown to decrease the rate of carbonation, while pulverized fuel ash and ground granulated blast-furnace slag have a detrimental effect on carbonation. Metakaolin has little effect on carbonation.

Alkali Activated Fuel Ash and Slag Mixes:Optimization Study from Mortars to Concrete Building Blocks

Alkali activated binders, based on ash and slag, also known as geopolymers, can play a key role in reducing the carbon footprint of the construction sector by replacing ordinary Portland cement in some concretes. Since 1970s, research effort has been ongoing in many research institutions. In this study, pulverized fuel ash (PFA) from a UK power plant, ground granulated blast furnace slag (GGBS) and combinations of the two have been investigated as geopolymer binders for concrete applications. Activators used were sodium hydroxide and sodium silicate solutions. Mortars with sand/binder ratio of 2.75 with several PFA and GGBS combinations have been mixed and tested. The optimization of alkali dosage (defined as the Na2O/binder mass ratio) and modulus (defined as the Na2O/SiO2 mass ratio) resulted in strengths in excess of 70 MPa for tested mortars. Setting time and workability have been considered for the identification of the best combination of PFA/GGBS and alkali activator dosage for different precast concrete products. Geopolymer concrete building blocks have been replicated in laboratory and a real scale factory trial has been successfully carried out. Ongoing microstructural characterization is aiming to identify reaction products arising from PFA/GGBS combinations.

Sustainable binders for concrete: a structured approach from waste screening to binder composition development

Worldwide, the building sector requires the production of 4 billion tonnes of cement annually, consuming more than 40% of global energy. Alkali activated “cementless” binders have recently emerged as a novel eco-friendly construction material with a promising potential to replace ordinary Portland cement. These binders consist of a class of inorganic polymer formed mainly by the reaction between an alkaline solution and an aluminosilicate source. Precursor materials for this reaction can be found in secondary material streams from different industrial sectors, from energy to agro-alimentary. However, the suitability of these materials in developing the polymerisation reaction must be assessed through a detailed chemical and physical characterisation, ensuring the availability of required chemical species in the appropriate quantity and physical state. Furthermore, the binder composition needs to be defined in terms of proper alkali activation dosages, water content in the mix, and curing conditions. The mix design must satisfy mechanical requirements and compliance to desired engineering properties (workability, setting time) for ensuring the suitability of the binder in replacing Portland cement in concrete applications. This paper offers a structured approach for the development of secondary material-based binders, from their identification to mix design and production procedure development. Essential features of precursor material can be determined through chemical and physical characterisation methods and advanced microscope techniques. Important mixing parameters and binder properties requirements are examined and some examples of developed binders are reported.

Alkali activated fuel ash and slag mixes:optimization study from paste to concrete building blocks

Alkali activated binders, based on ash and slag, also known as geopolymers, can play a key role in reducing the carbon footprint of the construction sector by replacing ordinary Portland cement in some concretes. Since 1970s, research effort has been ongoing in many research institutions. In this study, pulverized fuel ash (pfa) from a UK power plant, ground granulated blast furnace slag (ggbs) and combinations of the two have been investigated as geopolymer binders for concrete applications. Activators used were sodium hydroxide and sodium silicate solutions. Mortars with sand/binder ratio of 2.75 with several pfa and ggbs combinations have been mixed and tested. The optimization of alkali dosage (defined as the Na2O/binder mass ratio) and modulus (defined as the Na2O/SiO2 mass ratio) resulted in strengths in excess of 70 MPa for tested mortars. Setting time and workability have been considered for the identification of the best combination of pfa/ggbs and alkali activator dosage for different precast concrete products. Geopolymer concrete building blocks have been replicated in laboratory and a real scale factory trial has been successfully carried out. Ongoing microstructural characterization is aiming to identify reaction products arising from pfa/ggbs combinations.