Mineralogical characteristics and transformations during long-term operation of a zero-valent iron reactive barrier

Received for publication October 31, 2002. Design and operation of Fe0 permeable reactive barriers (PRBs) can be improved by understanding the long-term mineralogical transformations that occur within PRBs. Changes in mineral precipitates, cementation, and corrosion of Fe0 filings within an in situ pilot-scale PRB were examined after the first 30 months of operation and compared with results of a previous study of the PRB conducted 15 months earlier using X-ray diffraction and scanning electron microscopy employing energy dispersive X-ray and backscatter electron analyses. Iron (oxy)hydroxides, aragonite, and maghemite and/or magnetite occurred throughout the cores collected 30 mo after installation. Goethite, lepidocrocite, mackinawite, aragonite, calcite, and siderite were associated with oxidized and cemented areas, while green rusts were detected in more reduced zones. Basic differences from our last detailed investigation include (i) mackinawite crystallized from amorphous FeS, (ii) aragonite transformed into calcite, (iii) akaganeite transformed to goethite and lepidocrocite, (iv) iron (oxy)hydroxides and calcium and iron carbonate minerals increased, (v) cementation was greater in the more recent study, and (vi) oxidation, corrosion, and disintegration of Fe0 filings were greater, especially in cemented areas, in the more recent study. If the degree of corrosion and cementation that was observed from 15 to 30 mo after installation continues, certain portions of the PRB (i.e., up-gradient entrance of the ground water to the Fe0 section of the PRB) may last less than five more years, thus reducing the effectiveness of the PRB to mitigate contaminants. Abbreviations: EDX, energy dispersive X-ray • Fe0, zerovalent iron • PRB, permeable reactive barrier • SEM, scanning electron microscopy • XRD, X-ray diffraction

Impact of sample preparation on mineralogical analysis of iron reactive barrier materials

Permeable reactive barriers (PRBs) of zero-valent iron (Fe0) are increasingly being used to remediate contaminated ground water. Corrosion of Fe0 filings and the formation of precipitates can occur when the PRB material comes in contact with ground water and may reduce the lifespan and effectiveness of the barrier. At present, there are no routine procedures for preparing and analyzing the mineral precipitates from Fe0 PRB material. These procedures are needed because mineralogical composition of corrosion products used to interpret the barrier processes can change with iron oxidation and sample preparation. The objectives of this study were (i) to investigate a method of preparing Fe0 reactive barrier material for mineralogical analysis by X-ray diffraction (XRD), and (ii) to identify Fe mineral phases and rates of transformations induced by different mineralogical preparation techniques. Materials from an in situ Fe0 PRB were collected by undisturbed coring and processed for XRD analysis after different times since sampling for three size fractions and by various drying treatments. We found that whole-sample preparation for analysis was necessary because mineral precipitates occurred within the PRB material in different size fractions of the samples. Green rusts quickly disappeared from acetone-dried samples and were not present in air-dried and oven-dried samples. Maghemite/magnetite content increased over time and in oven-dried samples, especially after heating to 105°C. We conclude that care must be taken during sample preparation of Fe0 PRB material, especially for detection of green rusts, to ensure accurate identification of minerals present within the barrier system.

Microbiological characteristics in a zero-valent iron reactive barrier

Zero-valent iron (Fe0)-based permeable reactive barriertreatment has been generating great interest for passivegroundwater remediation, yet few studies have paid particularattention to the microbial activity and characteristics withinand in the vicinity of the Fe0-barrier matrix. The presentstudy was undertaken to evaluate the microbial population andcommunity composition in the reducing zone of influence byFe0 corrosion in the barrier at the Oak Ridge Y-12 Plantsite. Both phospholipid fatty acids and DNA analyses were usedto determine the total microbial population and microbialfunctional groups, including sulfate-reducing bacteria,denitrifying bacteria, and methanogens, in groundwater andsoil/iron core samples. A diverse microbial community wasidentified in the strongly reducing Fe0 environment despitea relatively high pH condition within the Fe0 barrier (up topH 10). In comparison with those found in the backgroundsoil/groundwater samples, the enhanced microbial populationranged from 1 to 3 orders of magnitude and appeared to increase from upgradient of the barrier to downgradient soil. Inaddition, microbial community composition appeared to change overtime, and the bacterial types of microorganismsincreased consistently as the barrier aged. DNA analysisindicated the presence of sulfate-reducing and denitrifyingbacteria in the barrier and its surrounding soil. However, theactivity of methanogens was found to be relatively low,presumably as a result of the competition by sulfate/metal-reducing bacteria and denitrifying bacteria because of the unlimited availability of sulfate and nitrate in the site groundwater. Results of this study provide evidenceof a diverse microbial population within and in the vicinity ofthe iron barrier, although the important roles of microbial activity, either beneficially or detrimentally, on the longevityand enduring efficiency of the Fe0 barriers are yet to be evaluated.

Electron-impact ionization of hydrogen-like iron ions

Electron-impact ionization cross sections have been determined for hydrogen like iron ions at selected electron energies between 1.45 and 4.3 times the threshold energy. The cross sections were obtained by measuring the equilibrium ionization balance in an electron beam ion trap. This ionization balance is obtained from x-ray measurements of radiative recombination into the K-shell of hydrogen-like and bare iron ions. The measured cross sections are compared with distorted-wave calculations and several semiempirical formulations.