A case study with a novel geometry for pulsed laser deposition

Aluminium thin films were deposited by a laser ablation technique from solid cylindrical targets rotated on a lead screw. Both smooth-surfaced targets and targets with screw threads cut into the area to he irradiated were used. The targets were irradiated with a focused circular spot size of 2.5 mm in diameter, at a power density equal to 5.4 +/- 0.2 x 10(8) W cm(-2). The polar distribution of the ablated atomic material was found to vary as a function of the target screw thread pitch, with the exponent n, in the polar distribution f(theta) = cos(n) theta, varying from 13.5 +/- 1.3 for no pitch to a minimum of 5 +/- 0.7 for a screw thread pitch of 0.2 mm. The use of such novel target geometries forms a possible basis for increasing thickness uniformity during the pulsed laser deposition of thin films.

Analysis of the compressive behaviour of the three-dimensional printed porous titanium for dental implants using a modified cellular solid model

A set of cylindrical porous titanium test samples were produced using the three-dimensional printing and sintering method with samples sintered at 900 °C, 1000 °C, 1100 °C, 1200 °C or 1300 °C. Following compression testing, it was apparent that the stress-strain curves were similar in shape to the curves that represent cellular solids. This is despite a relative density twice as high as what is considered the threshold for defining a cellular solid. As final sintering temperature increased, the compressive behaviour developed from being elastic-brittle to elastic-plastic and while Young's modulus remained fairly constant in the region of 1.5 GPa, there was a corresponding increase in 0.2% proof stress of approximately 40-80 MPa. The cellular solid model consists of two equations that predict Young's modulus and yield or proof stress. By fitting to experimental data and consideration of porous morphology, appropriate changes to the geometry constants allow modification of the current models to predict with better accuracy the behaviour of porous materials with higher relative densities (lower porosity).