Transesterification of vegetable oils on basic large mesoporous alumina supported alkaline fluorides-Evidences of the nature of the active site and catalytic performances

KF, LiF and CsF/A(2)O(3) catalysts with different loadings from 1 to 20 wt% were prepared using aqueous solutions of the alkaline fluoride compounds by wet impregnation of basic mesoporous MSU-type alumina. The catalysts were activated under At at 400 degrees C for 2 h and monitored by in situ XRD measurements. The catalysts were also characterized using several techniques: N-2 adsorption/desorption isotherms at -196 degrees C, FTIR, DR-UV-vis, CO2-TPD, XRD, Al-27 CP/MAS NMR. These characterizations led to the conclusion that the deposition of alkaline fluorides on the alumina surface generates fluoroaluminates and aluminate species. The process is definitivated at 400 degrees C. The fluorine in these structures is less basic than in the parent fluorides, but the oxygen becomes more basic. The catalysts were tested for the transesterification of fatty esters under different experimental conditions using conventional heating, microwave and Ultrasound irradiation. Recycling experiments showed that these catalysts are stable for a limited number of cycles. (C) 2009 Elsevier Inc. All rights reserved.

Ultracold fluorine production via Doppler cooled BeF

Large parts of the periodic table cannot be cooled by current laser-based methods. We investigate whether zero energy fragmentation of laser cooled fluorides is a potential source of ultracold fluorine atoms. We report new ab initio calculations on the lowest electronic states of the BeF diatomic molecule including spin-orbit coupling, the calculated minima for the valence electronic states being within 1 pm of the spectroscopic values. A four colour cooling scheme based on the A2? ? X2S+ transition is shown to be feasible for this molecule. Multi-Reference Configuration Interaction (MRCI) potentials of the lowest energy Rydberg states are reported for the first time and found to be in good agreement with experimental data. A series of multi-pulse excitation schemes from a single rovibrational level of the cooled molecule are proposed to produce cold fluorine atoms.

From non-porous crystalline to amorphous microporous metal(IV) bisphosphonates

Porous layered hybrid materials have been prepared by the reaction of organo-bisphosphonate ligands, 4-(4'-phosphonophenoxy)phenylphosphonic, 4,4'-biphenylenbisphosphonic and phenylphosphonic acids, with metal(IV) cations (Zr and Sn). Crystalline Zr(IV) and Sn(IV) layered bisphosphonates were also prepared, which were non-porous. The amorphous M(IV) bisphosphonates showed variable compositions and textural properties ranging from mainly mesoporous to highly microporous solids with BET surface areas varying from 300 to 480 m(2) g(-1), micropore volumes ranging 0.10-0.20 cm(3)/g, and narrow porous size distributions for some materials. N-2 isotherms suggest that Sn(IV) derivatives show a comparatively higher micropore contribution than the Zr(IV) analogous at least for the ether-bisphosphonate hybrids. Sn(IV) bisphosphonates exhibit high microporosities without the need of using harmful DMSO as solvent. If ether-bisphosphonic acid is partially replaced by less expensive phenylphosphonic ligand, porous products are also obtained. P-31 and F-17 MAS NMR and XPS data revealed the presence of hydrogen-phosphonate groups and small (F-, Cl- and OH-) anions, which act as spacer ligands within the inorganic layers, in these hybrid materials. The complexity of the inorganic layers is higher for the Sn(IV) bisphosphonates likely due to the larger amount of small bridging anions including fluorides. It is suggested that the presence of these small inorganic ligands may be a key factor influencing both, the interaction of the inorganic layer with the bisphosphonate groups, which bridge the inorganic layers, and the generation of internal voids within a given inorganic layer. Preliminary studies of gases adsorption (H-2 and NO) have been carried out for selected Sn(IV) bisphosphonates. The H-2 adsorption capacity at 77 K and 1 bar was low, 0.26 wt%, but the NO adsorption capacity at similar to 1 bar and 298 K was relatively high, 4.2 wt%. Moreover, the hysteresis in the NO isotherms is indicative of partial strong irreversible adsorption of NO. (C) 2008 Elsevier Inc. All rights reserved.