Synthesis and Thermophysical Properties of Ether Functionalized Sulfonium Ionic Liquids as Potential Electrolytes for Electrochemical Applications

During this work, a novel series of hydrophobic room temperature ionic liquids (ILs) based on five ether functionalized sulfonium cations bearing the bis(trifluoromethyl)sulfonylimide, [NTf2]- anion were synthesized and characterized. Their physicochemical properties, such as density, viscosity and ionic conductivity, electrochemical window along with thermal properties including phase transition behavior and decomposition temperature, have been measured. All of these ILs showed large liquid range temperature, low viscosity and good conductivity. Additionally, by combining DFT calculations along with electrochemical characterization it appears that these novel ILs show good electrochemical stability windows, suitable for the potential application as electrolyte materials in electrochemical energy storage devices.

An ether-functionalised cyclic sulfonium based ionic liquid as an electrolyte for electrochemical double layer capacitors

A novel cyclic sulfonium cation-based ionic liquid (IL) with an ether-group appendage and the bis{(trifluoromethyl)sulfonyl}imide anion was synthesised and developed for electrochemical double layer capacitor (EDLC) testing. The synthesis and chemical-physical characterisation of the ether-group containing IL is reported in parallel with a similarly sized alkyl-functionalised sulfonium IL. Results of the chemical-physical measurements demonstrate how important transport properties, i.e. viscosity and conductivity, can be promoted through the introduction of the ether-functionality without impeding thermal, chemical or electrochemical stability of the IL. Although the apparent transport properties are improved relative to the alkyl-functionalised analogue, the ether-functionalised sulfonium cation-based IL exhibits moderately high viscosity, and poorer conductivity, when compared to traditional EDLC electrolytes based on organic solvents (propylene carbonate and acetonitrile). Electrochemical testing of the ether-functionalised sulfonium IL was conducted using activated carbon composite electrodes to inspect the performance of the IL as a solvent-free electrolyte for EDLC application. Good cycling stability was achieved over the studied range and the performance was comparable to other solvent free,
IL-based EDLC systems. Nevertheless, limitations of the attainable performance are primarily the result of sluggish transport properties and a restricted operative voltage of the IL, thus highlighting key aspects of this field which require further attention.

Facile synthesis of copper-manganese spinel anodes with high capacity and cycling performance for lithium-ion batteries

Copper-manganese spinel containing anodes were synthesized by a facile sol-gel method and evaluated in lithium-ion battery applications for the first time. The synergistic effects between copper-manganese and the aqueous binder (sodium carboxymethyl cellulose) provided a high specific capacity and excellent cycling performance. It was found that the specific capacity of the copper-manganese spinel remained at 608 mAh g⁻¹ after 100 cycles at a current density of 200 mA g⁻¹. Furthermore, a relatively high reversible capacity of 278 mAh g⁻¹ could be obtained at a current density of 2000 mA g⁻¹, indicating a good rate capability. These studies suggest that copper-manganese spinel is a promising material for lithium-ion battery applications due to a combination of good electrochemical performance and low cost.

Synthesis of Pr0.6Sr0.4FeO 3-δ -xCe0.9Pr0.1O 2-δ cobalt-free composite cathodes by a one-pot method for intermediate-temperature solid oxide fuel cells

Cobalt-free composite cathodes consisting of Pr_0.6Sr_0.4FeO _3-δ -xCe_0.9Pr_0.1O _2-δ (PSFO-xCPO, x = 0-50 wt%) have been synthesized using a one-pot method. X-ray diffraction, scanning electron microscopy, thermal expansion coefficient, conductivity, and polarization resistance (R _P ) have been used to characterize the PSFO-xCPO cathodes. Furthermore the discharge performance of the Ni-SSZ/SSZ/GDC/PSFO-xCPO cells has been measured. The experimental results indicate that the PSFO-xCPO composite materials fully consist of PSFO and CPO phases and posses a porous microstructure. The conductivity of PSFO-xCPO decreases with the increase of CPO content, but R _P of PSFO-40CPO shows the smallest value amongst all the samples. The power density of single cells with a PSFO-40CPO composite cathode is significantly improved compared with that of the PSFO cathode, exhibiting 0.43, 0.75, 1.08 and 1.30 W cm^-2 at 650, 700, 750 and 800 °C, respectively. In addition, single cells with the PSFO-40CPO composite cathode show a stable performance with no obvious degradation over 100 h when operating at 750 °C.