Performance of calcium deficient hydroxyapatite-polyglycolic acid composites: An in vitro study

The strategic incorporation of bioresorbable polymeric additives to calcium-deficient hydroxyapatite cement may provide short-term structural reinforcement and modify the modulus to closer match bone. The longer-term resorption properties may also be improved, creating pathways for bone in-growth. The aim of this study was to investigate the resorption process of a calcium phosphate cement system containing either in polyglycolic acid tri-methylene carbonate particles or polyglycolic acid fibres. This was achieved by in vitro aging in physiological conditions (phosphate buffered solution at 37°C) over 12 weeks. The unreinforced CPC exhibited an increase in compressive strength at 12 weeks, however catastrophic failure was observed above a critical loading. The fracture behaviour of cement was improved by the incorporation of PGA fibres; the cement retained its cohesive structure after critical loading. Gravimetric analysis and scanning electron microscopy showed a large proportion of the fibres had resorbed after 12 weeks allowing for the increased cement porosity, which could facilitate cell infiltration and faster integration of natural bone. Incorporating the particulate additives in the cement did not provide any mechanism for mechanical property augmentation or did not demonstrate any appreciable level of resorption after 12 weeks.

Multilayered glass fibre-reinforced composites in rotational moulding

The potential of multiple layer fibre-reinforced mouldings is of growing interest to the rotational moulding industry because of their cost/performance ratio. The particular problem that arises when using reinforcements in this process relate to the fact that the process is low shear and good mixing of resin and reinforcement is not optimum under those conditions. There is also a problem of the larger/heavier reinforcing agents segregating out of the powder to lay up on the inner part surface. In this study, short glass fibres were incorporated and distributed into a polymer matrix to produce fibre-reinforced polymer composites using the rotational moulding process and characterised in terms of morphology and mechanical properties. © 2011 American Institute of Physics.

Glass fibre-reinforced polyethylene composites in rotational moulding

Fibre-reinforced mouldings are of growing interest to the rotational moulding industry due to their outstanding price performance ratio. However, a particular problem that arises when using reinforcements in this process is that the process is low shear and good mixing of resin and reinforcement is not optimum under those conditions. There is also a problem of the larger/heavier reinforcing agents segregating out of the powder to lay up on the inner part surface. In this paper we report on studies to incorporate, short glass fibres into rotationally moulded parts. Four different approaches were investigated; direct addition of fibre in between two powder shots, addition of a layer of pre-compounded polyethylene-glass fibre pellets between two powder shots, addition of a layer of pre-compounded polyethylene-glass fibre powder between two powder shots and a single layer of glass-reinforced, pre-compounded powder. Results indicate that pre-compounding is necessary to gain performance enhancement and the single layer part made from glass-reinforced, pre-compounded powder exhibited the highest tensile and flexural modulus.