Abatement of nitrous oxide over natural and iron modified natural zeolites

The natural zeolite obtained from the Sivas-Yavu region in Turkey and iron modified forms were studied for the decomposition of N2O and selective catalytic reduction of N2O with NH3. The natural and iron modified zeolites were characterised by XRD, SEM, H-2-TPR, NH3-TPD and low temperature nitrogen sorption. The effect iron loading, precursor and valency on the catalytic performance of catalysts were studied. The catalytic activity of the zeolites increased up to about 7.0 wt.% Fe. Above this value, the activity decreased as a result of a reduction in the surface area and pore volume of the zeolite. The highest catalytic activity was observed using catalysts prepared with FeCl2 due to the formation of more reducible iron species in the zeolites. When FeSO4 was used as the iron precursor, sulphate remained on the surface even after extensive washing resulting in a decrease in the N2O decomposition activity and a shift the N2O reduction temperature to higher values. Since the natural and iron exchanged natural zeolites prepared using FeCl2 have comparable activity with synthetic zeolites, the offer a promising alternative catalyst for the abatement of N2O, particularly for the selective reduction of N2O with NH3. (C) 2011 Elsevier B.V. All rights reserved.

The transformation of cyclohexane on Zn/H-ZSM-5 zeolites

Samples of Zn/H-ZSM-5 zeolite were prepared by impregnation of the parent zeolite with Zn(NO3)(2). The state of zinc in the samples was analyzed by XPS measurements, (ald the degree of reduction for the zinc oxide on the ZSM-5 zeolite surface in hydrogen atmosphere was determined, as well as the influence of this reducing treatment upon the activity and selectivity for aromatics of zeolites in aromatization of cyclohexane. It resulted that the degree of reduction depends on the concentration of zinc in the zeolite and is influenced by the presence of alumina binder. The results of the activity and selectivity to aromatics were correlated with the reduction of zinc oxide.

The effect of various treatment conditions on natural zeolites: Ion exchange, acidic, thermal and steam treatments

Two different natural zeolites having different phase compositions were obtained from different regions of Turkey and modified by ion-exchange (0.5 M NH4NO3) and acid leaching using 1 M HCl. The natural and modified samples were treated at low temperature (LT), high temperature (HT) and steam (ST) conditions and characterised by XRF, XRD, BET, FTIR, DR-UV-Vis, NH3-TPD and TGA. Ion-exchange with NH4+ of natural zeolites results in the exchange of the Na+ and Ca2+ cations and the partial exchange of the Fe3+ and Mg2+ cations. However, steam and acidic treatments cause significant dealumination and decationisation, as well as loss of crystalline, sintering of phases and the formation of amorphous material. The presence of mordenite and quartz phases in the natural zeolites increases the stability towards acid treatment, whereas the structure of clinoptilolite-rich zeolites is mostly maintained after high temperature and steam treatments. The natural and modified zeolites treated at high temperature and in steam were found to be less stable compared with synthetic zeolites, resulting in a loss of crystallinity, a decrease in the surface area and pore volume, a decrease in the surface acidity as well as dealumination, and decationisation. (C) 2012 Elsevier Inc. All rights reserved.

Hierarchical zeolites prepared by organosilane templating: A study of the synthesis mechanism and catalytic activity

The crystallization of hierarchical ZSM-5 in the presence of the organosilane octadecyl-dimethyl-(3-trimethoxysilyl-propyl)-ammonium chloride as the mesoporogen was investigated as a function of time and temperature. The synthesis by this method proceeds in two steps. The rapid formation of a predominantly amorphous disordered mesoporous aluminosilicate precursor phase is followed by the formation of globular highly mesoporous zeolite particles involving dissolution of the precursor phase. It is difficult to completely convert the initial phase into the final hierarchical zeolite. This limits the amount of aluminium built into the MFI network and the resulting Bronsted acidity. In the presence of iron, more crystalline hierarchical zeolite is obtained. These Fe-containing zeolites are excellent catalysts for the selective oxidation of benzene to phenol. Their hierarchical pore structure leads to higher reaction rates due to increased mass transfer and increased catalyst longevity despite more substantial coke formation. (C) 2011 Elsevier B.V. All rights reserved.

Catalytic performance of sheet-like Fe/ZSM-5 zeolites for the selective oxidation of benzene with nitrous oxide

Hierarchical Fe/ZSM-5 zeolites were synthesized with a diquaternary ammonium surfactant containing a hydrophobic tail and extensively characterized by XRD, Ar porosimetry, TEM, DRUV-Vis, and UV-Raman spectroscopy. Their catalytic activities in catalytic decomposition of NO and the oxidation of benzene to phenol with NO as the oxidant were also determined. The hierarchical zeolites consist of thin sheets limited in growth in the b-direction (along the straight channels of the MFI network) and exhibit similar high hydrothermal stability as a reference Fe/ZSM-5 zeolite. Spectroscopic and catalytic investigations point to subtle differences in the extent of Fe agglomeration with the sheet-like zeolites having a higher proportion of isolated Fe centers than the reference zeolite. As a consequence, these zeolites have a somewhat lower activity in catalytic NO decomposition (catalyzed by oligomeric Fe), but display higher activity in benzene oxidation (catalyzed by monomeric Fe). The sheet-like zeolites deactivate much slower than bulk Fe/ZSM-5, which is attributed to the much lower probability of secondary reactions of phenol in the short straight channels of the sheets. The deactivation rate decreases with decreasing Fe content of the Fe/ZSM-5 nanosheets. It is found that carbonaceous materials are mainly deposited in the mesopores between the nanosheets and much less so in the micropores. This contrasts the strong decrease in the micropore volume of bulk Fe/ZSM-5 due to rapid clogging of the continuous micropore network. The formation of coke deposits is limited in the nanosheet zeolites because of the short molecular trafficking distances. It is argued that at high Si/Fe content, coke deposits mainly form on the external surface of the nanosheets. © 2012 Elsevier Inc. All rights reserved.

NO-releasing zeolites and their antithrombotic properties

Transition metal-exchanged zeolite-A adsorbs and stores nitric oxide in relatively high capacity (up to 1 mmol of NO/g of zeolite). The stored NO is released on contact with an aqueous environment under biologically relevant conditions of temperature and pH. The release of the NO can be tuned by altering the chemical composition of the zeolite, by controlling the amount of water contacting the zeolite, and by blending the zeolite with different polymers. The high capacity of zeolite for NO makes it extremely attractive for use in biological and medical applications, and our experiments indicate that the NO released from Co-exchanged zeolite-A inhibits platelet aggregation and adhesion of human platelets in vitro.

The adsorption, storage and release of nitric oxide using ion exchanged zeolites

Zeolites exchanged with transition metal cations Co2+, Mn2+, Zn2+ and Cu2+ are capable of storing and delivering a large quantity of nitric oxide in a range of 1.2-2.7 mmolg(-1). The metal ion exchange impacts the pore volumes of zeolite FAU more significantly than LTA. The storage of NO mainly involves coordination of NO to metal cation sites. By exposing zeolites to a moisture atmosphere, the stored nitric oxide can be released. The NO release takes more than 2 hours for the NO concentration decreasing below similar to 5ppb in outlet gas. Its release rate can be controlled by tailoring zeolite frameworks and optimising release conditions.

Simultaneous Gas Storage and Catalytic Gas Production Using Zeolites-A New Concept for Extending Lifetime Gas Delivery

Copper containing MCM-41 materials can be used to both store gaseous nitric oxide and to catalytically produce nitric oxide from nitrite. The active species for the reaction is copper (I). Addition of cysteine to the solution in contact with the material has different effects depending on how much Cu(I) is present. This is a new method of extending the lifetime of gas delivery from a gas storage material.

Simultaneous and cooperative gas storage and gas production using bifunctional zeolites

Nitric oxide can be stored in and produced from zeolites in a simultaneous and cooperative process

Acidic properties of nanolayered ZSM-5 zeolites

The acidic properties of nanolayered ZSM-5 zeolites synthesized with the aid of multiquaternary ammonium surfactants were investigated in detail. A substantial fraction of Al is present in highly dispersed form at extraframework positions indicative of the defective nature of the calcined nanolayered zeolites. Acidity characterization reveals that the Brønsted acid sites are similar in strength to those in bulk HZSM-5. Nanolayered zeolites contain a higher amount of Brønsted acid sites (BAS) at their external (mesopore) surface. Unilamellar zeolites have a higher concentration of external BA and silanol sites than multilamellar ones. The number of BAS in the nanolayered zeolites is considerably lower than the tetrahedral Al content, the difference increasing with nanolayer thickness. Except for one particular sample (nanolayered ZSM-5 synthesized from COH template), the total turnover of methanol normalized per BAS trends inversely with the concentration of BAS. There is no correlation with the concentration of external BAS. Catalyst deactivation due to coke mainly depends on the BAS concentration. A unilamellar ZSM-5 zeolite prepared using COH displayed substantially improved performance in terms of a much lower rate of coke deactivation in line with earlier data Choi et al. [10]. Since the acidic and textural properties of this zeolite did not differ significantly from the others, it remains to be determined why this zeolite performs so much better. © 2013 Elsevier Ltd. All rights reserved.