Stripe domain structure in epitaxial (001) BiFeO3 thin films on orthorhombic TbScO3 substrate

We have analyzed the ferroelastic and ferroelectric domain structure of high crystalline quality (001) BiFeO3 films on orthorhombic (110) TbScO3 substrates. Two domains were present in stripes separated by (010) vertical boundaries, with spontaneous polarizations in adjacent domains rotated by 109 degrees. The striped morphology was caused by nucleation of only two ferroelastic domains on the low symmetry GdFeO3-type substrate. Domain engineering through substrate symmetry is an important finding for rhombohedral ferroelectric epitaxial thin films. The stripe pattern with vertical walls may be useful for extracting domain wall contributions to magnetism and electrical transport properties of BiFeO3 materials.

Stability of 71 degrees stripe domains in epitaxial BiFeO3 films upon repeated electrical switching

The 71 degrees stripe domain patterns of epitaxial BiFeO3 thin films are frequently being explored to achieve new functional properties, dissimilar from the BiFeO3 bulk properties. We show that in-plane switching and out-of-plane switching of these domains behave very differently. In the in-plane configuration the domains are very stable, whereas in the out-of-plane configuration the domains change their size and patterns, depending on the applied switching voltage frequency.

Ferroelectric nanostructures fabricated by focused-ion-beam milling in epitaxial BiFeO3 thin films

We studied a suitable route to fabricate ferroelectric islands by focused-ion-beam milling in bismuth ferrite epitaxial thin films. Piezoresponse force microscopy shows that the damage induced by the milling process is extended to 1 mu m away from the edge of the focused-ion-beam patterned islands. After a combined vacuum and oxygen atmosphere annealing procedure, ferroelectricity is fully recovered in structures with sizes down to 500 nm, while for 250 nm islands the defects at the interfaces induce polarization direction pinning.

Piezoelectric properties of PbTiO(3) thin films characterized with piezoresponse force and high resolution transmission electron microscopy

In this paper we investigate the piezoelectric properties of PbTiO(3) thin films grown by pulsed laser deposition with piezoresponse force microscopy and transmission electron microscopy. The as-grown films exhibit an upward polarization, inhomogeneous distribution of piezoelectric characteristics concerning local coercive fields, and piezoelectric coefficient. In fact, the data obtained reveal imprints during piezoresponse force microscopy measurements, nonlinearity in the piezoelectric deformation, and limited polarization reversal. Moreover, transmission electron microscopy shows the presence of defects near the film/substrate interface, which can be associated with the variations of piezoelectric properties.

Monodomain strained ferroelectric PbTiO(3) thin films: Phase transition and critical thickness study

This work demonstrates that instead of paraelectric PbTiO(3), completely c-oriented ferroelectric PbTiO(3) thin films were directly grown on (001)-SrTiO(3) substrates by pulsed-laser deposition with thickness up to 340 nm at a temperature well above the Curie temperature of bulk PbTiO(3). The influence of laser-pulse frequency, substrate-surface termination on growth, and functional properties were studied using x-ray diffraction, transmission electron microscopy, and piezoresponse force microscopy. At low growth rates (frequency 8 Hz) a domains were formed for film thickness above 20-100 nm. Due to coherency strains the Curie temperature (T(c)) of the monodomain films was increased approximately by 350 degrees C with respect to the T(c) of bulk PbTiO(3) even for 280-nm-thick films. Nonetheless, up to now this type of growth mode has been considered unlikely to occur since the Matthews-Blakeslee (MB) model already predicts strain relaxation for films having a thickness of only similar to 10 nm. However, the present work disputes the applicability of the MB model. It clarifies the physical reasons for the large increase in T(c) for thick films, and it is shown that the experimental results are in good agreement with the predictions based on the monodomain model of Pertsev et al. [Phys. Rev. Lett. 80, 1988 (1998)].

Piezoresponse force microscopy of ferroelectric thin films: Frequency dependence of phase imaging

The objective of this work is an evaluation of quantitative measurements of piezoresponse force microscopy for nanoscale characterization of ferroelectric films. To this end, we investigate how the piezoresponse phase difference Delta Phi between c domains depends on the frequency omega of the applied ac field much lower than the cantilever first resonance frequency. The main specimen under study was a 102 nm thick film of Pb(Zr(0.2)Ti(0.8))O(3). For the sake of comparison, a 100 nm thick PbTiO(3) film was also used. From our measurements, we conclude a frequency dependent behavior Delta Phi similar to omega(-1), which can only be partially explained by the presence of adsorbates on the surface. (C) 2008 American Institute of Physics.