Light emission from scanning tunnelling microscope on polycrystalline Au films - what is happening at the single-grain level?

When operated with a metallic tip and sample the scanning tunnelling microscope constitutes a nanoscale, plasmonic light source yielding broadband emission up to a photon energy determined by the applied bias. The emission is due to tunnelling electron excitation and subsequent radiative decay of localized plasmon modes, which can be on the lateral scale of a single metal grain (similar to 25 nm) or less. For a Au-tip/Au-polycrystalline sample under ambient conditions it is found that the intensity and spectral content of the emitted light are not dependent on the lateral grain dimension, but are predominantly determined by the tip geometry. However, the intensity increases strongly with increasing film thickness (grain depth) up to 20-25 nm or approximately the skin depth of the Au film. Photon maps can show less emissive grains and two classes of this occurrence are distinguished. The first is geometrical in origin - a double-tip structure in this case - while the second is due to a contamination-induced lowering of the local work function that causes the tunnel gap to increase. It is suggested that differences in work-function lowering between grains presenting different crystalline facets, combined with an exponential decay in emitted light intensity with tip - sample distance, leads to grain contrast. These results are relevant to tip-enhanced Raman scattering and the fabrication of micro/nano-scale planar, light-emitting tunnel devices.

Origin authentication of distillers' dried grains and solubles (DDGS) - Application and comparison of different analytical strategies

In the context of products from certain regions or countries being banned because of an identified or non-identified hazard, proof of geographical origin is essential with regard to feed and food safety issues. Usually, the product labeling of an affected feed lot shows origin, and the paper documentation shows traceability. Incorrect product labeling is common in embargo situations, however, and alternative analytical strategies for controlling feed authenticity are therefore needed. In this study, distillers' dried grains and solubles (DDGS) were chosen as the product on which to base a comparison of analytical strategies aimed at identifying the most appropriate one. Various analytical techniques were investigated for their ability to authenticate DDGS, including spectroscopic and spectrometric techniques combined with multivariate data analysis, as well as proven techniques for authenticating food, such as DNA analysis and stable isotope ratio analysis. An external validation procedure (called the system challenge) was used to analyze sample sets blind and to compare analytical techniques. All the techniques were adapted so as to be applicable to the DDGS matrix. They produced positive results in determining the botanical origin of DDGS (corn vs. wheat), and several of them were able to determine the geographical origin of the DDGS in the sample set. The maintenance and extension of the databanks generated in this study through the analysis of new authentic samples from a single location are essential in order to monitor developments and processing that could affect authentication.

Effect of Single and Double Austenitization heat treatments on the Microstructure and Hardness of AISI D2 Tool Steel

This investigation is concerned with the study of effect of Double Austenitization (DA) and Single Austenitization (SA) heat treatment processes on microstructure and mechanical property of AISI D2type cold worked tool steel. To maximize hardness, tool steels are used in a quenched and tempered condition. This involves heating the material to the austenitizing temperature (∼850−1100 °C), quenching at an appropriate rate to form martensite, and tempering to reduce the retained austenite content and induce toughness. The merits of DA treatment isto promote dissolution of carbides at the same time proscribe grain coarsening significantly was attempted in D2 tool steel. The study has found that DA treatment has induced high hardness with insignificant growth in grains. The increase in hardness is attributed to increase in carbon content in matrix due to dissolution of carbides; whereas finer grains due to role of inclusions.

Effect of Single and Double Austenitization heat treatments on the Microstructure and Hardness of AISI D2 Tool Steel

This investigation is concerned with the study of effect of Double Austenitization (DA) and Single Austenitization (SA) heat treatment processes on microstructure and mechanical property of AISI D2type cold worked tool steel. To maximize hardness, tool steels are used in a quenched and tempered condition. This involves heating the material to the austenitizing temperature (∼850−1100 °C), quenching at an appropriate rate to form martensite, and tempering to reduce the retained austenite content and induce toughness. The merits of DA treatment isto promote dissolution of carbides at the same time proscribe grain coarsening significantly was attempted in D2 tool steel. The study has found that DA treatment has induced high hardness with insignificant growth in grains. The increase in hardness is attributed to increase in carbon content in matrix due to dissolution of carbides; whereas finer grains due to role of inclusions.