An investigation into the effect of thickness of titanium dioxide and gold-silver nanoparticle titanium dioxide composite thin-films on photocatalytic activity and photo-induced oxygen production in a sacrificial system

Thin films of titanium dioxide and titanium dioxide with incorporated gold and silver nanoparticles were deposited onto glass microscope slides, steel and titanium foil coupons by two sol-gel dip-coating methods. The film's photocatalytic activity and ability to evolve oxygen in a sacrificial solution were assessed. It was found that photocatalytic activity increased with film thickness (from 50 to 500 nm thick samples) for the photocatalytic degradation of methylene blue in solution and resazurin redox dye in an intelligent ink dye deposited on the surface. Contrastingly, an optimum film thickness of similar to 200 nm for both composite and pure films of titanium dioxide was found for water oxidation, using persulfate (S2O82-) as a sacrificial electron acceptor. The nanoparticle composite films showed significantly higher activity in oxygen evolution studies compared with plain TiO2 films.

Fermentable sugars recovery from lignocellulosic waste-newspaper by catalytic hydrolysis

The urgent need for alternative renewable energies to supplement petroleum-based fuels and the reduction of landfill sites for disposal of solid wastes makes it increasingly attractive to produce inexpensive biofuels from the organic fraction of the municipal solid waste. Therefore, municipal waste in the form of newspaper was investigated as a potential feedstock for fermentable sugars production. Hydrolysis of newspaper by dilute phosphoric acid was carried out in autoclave Parr reactor, where reactor temperature and acid concentration were examined. Xylose concentration reached a maximum value of 14 g/100 g dry mass corresponding to a yield of 94% at the best identified conditions of 2.5 wt% HPO, 135°C, 120 min reaction time, and at 2.5 wt% HPO, 150°C, and 60 min reaction time. For glucose, an average yield of 26% was obtained at 2.5 wt% HPO, 200°C, and 30 min. Furfural and 5-hydroxymethylfurfural (HMF) formation was clearly affected by reaction temperature, where the higher the temperature the higher the formation rate. The maximum furfural formed was an average of 3 g/100 g dry mass, corresponding to a yield of 28%. The kinetic study of the acid hydrolysis was also carried out using the Saeman and the two-fraction models. It was found for both models that the kinetic constants (K) depend on the acid concentration and temperature. The degradation of HMF to levulinic acid is faster than the degradation of furfural to formic acid. Also, the degradation rate is higher than the formation rate for both inhibitors when degradation is observed.

N,O-Ligated Pd(II) Complexes for Catalytic Alcohol Oxidation

N,O-ligated Pd(II) complexes show considerable promise for the oxidation of challenging secondary aliphatic alcohols. The crystal structures of the highly active complexes containing the 8-hydroxyquinoline-2-carboxylic acid (HCA) and 8-hydroxyquinoline-2-sulfonic acid (HSA) ligands have been obtained. The (HSA)Pd(OAc)2 system can effectively oxidise a range of secondary alcohols, including unactivated alcohols, within 4–6 h using loadings of 0.5 mol%, while lower loadings (0.2 mol%) can be employed with extended reaction times. The influence of reaction conditions on catalyst degradation was also examined in these studies.