Templated electrodeposition of silver nanowires in a nanoporous polycarbonate membrane from a nonaqueous ionic liquid electrolyte

Template electrodeposition has been used to prepare a wide range of nanostructures but has generally been restricted to aqueous electrolytes. We report the deposition of silver nanowires in a commercial nuclear track-etched polycarbonate template from the nonaqueous ionic liquid, 1-butyl-3-methylimidazolium hexafluorophosphate ([bmim][PF6]) using silver electrochemically dissolved from the anode. Transmission electron microscopy (TEM) shows that the nanowires have a very high aspect ratio with an average diameter of 80 nm and length of 5 mu m. Ionic liquid electrolytes should greatly extend the range of metals that can be electrodeposited as nanowires using templates.

KCNQ Currents and Their Contribution to Resting Membrane Potential and the Excitability of Interstitial Cells of Cajal From the Guinea Pig Bladder

PURPOSE: The presence of novel KCNQ currents was investigated in guinea pig bladder interstitial cells of Cajal and their contribution to the maintenance of the resting membrane potential was assessed. MATERIALS AND METHODS: Enzymatically dispersed interstitial cells of Cajal were patch clamped with K(+) filled pipettes in voltage clamp and current clamp modes. Pharmacological modulators of KCNQ channels were tested on membrane currents and the resting membrane potential. RESULTS: Cells were stepped from -60 to 40 mV to evoke voltage dependent currents using a modified K(+) pipette solution containing ethylene glycol tetraacetic acid (5 mM) and adenosine triphosphate (3 mM) to eliminate large conductance Ca activated K channel and K(adenosine triphosphate) currents. Application of the KCNQ blockers XE991, linopirdine (Tocris Bioscience, Ellisville, Missouri) and chromanol 293B (Sigma) decreased the outward current in concentration dependent fashion. The current-voltage relationship of XE991 sensitive current revealed a voltage dependent, outwardly rectifying current that activated positive to -60 mV and showed little inactivation. The KCNQ openers flupirtine and meclofenamic acid (Sigma) increased outward currents across the voltage range. In current clamp mode XE991 or chromanol 293B decreased interstitial cell of Cajal resting membrane potential and elicited the firing of spontaneous transient depolarizations in otherwise quiescent cells. Flupirtine or meclofenamic acid hyperpolarized interstitial cells of Cajal and inhibited any spontaneous electrical activity. CONCLUSIONS: This study provides electrophysiological evidence that bladder interstitial cells of Cajal have KCNQ currents with a role in the regulation of interstitial cell of Cajal resting membrane potential and excitability. These novel findings provide key information on the ion channels present in bladder interstitial cells of Cajal and they may indicate relevant targets for the development of new therapies for bladder instability.

Path-selective photoinduced electron transfer (PET) in a membrane-associated system studied by pH-dependent fluorescence

The pH-dependent fluorescence behavior of two regioisomeric 'receptor(1)-spacer(1)-fluorophore-spacer(2)-receptor(2)' systems 1 and 2 in micellar solutions of sodium dodecyl sulfate show that photoinduced electron transfer (PET) only occurs from the amine group connected to the 4-amino position of the aminonaphthalimide fluorophore in both cases. This demonstrates the directing influence of the photogenerated electric field within the aminonaphthalimide excited state on the electron transfer process. Since path-selectivity of PET is also known within the membrane-bound photosynthetic reaction center in bacteria, its origins may be illuminated by the simple experiments described here. (C) 2011 Elsevier B. V. All rights reserved.

Development and testing of an intermediate temperature glass sealant for use in mixed ionic and electronic conducting membrane reactors

High temperature ceramic membranes have interesting possibilities for application in areas of new and developing technologies such as hydrocarbon combustion with carbon dioxide capture and electrochemical promotion of catalysis (EPOC). However, membrane module sealing remains a significant technical challenge. In this work a borosilicate glass sealant (50SiO₂·25B₂O₃·25Na₂O, mol%) was developed to fit the requirements of sealing an air separation membrane system at intermediate temperatures (300-600 °C). The seal was assessed by testing the leak rates under a range of conditions. The parameters tested included the effect of flowrate on the leak rate, the heating and cooling rates of the reactor and the range of temperatures under which the system could operate. Tests for durability and reliability were also performed. It was found that the most favourable reactor configuration employed a reactor with the ceramic pellet placed underneath the inner chamber alumina tube (inverted configuration), using a quartz wool support to keep the membrane in place prior to sealing. Using this configuration the new glass-based seal was found to be a more suitable sealant than traditional alternatives; it produced lower leak rates at all desirable flowrates, with the potential for rapid heating and cooling and multiple cycling, allowing for prolonged usage. © 2010 Elsevier B.V. All rights reserved.

Hydrogen-permeation characteristics of a SrCeO3-based ceramic separation membrane:Thermal, ageing and surface-modification effects

Dense ceramics with mixed protonic-electronic conductivity are of considerable interest for the separation and purification of hydrogen and as electrochemical reactors. In this work, the hydrogen permeability of a Sr_0.97Ce_0.9Yb_0.1O_{3 - δ} (SCYb) membrane with a porous Pt catalytic layer on the hydrogen feed-exposed side has been studied over the temperature range 500-804 °C employing Ar as the permeate sweep gas. A SiO₂-B₂O₃-BaO-MgO-ZnO-based glass-ceramic sealant was successfully employed to seal the membrane to the dual-chamber reactor. After 14 h of exposure to 10% H₂:90% N₂ at 804 °C, the H₂ flux reached a maximum of 33 nmol cm^{- 2} s^{- 1}, over an order of magnitude higher than that obtained on membranes of similar thickness without surface modification. The permeation rate then decreased slowly and moderately on annealing at 804 °C over a further 130 h. Thereafter, the flux was both reproducible and stable on thermal cycling in the range 600-804 °C. The results indicate an important role of superficial activation processes in the flux rate and suggest that hydrogen fluxes can be further optimised in cerate-based perovskites. © 2009 Elsevier B.V. All rights reserved.

Remote control of the activity of a Pt catalyst supported on a mixed ionic electronic conducting membrane

A novel configuration for the in situ control of the catalytic activity of a polycrystalline Pt catalyst supported on a mixed ionic electronic conducting (MIEC) substrate is investigated. The modification of the catalytic activity is achieved by inducing the reverse spillover of oxygen promoting species from the support onto the catalyst surface, thus modifying the chemisorptive bond energy of the gas phase adsorbed reactants. This phenomenon is known as Electrochemical Promotion of Catalysis (EPOC). In this work we investigate the use of a wireless system that takes advantage of the mixed ionic electronic conductivity of the catalyst support (internally short-circuiting the system) in a dual chamber reactor. In this wireless configuration, the reaction takes place in one chamber of the membrane reactor while introduction of the promoting species is achieved by the use of an appropriate sweep gas (and therefore control of the oxygen chemical potential difference across the membrane) on the other chamber. Experimental results have shown that the catalytic rate can be enhanced by using an oxygen sweep, while a hydrogen sweep can reverse the changes. Total rate enhancement ratios of up to 3.5 were measured. © 2008 Elsevier B.V. All rights reserved.