Wavelets for the Analysis and Compression of Power System Disturbances

Wavelets introduce new classes of basis functions for time-frequency signal analysis and have properties particularly suited to the transient components and discontinuities evident in power system disturbances. Wavelet analysis involves representing signals in terms of simpler, fixed building blocks at different scales and positions. This paper examines the analysis and subsequent compression properties of the discrete wavelet and wavelet packet transforms and evaluates both transforms using an actual power system disturbance from a digital fault recorder. The paper presents comparative compression results using the wavelet and discrete cosine transforms and examines the application of wavelet compression in power monitoring to mitigate against data communications overheads.

Co-melt fluidised bed granulation of pharmaceutical powders: Improvements in drug bioavailability

This study investigates the use of co-melt fluidised bed granulation for the agglomeration of model pharmaceutical powders, namely, lactose mono-hydrate, PEG 10000, poly-vinyl pyrolidone and ibuprofen as a model drug. Granulation within the co-melt system was found to follow a nucleationâ??steady growthâ??coating regime profile. Using high molecular weight PEG binder, the granulation mechanism and thus the extent of granulation was found to be significantly influenced by binder viscosity. The compression properties of the granulate within the hot fluidised bed were correlated using a novel high temperature experimental procedure. It was found that the fracture stress and fractural modulus of the materials under hot processing conditions were orders of magnitude lower than those measured under ambient conditions. A range of particle velocities within the granulator were considered based on theoretical models. After an initial period of nucleation, the Stokes deformation number analysis indicated that only velocities within the high shear region of the fluidised bed were sufficient to promote significant granule deformation and therefore, coalescence. The data also indicated that larger granules de-fluidised preventing agglomeration by coalescence. Furthermore, experimental data indicated that dissipation of the viscous molten binder to the surface was the most important factor in the latter stages of the granulation process. From a pharmaceutical perspective the inclusion of the model drug, ibuprofen, combined with PVP in the co-melt process proved to be highly significant. It was found that using DSC analysis on the formulations that the decrease in the heat of fusion associated with the melting of ibuprofen within the FHMG systems may be attributed to interaction between PVP and ibuprofen through inter-molecular hydrogen bonding. This interaction decreases the crystallinity of ibuprofen and facilitates solubilisation and bioavailability within the solid matrix.

Protection Assessment using Reduced Power System Fault Data

Wavelet transforms provide basis functions for time-frequency analysis and have properties that are particularly useful for the compression of analogue point on wave transient and disturbance power system signals. This paper evaluates the compression properties of the discrete wavelet transform using actual power system data. The results presented in the paper indicate that reduction ratios up to 10:1 with acceptable distortion are achievable. The paper discusses the application of the reduction method for expedient fault analysis and protection assessment.

Influence of fill factor variation in high shear granulation on the post granulation processes: Compression and tablet properties

This paper describes an investigation of the effect of fill factor; on the compaction behaviour of the granules during tableting and hence mechanical properties of tablets formed. The fill factor; which is the ratio of volume of wet powder material to vessel volume of the granulator, was used as an indicator of batch size. It has been established previously that in high shear granulation the batch size influences the size distribution and granule mechanical properties [1]. The work reported in this paper is an extension to the work presented in [1], hence granules from the same batches were used in production of tablets. The same tabletting conditions were employed during tabletting to allow a comparison of their properties. The compaction properties of the granules are inferred from the data generated during the tabletting process. The tablet strength and dissolution properties of the tablets were also measured. The results obtained show that the granule batch size affects the strength and dissolution of the tablets formed. The tablets produced from large batches were found to be weaker and had a faster dissolution rate. The fill factor was also found to affect the tablet to tablet variation of a non-functional active pharmaceutical ingredient included in the feed powder. Tablets produced from larger batches show greater variation compared to those from smaller batches.

Structure, mechanical, and electrical properties of high-density polyethylene/multi-walled carbon nanotube composites processed by compression molding and blown film extrusion

The structure and properties of melt mixed high-density polyethylene/multi-walled carbon nanotube (HDPE/MWCNT) composites processed by compression molding and blown film extrusion were investigated to assess the influence of processing route on properties. The addition of MWCNTs leads to a more elastic response during deformations that result in a more uniform thick-ness distribution in the blown films. Blown film composites exhibit better mechanical properties due to the enhanced orientation and disentanglement of MWCNTs. At a blow up ratio (BUR) of 3 the breaking strength and elongation in the machine direction of the film with 4 wt % MWCNTs are 239% and 1054% higher than those of compression molded (CM) samples. Resistivity of the composite films increases significantly with increasing BURs due to the destruction of conductive pathways. These pathways can be recovered partially using an appropriate annealing process. At 8 wt % MWCNTs, there is a sufficient density of nanotubes to maintain a robust network even at high BURs.

Joined Spectral Trees for Scalable SPIHT-Based Multispectral Image Compression

In this paper, the compression of multispectral images is addressed. Such 3-D data are characterized by a high correlation across the spectral components. The efficiency of the state-of-the-art wavelet-based coder 3-D SPIHT is considered. Although the 3-D SPIHT algorithm provides the obvious way to process a multispectral image as a volumetric block and, consequently, maintain the attractive properties exhibited in 2-D (excellent performance, low complexity, and embeddedness of the bit-stream), its 3-D trees structure is shown to be not adequately suited for 3-D wavelet transformed (DWT) multispectral images. The fact that each parent has eight children in the 3-D structure considerably increases the list of insignificant sets (LIS) and the list of insignificant pixels (LIP) since the partitioning of any set produces eight subsets which will be processed similarly during the sorting pass. Thus, a significant portion from the overall bit-budget is wastedly spent to sort insignificant information. Through an investigation based on results analysis, we demonstrate that a straightforward 2-D SPIHT technique, when suitably adjusted to maintain the rate scalability and carried out in the 3-D DWT domain, overcomes this weakness. In addition, a new SPIHT-based scalable multispectral image compression algorithm is used in the initial iterations to exploit the redundancies within each group of two consecutive spectral bands. Numerical experiments on a number of multispectral images have shown that the proposed scheme provides significant improvements over related works.

Mechanical behaviour of unsaturated kaolin (with isotropic and anisotropic stress history). Part 1: wetting and compression behaviour

Over the last 40 years considerable progress has been made in understanding the complex behaviour of unsaturated soils. Research using constitutive modelling has extended the critical state framework and the concept of yielding in saturated soils to encompass unsaturated soils experiencing suction. However, validation testing of the framework for unsaturated soils has shown disagreement with the basic propositions. The main reason for this disparity is the anisotropic properties of the soil specimens tested as a result of preparation using one-dimensional compaction. The paper describes the detailed testing carried out to justify this statement. As part of the work presented, samples of unsaturated kaolin were prepared using isotropic compression. The suctions in these samples were reduced to predefined values by wetting under low isotropic loading. The pore size distributions, the pressure–volume relationships and yielding under subsequent isotropic loading are compared with tests on samples prepared by statically compressing kaolin into a one-dimensional compaction mould. The anisotropically compressed samples had initial water contents and specific volumes similar to those of the isotropically prepared samples and were also tested under reducing suctions; they exhibited distinctly different behaviour when tested under similar conditions. The results obtained from the isotropically prepared and tested samples have shown, probably for the first time, the existence of a unique normal compression surface that is not dependent on the initial conditions of the samples. The shape of the loading–collapse (LC) yield locus is shown to be different from the generally accepted form.

Relationship between microstructure and deformation behaviour during dynamic compression in Ti-3Al-5Mo-5V alloy

The relationship between microstructure and deformation and damage behaviour during dynamic compression in Ti-3Al-5Mo-5V alloy has been studied using several experimental techniques, including optical microscopy, scanning electron microscopy and microhardness measurements. It was found that the deformation behaviour during dynamic compression was closely related to deformation parameters. After dynamic deformation, the deformation shear band that formed in the titanium alloy had microhardness similar to that of the matrix. However, the microhardness of the white shear band was much higher than the matrix microhardness. The effects of deformation parameters, including deformation rate and deformation degree, on deformation localisation were investigated. Based on the results from the present work, the microstructure and deformation processing parameters can be optimised. In addition, treatment methods after dynamic compression were explored to restore alloy properties. Using post-deformation heat treatment, the microstructure and property inhomogeneity caused by shear bands could be largely removed.

Mucoadhesive, syringeable drug delivery systems for controlled application of metronidazole to the periodontal pocket: In vitro release kinetics, syringeability, mechanical and mucoadhesive properties

Novel mucoadhesive formulations containing hydroxyethylcellulose (HEC; 3 and 5%, w/w) or Carbopol (3 and 5%, w/w), polycarbophil (PC; 1 and 3%, w/w) and metronidazole (5%, w/w) at pH 6.8 were designed for the treatment of periodontal diseases. Each formulation was characterised in terms of hardness, compressibility, adhesiveness and cohesiveness (using Texture Profile Analysis), drug release, adhesion to a mucin disc (measured as a detachment force using the texture analyser in tensile mode) and, finally, syringeability (using the texture analyser in compression mode). Drug release from all formulations was non-diffusion controlled. Drug release was significantly decreased as the concentration of each polymeric component was increased, due to both the concomitant increased viscosity of the formulations and, additionally, the swelling kinetics of PC following contact with dissolution fluid. Increasing the concentrations of each polymeric component significantly increased formulation hardness, compressibility, adhesiveness, mucoadhesion and syringeability, yet decreased cohesiveness. Increased product hardness, compressibility and syringeability were due to polymeric effects on formulation viscosity. The effects on cohesiveness may be explained both by increased viscosity and also by the increasing semi-solid nature of products containing 5% HEC or Carbopol and PC (1 or 3%). The observations concerning formulation adhesiveness/mucoadhesion illustrate the adhesive nature of each polymeric component. Greatest adhesion was noted in formulations where neutralisation of PC was maximally suppressed. For the most part, increased time of contact between formulation and mucin significantly increased the required force of detachment, due to the greater extent of mucin polymer hydration and interpenetration with the formulations. Significant statistical interactions were observed between the effects of each polymer on drug release and mechanical/mucoadhesive properties. These interactions may be explained by formulatory effects on the extent of swelling of PC. In conclusion, the formulations described offered a wide range of mechanical and drug release characteristics. Formulations containing HEC exhibited superior physical characteristics for improved drug delivery to the periodontal pocket and are now the subject of long-term clinical investigations. (C) 1997 Elsevier Science B.V.

Morphology and compression behaviour of biodegradable scaffolds produced by the sintering process

Porous poly(L-lactic acid) (PLA) scaffolds of 85 per cent and 90 per cent porosity are prepared using polymer sintering and porogen leaching method. Different weight fractions of 10 per cent, 30 per cent, and 50 per cent of hydroxyapatite (HA) are added to the PLA to control the acidity and degradation rate. The three-dimensional (3D) morphology and surface porosity are tested using micro-computer tomography (micro-CT), optical microscopy, and scanning electron microscopy (SEM). Results indicate that the surface porosity does not change on the addition of HA. The micro-CT examinations show a slight decrease in the pore size and increase in the wall thickness accompanied by reduced anisotropy for the scaffolds containing HA. Scanning electron micrographs show detectable interconnected pores for the scaffold with pure PLA. Addition of the HA results in agglomeration of the HA particles and reduced leaching of the porogen. Compression tests of the scaffold identify three stages in the stress-strain curve. The addition of HA results in a reduction in the modulus of the scaffold at the first stage of elastic bending of the wall, but this is reversed for the second and third stages of collapse of the wall and densification in the compression tests. In the scaffolds with 85 per cent porosity, the addition of a high percentage of HA could result in 70 per cent decrease in stiffness in the first stage, 200 per cent increase in stiffness in the second stage, and 20 per cent increase in stiffness in the third stage. The results of these tests are compared with the Gibson cellular material model that is proposed for prediction of the behaviour of cellular material under compression. The pH and molecular weight changes are tracked for the scaffolds within a period of 35 days. The addition of HA keeps the pH in the alkaline region, which results in higher rate of degradation at an early period of observation, followed by a reduced rate of degradation later in the process. The final molecular weight is higher for the scaffolds with HA than for scaffolds of pure PLA. The manufactured scaffolds offer acceptable properties in terms of the pore size range and interconnectivity of the pores and porosity for non-load-bearing bone graft substitute; however, improvement to the mixing of the phases of PLA and HA is required to achieve better integrity of the composite scaffolds. © 2008 IMechE.

Enhancement of the properties of EPDM/NBR elastomers using nanoclay for seal applications

In this research, we have investigated the effects of addition of different percentages of nanoclay to the ethylene propylene diene monomer (EPDM) and nitrile butadiene rubber (NBR) on the characteristics of these rubbers as seal material. Properties such as tensile strength, modulus at different extensions, elongation at break, compressive set, hardness, and permeability and abrasion resistance are tested to assess the effect of addition of the nanoclay. Results indicate that addition of nanoclay at certain compositions could slightly reduce the strength of the rubber. However more stable modulus at different strains are provided, the hardness of the rubber is preserved and slightly enhanced, the permeability is reduced in both rubbers especially considerable decrease in EPDM is observed which is desirable in diminishing the effect of explosive decompression. At the same time the compression test shows that the nanoclay improves the performance of the rubbers under compression which is essential in seal application. The X-ray diffraction tests clarify that the dispersion of the nanoclay in the NBR samples is of high quality. In the EPDM samples, the dispersion is in need of improvement. POLYM. COMPOS., 30:1657-1667, 2009. © 2008 Society of Plastics Engineers.

Numerical prediction of the low-velocity impact damage and compression after impact strength of composite laminates

Low-velocity impact damage can drastically reduce the residual mechanical properties of the composite structure even when there is barely visible impact damage. The ability to computationally predict the extent of damage and compression after impact (CAI) strength of a composite structure can potentially lead to the exploration of a larger design space without incurring significant development time and cost penalties. A three-dimensional damage model, to predict both low-velocity impact damage and compression after impact CAI strength of composite laminates, has been developed and implemented as a user material subroutine in the commercial finite element package, ABAQUS/Explicit. The virtual tests were executed in two steps, one to capture the impact damage and the other to predict the CAI strength. The observed intra-laminar damage features, delamination damage area as well as residual strength are discussed. It is shown that the predicted results for impact damage and CAI strength correlated well with experimental testing.

Numerical prediction of the low-velocity impact damage and compression after impact strength of composite laminates

Low-velocity impact damage can drastically reduce the residual mechanical properties of the composite structure even when there is barely visible impact damage. The ability to computationally predict the extent of damage and compression after impact (CAI) strength of a composite structure can potentially lead to the exploration of a larger design space without incurring significant development time and cost penalties. A three-dimensional damage model, to predict both low-velocity impact damage and compression after impact CAI strength of composite laminates, has been developed and implemented as a user material subroutine in the commercial finite element package, ABAQUS/Explicit. The virtual tests were executed in two steps, one to capture the impact damage and the other to predict the CAI strength. The observed intra-laminar damage features, delamination damage area as well as residual strength are discussed. It is shown that the predicted results for impact damage and CAI strength correlated well with experimental testing.

Low cycle fatigue properties of CLAM steel at room temperature

The low cycle fatigue (LCF) properties and the fracture behavior of China Low Activation Martensitic (CLAM) steel have been studied over a range of total strain amplitudes from 0.2 to 2.0%. The specimens were cycled using tension-compression loading under total strain amplitude control. The CLAM steel displayed initial hardening followed by continuous softening to failure at room temperature in air. The relationship between strain and fatigue life was predicted using the parameters obtained from fatigue test. The factors effecting on low cycle fatigue of CLAM steel consisted of initial state of matrix dislocation arrangement, magnitude of cyclic stress, magnitude of total strain amplitude and microstructure. The potential mechanisms controlling the stress response, cyclic strain resistance and low cycle fatigue life have been evaluated.

Effect of cooling rate on the properties of high density polyethylene/multi-walled carbon nanotube composites

High density polyethylene (HDPE)/multi-walled carbon nanotube (MWCNT) nanocomposites were prepared by melt mixing using twin-screw extrusion. The extruded pellets were compression moulded at 200°C for 5min followed by cooling at different cooling rates (20°C/min and 300°C/min respectively) to produce sheets for characterization. Scanning electron microscopy (SEM) shows that the MWCNTs are uniformly dispersed in the HDPE. At 4 wt% addition of MWCNTs composite modulus increased by over 110% compared with the unfilled HDPE (regardless of the cooling rate). The yield strength of both unfilled and filled HDPE decreased after rapid cooling by about 10% due to a lower crystallinity and imperfect crystallites. The electrical percolation threshold of composites, irrespective of the cooling rate, is between a MWCNT concentration of 1∼2 wt%. Interestingly, the electrical resistivity of the rapidly cooled composite with 2 wt% MWCNTs is lower than that of the slowly cooled composites with the same MWCNT loading. This may be due to the lower crystallinity and smaller crystallites facilitating the formation of conductive pathways. This result may have significant implications for both process control and the tailoring of electrical conductivity in the manufacture of conductive HDPE/MWCNT nanocomposites.