High capacity carbon based electrodes for lithium/oxygen batteries

Porous carbon aerogels are prepared by polycondensation of resorcinol (R) and formaldehyde (F)catalyzed by sodium carbonate (C) followed by carbonization of the resultant aerogels at 800? in an inert atmosphere. The porous texture of the carbons has been adjusted by the change of the molar ratio of resorcinol to catalyst (R/C) in the gel precursors in the range of 100 to 500. The porous structure of the aerogels and carbon aerogels are characterized by N2 adsorption-desorption measurements at 77 K. It is found that total pore volume and average pore diameter of the carbons increase with increase in the R/C ratio of the gel precursors.The prepared carbon aerogels are used as active materials in fabrication of composite carbon electrodes. The electrochemical performance of the electrodes has been tested by using them as cathodes in a Li/O2 cell. Through the galvanostatic charge/discharge measurements, it is found that with an increase of R/C ratio, the specific capacity of the Li/O2 cell fabricated from the carbon aerogels increases from 716 to 2077 charge/discharge cycles indicate that the carbon samples possess excellent stability on cycling.

Voltammetric studies of gold, protons, and [HCl2](-) in ionic liquids

The comparative study of the voltammetry of H[NTf2], HCl and H[AuCl4] in [C(4)mim][NTf2] has provided an insight into the influence of protons on the reduction of [AuCl4](-) at Au, Pt or glassy carbon (GC) electrodes, and has allowed the identification of an unprecedented proton-induced electroless deposition of Au on relatively inert GC surfaces. For the first time, clear evidence of the quantitative formation of [HCl2](-) has been obtained in HCl/[C(4)mim][NTf2] mixtures, and the electrochemical behavior of these mixtures analyzed. In particular, a significant shift of the dissociation equilibrium toward the formation of chloride and the solvated proton (H-IL(+)), following electrochemical reduction of H-IL(+) has been observed in the time-scale of the experiments.

Electrochemical studies of gold and chloride in ionic liquids

For the first time, the electrochemistry of gold has been studied in detail in a 'second-generation', non-haloaluminate, ionic liquid. In particular, the electrochemical behaviour of Na[AuCl4] has been investigated in 1-butyl-3-methylimidazolium bis{(tifluoromethyl)sulfonyl} imide, [C(4)mim][NTf2], over gold, platinum and glassy carbon working electrodes. The reduction of [AuCl4](-) initially forms [AuCl2](-) before deposition on the electrode as Au(0). To enable stripping of deposited gold or electrodissolution of bulk gold, the presence of chloride, trichloride or chlorine is required. Specifically trichloride and chlorine have been identified as the active species which preferentially form Au(I) and Au(III), respectively.

Electroreduction of oxygen in a series of room temperature ionic liquids composed of group 15-centered cations and anions

The electrochemical reduction of oxygen is reported in four room temperature ionic liquids (RTILs) based on quaternary alkyl -onium cations and heavily fluorinated anions in which the central atom is either nitrogen or phosphorus. Data were collected using cyclic voltammetry and potential step chronoamperometry at gold, platinum, and glassy carbon disk electrodes of micrometer dimension under water-free conditions at a controlled temperature. Analysis via fitting, to appropriate theoretical equations was then carried out to obtain kinetic and thermodynamic information pertaining to the electrochemical processes observed. In the quaternary ammonium electrolytes, reduction of oxygen was found to occur reversibly to give stable superoxide, in an analogous manner to that seen in conventional aprotic solvents such as dimethyl sufoxide and acetonitrile. The most significant difference is in the relative rate of diffusion; the diffusion coefficients of oxygen in the RTILs are an order of magnitude lower than in common organic solvents, and for superoxide these values are reduced by a further factor of 10. In the quaternary phosphonium ionic liquids, however, more complex voltammetry is observed, akin to that expected for the reduction of oxygen in acidified organic media. This is shown to be consistent with the occurrence of a proton abstraction reaction between the electrogenerated superoxide and quaternary alkyl phosphonium cations following the initial electron transfer.

The effects of temperature on the performance of electrochemical double layer capacitors

An electrochemical double layer capacitor test cell containing activated carbon xerogel electrodes and ionic liquid electrolyte was tested at 15, 25 and 40 OC to examine the effect of temperature on electrolyte resistance (RS) and equivalent series resistance (ESR) measured using impedance spectroscopy and capacitance using charge/discharge cycling. A commercial 10F capacitor was used as a comparison. Viscosity, ionic self-diffusion coefficients and differential scanning calorimetry measurements were used to provide an insight into the behaviour of the 1,2-dimethyl-3-propylimdazolium electrolyte. Both RS and ESR decreased with increasing temperature for both capacitors. Increasing the temperature also increased the capacitance for both the test cell and the commercial capacitor but proportionally more for the test cell. An increase in temperature decreased the ionic liquid electrolyte viscosity and increased the self diffusion coefficients of both the anion and the cation indicating an increase in dissociation and increase in ionic mobility.

An ether-functionalised cyclic sulfonium based ionic liquid as an electrolyte for electrochemical double layer capacitors

A novel cyclic sulfonium cation-based ionic liquid (IL) with an ether-group appendage and the bis{(trifluoromethyl)sulfonyl}imide anion was synthesised and developed for electrochemical double layer capacitor (EDLC) testing. The synthesis and chemical-physical characterisation of the ether-group containing IL is reported in parallel with a similarly sized alkyl-functionalised sulfonium IL. Results of the chemical-physical measurements demonstrate how important transport properties, i.e. viscosity and conductivity, can be promoted through the introduction of the ether-functionality without impeding thermal, chemical or electrochemical stability of the IL. Although the apparent transport properties are improved relative to the alkyl-functionalised analogue, the ether-functionalised sulfonium cation-based IL exhibits moderately high viscosity, and poorer conductivity, when compared to traditional EDLC electrolytes based on organic solvents (propylene carbonate and acetonitrile). Electrochemical testing of the ether-functionalised sulfonium IL was conducted using activated carbon composite electrodes to inspect the performance of the IL as a solvent-free electrolyte for EDLC application. Good cycling stability was achieved over the studied range and the performance was comparable to other solvent free,
IL-based EDLC systems. Nevertheless, limitations of the attainable performance are primarily the result of sluggish transport properties and a restricted operative voltage of the IL, thus highlighting key aspects of this field which require further attention.

Characteristics of the interfacial capacitance in thin film Ba0.5Sr0.5TiO3 capacitors with SrRuO3 and (La, Sr)CoO3 bottom electrodes

Thin film Ba0.5Sr0.5TiO3 (BST) capacitors of thickness similar to75 nm to similar to1200 nm, with Au top electrodes and SrRuO 3 (SRO) or (La, Sr)CoO3 (LSCO) bottom electrodes were fabricated using Pulsed Laser Deposition. Implementing the "series capacitor model," bulk and interfacial capacitance properties were extracted as a function of temperature and frequency. 'Bulk' properties demonstrated typical ceramic behaviour, displaying little frequency dependence and a permittivity and loss peak at 250 K and 150 K respectively. The interfacial component was found to be relatively temperature and frequency independent for the LSCO/BST capacitors, but for the SRO/BST configuration the interfacial capacitance demonstrated moderate frequency and little temperature dependence below T similar to 300 K but a relatively strong frequency and temperature dependence above T similar to3 00 K. This was attributed to the thermal activation of a space charge component combined with a thermally independent background. The activation energy for the space charge was found to be E-A similar to 0.6 eV suggesting de-trapping of electrons from shallow level traps associated with a thin interfacial layer of oxygen vacancies, parallel to the electrodes.

Thin plastic film colorimetric sensors for carbon dioxide: Effect of plasticizer on response

Different plasticizers, including phosphate-, phthalate-and adipate-based types were used in the creation of a range of colorimetric plastic film sensors for CO2, The different types of plasticizer used in the formulation of a colorimetric plastic film sensor for CO2 affect the response and recovery times of the sensor differently, An effective plasticizer was taken as one that decreased the response and recovery times of the final film sensor when exposed to an alternating atmosphere of 0-5% CO2. On this basis, the most efficient plasticizers appeared to be phosphate-based, followed by phthalate- and adipate-based plasticizers, This trend appears to reflect the degree of the polymer-plasticizer compatibility. Increasing the amount of plasticizer in the film formulation decreased the response and recovery times of the sensor dramatically, The sensitivity of the film sensor towards CO2 appears to decrease with increasing plasticizer effectiveness; thus, the general order of film CO2 sensitivity with respect to plasticizer type was found to be adipate > phthalate > phosphate. In general, the response of the optical films towards CO2 was found to be temperature sensitive [typically, Delta H = -(44-55) kJ mol(-1)], The phosphate-based plasticized films appear to be less temperature sensitive than the other plasticized films, and 2-ethylhexyl diphenylphosphate appears particularly effective in this respect (Delta H = -18.5 kJ mol(-1)).

COLORIMETRIC POLYMER FILM SENSORS FOR DISSOLVED CARBON-DIOXIDE

Plasticized and unplasticized polymer colorimetric film sensors for gaseous CO2, containing the dye m-cresol purple, are tested as sensors for dissolved CO2. The plasticized polymer m-cresol purple film sensor develops a measurable degree of opacity when exposed to aqueous solution, especially in neutral, compared with alkaline, solution. However, it is shown that a presoaked, fogged plasticized polymer m-cresol purple film does function as a quantitative sensor for dissolved CO2 over the range 0-4% CO2. An unplasticized polymer m-cresol purple film remains largely dear upon exposure to aqueous solution and also functions as a quantitative sensor for dissolved CO2 over the range 0-4% CO2. However, in both types of films the dye interacts with electrolytes present in solution; invariably the dye appears to be converted from its initial deprotonated form (blue) to its protonated form (yellow) and the rate of this process appears to increase with increasing ionic strength, anionic charge and decreasing pH. The 90% response and recovery times for an unplasticized film are determined as 19 s(CO2:0-->5%) and 21 s (CO2:5-->3.6%), respectively.

FLUORESCENCE PLASTIC THIN-FILM SENSOR FOR CARBON-DIOXIDE

The method of preparation of a novel plastic thin-film sensor that incorporates the fluorescent dye 8-hydroxypryrene-1,3,6-trisulfonic acid is described; the shelf-life of the film is over 6 months. The results of a study on the equilibrium response of the sensor towards different levels of gaseous CO2 fit a model there is a 1 + 1 equilibrium reaction between the deprotonated form of the dye (present in the film as an ion pair) and the concentration of gaseous CO2 present. In contrast to the situation in aqueous solution, in the plastic film the pK(a) of the excited form of the dye appears close to that of the ground-state form, although this does not interfere with its use as 8 CO2 sensor. The 0 to 90% response and recovery times of the film when exposed to an alternating atmosphere of air and 5% CO2 are typically 4.3 and 7.1 s, respectively.

EQUILIBRIUM STUDIES ON COLORIMETRIC PLASTIC FILM SENSORS FOR CARBON-DIOXIDE

The equilibrium responses of three new colorimetric plastic film sensors for CO2 as a function of % CO2 and temperature are described. The results fit a model in which there is a 1:1 equilibrium reaction between the deprotonated form of the dye (present in the film as an ion pair) and CO2. The 0-50% and 0-90% response and recovery times of each of these films when exposed to an alternating atmosphere of air and 5% CO2 are determined and in two cases are typically less than 3 s. The shelf life of the films is long (many months); however, prolonged use of the films leads to the permanent generation of the protonated form of the dye over a period of 20-100 h. A possible cause of this latter effect is discussed.