From non-porous crystalline to amorphous microporous metal(IV) bisphosphonates

Porous layered hybrid materials have been prepared by the reaction of organo-bisphosphonate ligands, 4-(4'-phosphonophenoxy)phenylphosphonic, 4,4'-biphenylenbisphosphonic and phenylphosphonic acids, with metal(IV) cations (Zr and Sn). Crystalline Zr(IV) and Sn(IV) layered bisphosphonates were also prepared, which were non-porous. The amorphous M(IV) bisphosphonates showed variable compositions and textural properties ranging from mainly mesoporous to highly microporous solids with BET surface areas varying from 300 to 480 m(2) g(-1), micropore volumes ranging 0.10-0.20 cm(3)/g, and narrow porous size distributions for some materials. N-2 isotherms suggest that Sn(IV) derivatives show a comparatively higher micropore contribution than the Zr(IV) analogous at least for the ether-bisphosphonate hybrids. Sn(IV) bisphosphonates exhibit high microporosities without the need of using harmful DMSO as solvent. If ether-bisphosphonic acid is partially replaced by less expensive phenylphosphonic ligand, porous products are also obtained. P-31 and F-17 MAS NMR and XPS data revealed the presence of hydrogen-phosphonate groups and small (F-, Cl- and OH-) anions, which act as spacer ligands within the inorganic layers, in these hybrid materials. The complexity of the inorganic layers is higher for the Sn(IV) bisphosphonates likely due to the larger amount of small bridging anions including fluorides. It is suggested that the presence of these small inorganic ligands may be a key factor influencing both, the interaction of the inorganic layer with the bisphosphonate groups, which bridge the inorganic layers, and the generation of internal voids within a given inorganic layer. Preliminary studies of gases adsorption (H-2 and NO) have been carried out for selected Sn(IV) bisphosphonates. The H-2 adsorption capacity at 77 K and 1 bar was low, 0.26 wt%, but the NO adsorption capacity at similar to 1 bar and 298 K was relatively high, 4.2 wt%. Moreover, the hysteresis in the NO isotherms is indicative of partial strong irreversible adsorption of NO. (C) 2008 Elsevier Inc. All rights reserved.

Examination of surface properties and in vitro biological performance of amorphous diamond-like carbon-coated polyurethane

Despite the emerging use of diamond-like carbon (DLC) as a coating for medical devices, few studies have examined the resistance of DLC coatings onto medical polymers to both microbial adherence and encrustation. In this study, amorphous DLC of a range of refractive indexes (1.7-1.9) and thicknesses (100-600 nm) was deposited onto polyurethane, a model polymer, and the resistance to microbial adherence (Escherichia coli; clinical isolate) and encrustation examined using in vitro models. In comparison to the native polymer, the advancing and receding contact angles of DLC-coated polyurethane were lower, indicating greater hydrophilic properties. No relationship was observed between refractive index, thickness, and advancing contact angle, as determined using multiple correlation analysis. The resistances of the various DLC-coated polyurethane films to encrustation and microbial adherence were significantly greater than that to polyurethane; however, there were individual differences between the resistances of the various DLC coatings. In general, increasing the refractive index of the coatings (100 nm thickness) decreased the resistance of the films to both hydroxyapatite and struvite encrustation and to microbial adherence. Films of lower thicknesses (100 and 200 nm; of defined refractive index, 1.8), exhibited the greatest resistance to encrustation and to microbial adherence. In conclusion, this study has uniquely illustrated both the microbial antiadherence properties and resistance to urinary encrustation of DLC-coated polyurethane. The resistances to encrustation and microbial adherence were substantial, and in light of this, it is suggested that DLC coatings of low thickness and refractive index show particular promise as coatings of polymeric medical devices. (c) 2006 Wiley Periodicals, Inc.