10 resultados para Zirconium.
em QUB Research Portal - Research Directory and Institutional Repository for Queen's University Belfast
Resumo:
Rings of perovskite lead zirconium titanate (PZT) with internal diameters down to similar to 5 nm and ring thicknesses of similar to 5-10 nm have been fabricated and structurally, crystallographically, and chemically characterized using an analytical transmission electron microscope. Ring fabrication involved conformal solution deposition of a thin layer of PZT on the inside of a thin film of anodized aluminum oxide nanopores, and subsequent sectioning of the coated pores perpendicular to their cylinder axes. Although the starting solution used for the solution deposition was made from morphotropic phase boundary PZT, the nanorings were found to be on the zirconium-rich side of the PZT phase diagram. Nevertheless, coatings were found to be of perovskite crystallography. The dimensions of these nanorings are such that they have the potential to demonstrate polarization vortices, as modeled by Naumov [Nature (London) 432, 737 (2004)], and moreover represent the perfect morphology to allow vortex alignment and the creation of the ferroelectric "solenoid" as modeled by Gorbatsevich and Kopaev [Ferroelectrics 161, 321 (1994)].
Resumo:
Periodic arrays of nanorings of morphotropic phase boundary lead zirconium titanate ( PZT) have been successfully fabricated using a novel self-assembly technique: close-packed monolayers of latex nanospheres were deposited onto Pt-coated silicon substrates, and then plasma cleaned to form ordered arrays of isolated nanospheres, not in contact with each other. Subsequent pulsed laser deposition of PZT, high angle argon ion etching and thermal annealing created the arrays of isolated nanorings, with diameters of similar to 100 nm and wall thicknesses of similar to 10 nm. Energy dispersive x-ray analysis confirms that the rings are compositionally morphotropic phase boundary PZT, and high resolution transmission electron microscopy imaging of lattice fringes demonstrates some periodicities consistent with perovskite rather than pyrochlore material. The dimensions of these nanorings, and the expected 'soft' behaviour of the ferroelectric material from which they are made, means that they offer the most likely opportunity to date for observing whether or not vortex arrangements of electrical dipoles, analogous to those seen in ferromagnetic nanostructures, actually exist.
Resumo:
Single oxides of Ti and Zr incorporated SBA-15 were prepared and characterized by N-2 adsorption, NMR, and XPS techniques. Si-29 MAS NMR results suggest the formation of Si-O-X linkages (X: Ti or Zr) by an increase in the ratio of Q(3)/Q(4) in the presence of Ti or Zr. XPS analysis of Ti-SBA-15 catalysts indicate the presence of Ti-O-Si bonds in addition to Ti-O-Ti and Si-O-Si bonds, supporting the NMR evidence.
Resumo:
Abstract Image
A high-capacity diffusive gradients in thin films (DGT) technique has been developed for measurement of total dissolved inorganic arsenic (As) using a long shelf life binding gel layer containing hydrous zirconium oxide (Zr-oxide). Both As(III) and As(V) were rapidly accumulated in the Zr-oxide gel and could be quantitatively recovered by elution using 1.0 M NaOH for freshwater or a mixture of 1.0 M NaOH and 1.0 M H2O2 for seawater. DGT uptake of As(III) and As(V) increased linearly with deployment time and was independent of pH (2.0–9.1), ionic strength (0.01–750 mM), the coexistence of phosphate (0.25–10 mg P L–1), and the aging of the Zr-oxide gel up to 24 months after production. The capacities of the Zr-oxide DGT were 159 μg As(III) and 434 μg As(V) per device for freshwater and 94 μg As(III) and 152 μg As(V) per device for seawater. These values were 5–29 times and 3–19 times more than those reported for the commonly used ferrihydrite and Metsorb DGTs, respectively. Deployments of the Zr-oxide DGT in As-spiked synthetic seawater provided accurate measurements of total dissolved inorganic As over the 96 h deployment, whereas ferrihydrite and Metsorb DGTs only measured the concentrations accurately up to 24 and 48 h, respectively. Deployments in soils showed that the Zr-oxide DGT was a reliable and robust tool, even for soil samples heavily polluted with As. In contrast, As in these soils was underestimated by ferrihydrite and Metsorb DGTs due to insufficient effective capacities, which were likely suppressed by the competing effects of phosphate.
Resumo:
We report on the successful fabrication of arrays of switchable nanocapacitors made by harnessing the self-assembly of materials. The structures are composed of arrays of 20-40 nm diameter Pt nanowires, spaced 50-100 nm apart, electrodeposited through nanoporous alumina onto a thin film lower electrode on a silicon wafer. A thin film ferroelectric (both barium titanate (BTO) and lead zirconium titanate (PZT)) has been deposited on top of the nanowire array, followed by the deposition of thin film upper electrodes. The PZT nanocapacitors exhibit hysteresis loops with substantial remnant polarizations, while although the switching performance was inferior, the low-field characteristics of the BTO nanocapacitors show dielectric behavior comparable to conventional thin film heterostructures. While registration is not sufficient for commercial RAM production, this is nevertheless an embryonic form of the highest density hard-wired FRAM capacitor array reported to date and compares favorably with atomic force microscopy read-write densities.
Resumo:
A conventional thin film capacitor heterostructure, consisting of sol-gel deposited lead zirconium titanate (PZT) layers with sputtered platinum top and bottom electrodes, was subjected to fatiguing pulses at a variety of frequencies. The fatigue characteristics were compared to those of a similarly processed capacitor in which a ~20nm tungsten trioxide layer had been deposited, using pulsed laser deposition, between the ferroelectric and upper electrode. The expectation was that, because of its ability to accommodate considerable oxygen non-stoichiometry, tungsten trioxide (WO3) might act as an efficient sink for any oxygen vacancies flushed to the electrode-ferroelectric boundary layer during repetitive switching, and hence would improve the fatigue characteristics of the thin film capacitor. However, it was found that, in general, the addition of tungsten trioxide actually increases the rate of fatigue. It appears that any potential benefit from the WO3, in terms of absorbing oxygen vacancies, is far outweighed by it causing dramatically increased charge injection in the system.
Resumo:
Recently, lead iron tantalate/lead zirconium titanate (PZTFT) was demonstrated to possess large, but unreliable, magnetoelectric coupling at room temperature. Such large coupling would be desirable for device applications but reproducibility would also be critical. To better understand the coupling, the properties of all 3 ferroic order parameters, elastic, electric, and magnetic, believed to be present in the material across a range of temperatures, are investigated. In high temperature elastic data, an anomaly is observed at the orthorhombic mm2 to tetragonal 4mm transition, Tot = 475 K, and a softening trend is observed as the temperature is increased toward 1300 K, where the material is known to become cubic. Thermal degradation makes it impos- sible to measure elastic behavior up to this temperature, however. In the low temperature region, there are elastic anomalies near ≈40 K and in the range 160–245 K. The former is interpreted as being due to a magnetic ordering transition and the latter is interpreted as a hysteretic regime of mixed rhom- bohedral and orthorhombic structures. Electrical and magnetic data collected below room temperature show anomalies at remarkably similar temperature ranges to the elastic data. These observations are used to suggest that the three order parameters in PZTFT are strongly coupled.
Resumo:
In order to combine the mechanical properties of yttria-stabilised zirconia (ZrO2-3 mol% Y2O3; code Y-ZrO2) with the bioactivity of titania (TiO2), Y-ZrO2-TiO2, green compacts with 0-40vol.% TiO2 were sintered at 1300, 1400, and 1500degreesC for 4h, respectively. The microstructural features such as grains, pores, and phases were examined using scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy dispersive spectroscopy (EDX). The mechanical properties such as hardness and toughness were also determined using the methods of Vickers indentation and Knoop indentation. All the composites showed the major tetragonal Y-ZrO2 phase regardless of the content of the added TiO2. However, rutile TiO2 phase was obtained at 1300degreesC, whereas zirconium titanate (ZrTi04) phase was found at 1400 and 1500degreesC. The Y-ZrO2-ZrTiO4 Composites sintered at 1500degreesC showed relatively high hardness (860-1000 kg/mm(2)) and toughness (4.0-4.5 MPa m(0.5)), whereas the Y-ZrO2-TiO2 composites sintered at 1300degreesC had slightly lower hardness (720-950kg/mm(2)) and fracture toughness (3.1-3.3 MPa m(0.5)). (C) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.