The removal of dyes from textile wastewater: a study of the physical characteristics and adsorption mechanisms of diatomaceous earth

The feasibility of using diatomite for the removal of the problematic reactive dyes as well as basic dyes from textile wastewater was investigated. Methylene blue, Cibacron reactive black and reactive yellow dyes were considered. Physical characteristics of diatomite such as pH(solution), pH(ZPC), surface area, Fourier transform infrared, and scanning electron microscopy were investigated. The surface area of diatomite was found to be 27.80 m(2) g(-1) and the pH(ZPC) occurred around pH of 5.4. The results indicated that the surface charge of diatomite decreased as the pH of the solution increased with the maximum methylene blue removal from aqueous solution occurring at basic pH of around (1011). Adsorption isotherms of diatomite with methylene blue, hydrolysed reactive black and yellow dyes were constructed at different pH values, initial dye concentrations and particle sizes. The experimental results were fitted to the Langmuir, Freundlich, and Henry models. The study indicated that electrostatic interactions play an important role in the adsorption of dyes onto diatomite. A model of the adsorption mechanism of methylene blue onto diatomite is proposed. (C) 2003 Elsevier Ltd. All rights reserved.

COD removal from textile industry effluent: pilot plant studies

This work involved the treatment of industrial waste water from a nylon carpet printing plant. As dyeing of nylon is particularly difficult, acid dyes, fixing agents, thickeners, finishing agents, are required for successful colouration and cause major problems with the plant's effluent disposal in terms of chemical oxygen demand (COD). Granular activated carbon (GAC) Filtrasorb 400 was used to treat a simulated process plant effluent containing all the pollutants. Equilibrium isotherm experiments were established and experimental data obtained showed good empirical correlation with Langmuir isotherm theory. Column experimental data, in terms of COD were correlated using the bed depth service time (BDST) model. Solid phase loading in the columns were found to approach that in equilibrium studies indicating an efficient use of adsorbent. The results from the BDST model were then used to design a pilot adsorption rig at the plant. The performance of the pilot plant column were accurately predicted by scale-up from the bench scale columns. (C) 2001 Elsevier Science BN. All rights reserved.

Textile wastewater treatment using granular activated carbon adsorption in fixed beds

This work involved the treatment of industrial wastewater from a nylon carpet printing plant which currently receives no treatment and is discharged to sea. As nylon is particularly difficult to dye, acid dyes are required for successful coloration and cause major problems with the plant's effluent disposal in terms of color removal. Granular activated carbon Filtrasorb 400 was used to treat a ternary solution of acid dyes and the process plant effluent containing the dyes in a fixed-bed column system. Experimental data were correlated using the bed depth service time (BDST) model to previously published work by the authors for single dye adsorption. The results were expressed in terms of the BDST adsorption capacity, in milligrams of adsorbate per gram of adsorbent, and indicated that there was a 12-25% decrease iri adsorption capacity in the ternary system compared to the single component system; This reduction has been attributed to competitive adsorption occurring in the ternary component system. Dye adsorption from the process plant effluent showed an approximate 65% decrease in adsorption capacity compared to the ternary solution system. This has been attributed to interference caused by the other colorless textile effluent pollutants found in the process wastewater. A chemical oxygen demand analysis on these components indicated that the dyes accounted for only 14% of the total oxygen demand.

The effect of 3D weaving and consolidation on carbon fiber tows, fabrics, and composites

This article investigates the damage imparted on load-bearing carbon fibers during the 3D weaving process and the subsequent compaction behavior of 3D woven textile preforms. The 3D multi-layer reinforcements were manufactured on a textile loom with few mechanical modifications to produce preforms with fibers orientated in the warp, weft, and through-the-thickness directions. Tensile tests were conducted on three types of commercially available carbon fibers, 12k HTA, 6k HTS, and 3k HTS in an attempt to quantify the effect of fiber damage induced during the 3D weaving process on the mechanical and physical performance of the fiber tows in the woven composite. The tests were conducted on fiber tows sampled from different locations in the manufacturing process from the bobbin, through the creel and loom mechanism, to the final woven fabric. Mechanical and physical testing were then conducted to quantify the tow geometry, orientation and the effect of compaction during manufacture of two styles of 3D woven composite by vacuumassisted resin transfer molding (VaRTM).