Fracture Mechanics Analysis of the Dentine-Luting Cement Interface.

The objectives of this study were to determine the fracture toughness of adhesive interfaces between dentine and clinically relevant, thin layers of dental luting cements. Cements tested included a conventional glass-ionomer, F (Fuji I), a resin-modified glass-ionomer, FP (Fuji Plus) and a compomer cement, D (DyractCem). Ten miniature short-bar chevron notch specimens were manufactured for each cement, each comprising a 40 µm thick chevron of lute, between two 1.5 mm thick blocks of bovine dentine, encased in resin composite. The interfacial KIC results (MN/m3/2) were median (range): F; 0.152 (0.14-0.16), FP; 0.306 (0.27-0.37), D; 0.351 (0.31-0.37). Non-parametric statistical analysis showed that the fracture toughness of F was significantly lower (p

Modelling the performance of self-compacting SIFCON of cement slurries containing limestone powder using genetic programming technique

The paper explores the potential of applicability of Genetic programming approach (GP), adopted in this investigation, to model the combined effects of five independent variables to predict the mini-slump, the plate cohesion meter, the induced bleeding test, the J-fiber penetration value, and the compressive strength at 7 and 28 days of self-compacting slurry infiltrated fiber concrete (SIFCON). The variables investigated were the proportions of limestone powder (LSP) and sand, the dosage rates of superplasticiser (SP) and viscosity modifying agent (VMA), and water-to-binder ratio (W/B). Twenty eight mixtures were made with 10-50% LSP as replacement of cement, 0.02-0.06% VMA by mass of cement, 0.6-1.2% SP and 50-150% sand (% mass of binder) and 0.42-0.48 W/B. The proposed genetic models of the self-compacting SIFCON offer useful modelling approach regarding the mix optimisation in predicting the fluidity, the cohesion, the bleeding, the penetration, and the compressive strength.

Quantification of all-ceramic crown margin surface profile from try-in to 1-week post-cementation

To use profilometry to assess the margin surface profile of all-ceramic crowns (ACC’s) at try-in and 1-week after cementation with dual-cured resin (DC, RelyX ARC, 3 M ESPE, St. Paul, MN, USA), self-adhesive dual-cured resin (SADC, RelyX Unicem, 3 M ESPE), light-cured resin (LC, RelyX Veneer, 3 M ESPE) or chemically cured resin-modified glass ionomer (RMGI, RelyX Luting Plus, 3 M ESPE) luting cement. Methods: Forty, sound, extracted, human, premolar teeth underwent a standardised preparation for ACC’s. IPS Empress (Ivoclar-Vivadent, Liechtenstein) crowns of standard dimensions were fabricated and 10 luted with each cement and stored in water for 7 days. Three groups of serial profiles were taken, the first of the tooth preparation, the second of the crown margins at try-in and lastly of the crown margins after cementation and 7 days water storage. Results: There were no significant differences in the crown margin surface profile between the four cement groups at try-in. The change in crown margin position between try-in and post-cementation was significantly greater for DC than for LC and RMGI. SADC was not significantly different to the other cements. There were no significant differences in the crown margin extensions between the four cement groups, however most of the IPS Empress ACC’s in this study were underextended but this was not statistically significant. Conclusions: IPS Empress ACC’s seated more fully with LC and RMGI than with DC cement

Statistical modelling of cement slurries for self compacting SIFCON containing silica fume

This paper reports a study carried out to develop a self-compacting fibre reinforced concrete containing a high fibre content with slurry infiltrated fibre concrete (SIFCON). The SIFCON was developed with 10% of steel fibres which are infiltrated by self-compacting cement slurry without any vibration. Traditionally, the infiltration of the slurry into the layer of fibres is carried out under intensive vibration. A two-level fractional factorial design was used to optimise the properties of cement-based slurries with four independent variables, such as dosage of silica fume, dosage of superplasticiser, sand content, and water/cement ratio (W/C). Rheometer, mini-slump test, Lombardi plate cohesion meter, J-fibre penetration test, and induced bleeding were used to assess the behaviour of fresh cement slurries. The compressive strengths at 7 and 28 days were also measured. The statistical models are valid for slurries made with W/C of 0.40 to 0.50, 50 to 100% of sand by mass of cement, 5 to 10% of silica fume by mass of cement, and SP dosage of 0.6 to 1.2% by mass of cement. This model makes it possible to evaluate the effect of individual variables on measured parameters of fresh cement slurries. The proposed models offered useful information to understand trade-offs between mix variables and compare the responses obtained from various test methods in order to optimise self-compacting SIFCON.

Factorial Design of Cement Slurries Containing Limestone Powder for Self-Consolidating Slurry-Infiltrated Fiber Concrete

Slurries with high penetrability for production of Self-consolidating Slurry Infiltrated Fiber Concrete (SIFCON) were investigated in this study. Factorial experimental design was adopted in this investigation to assess the combined effects of five independent variables on mini-slump test, plate cohesion meter, induced bleeding test, J-fiber penetration test and compressive strength at 7 and 28 days. The independent variables investigated were the proportions of limestone powder (LSP) and sand, the dosages of superplasticiser (SP) and viscosity agent (VA), and water-to-binder ratio (w/b). A two-level fractional factorial statistical method was used to model the influence of key parameters on properties affecting the behaviour of fresh cement slurry and compressive strength. The models are valid for mixes with 10 to 50% LSP as replacement of cement, 0.02 to 0.06% VA by mass of cement, 0.6 to 1.2% SP and 50 to 150% sand (% mass of binder) and 0.42 to 0.48 w/b. The influences of LSP, SP, VA, sand and W/B were characterised and analysed using polynomial regression which identifies the primary factors and their interactions on the measured properties. Mathematical polynomials were developed for mini-slump, plate cohesion meter, J-fiber penetration test, induced bleeding and compressive strength as functions of LSP, SP, VA, sand and w/b. The estimated results of mini-slump, induced bleeding test and compressive strength from the derived models are compared with results obtained from previously proposed models that were developed for cement paste. The proposed response models of the self-consolidating SIFCON offer useful information regarding the mix optimization to secure a highly penetration of slurry with low compressive strength