Imaging domains in BaTiO3 single crystal nanostructures: comparing information from transmission electron microscopy and piezo-force microscopy

This article compares and contrasts information
obtained, using transmission electron microscopy (TEM)
and piezo-force microscopy (PFM), on domain configurations
adopted in single crystal lamellae of BaTiO3, that had
been cut directly from bulk using a focused ion beam
microscope with top and bottom surfaces parallel to
{100}pseudocubic. Both forms of imaging reveal domain
walls parallel to {110}pseudocubic, consistent with sets of 90
domains with dipoles oriented parallel to the two
\001[pseudocubic directions in the plane of the lamellae.
However, the domain width was observed to be dramatically
larger using PFM than it was using TEM. This suggests
significant differences in the surface energy densities
that drive the domain formation in the first place, that could
relate to differences in the boundary conditions in the two
modes of imaging (TEM samples are imaged under high
vacuum, whereas PFM imaging was performed in air).
Attempts were made to map local dipole orientations
directly, using a form of ‘vector’ PFM. However, information
inferred was largely inconsistent with the known
crystallography of the samples, raising concern about the
levels of care needed for accurate interpretation of PFM
images.

Giant energy density in [001]-textured Pb(Mg1/3Nb2/3)O-3-PbZrO3-PbTiO3 piezoelectric ceramics

Pb(Zr,Ti)O-3 (PZT) based compositions have been challenging to texture or grow in a single crystal form due to the incongruent melting point of ZrO2. Here we demonstrate the method for achieving 90% textured PZT-based ceramics and further show that it can provide highest known energy density in piezoelectric materials through enhancement of piezoelectric charge and voltage coefficients (d and g). Our method provides more than similar to 5x increase in the ratio d(textured)/d(random). A giant magnitude of d.g coefficient with value of 59 000 x 10(-15) m(2) N-1 (comparable to that of the single crystal counterpart and 359% higher than that of the best commercial compositions) was obtained. (C) 2013 American Institute of Physics. [http://dx.doi.org/10.1063/1.4789854]

Mapping Irreversible Electrochemical Processes on the Nanoscale: Ionic Phenomena in Li Ion Conductive Glass Ceramics

A scanning probe microscopy approach for mapping local irreversible electrochemical processes based on detection of bias-induced frequency shifts of cantilevers in contact with the electrochemically active surface is demonstrated. Using Li ion conductive glass ceramic as a model, we demonstrate near unity transference numbers for ionic transport and establish detection limits for current-based and strain-based detection. The tip-induced electrochemical process is shown to be a first-order transformation and nucleation potential is close to the Li metal reduction potential. Spatial variability of the nucleation bias is explored and linked to the local phase composition. These studies both provide insight into nanoscale ionic phenomena in practical Li-ion electrolyte and also open pathways for probing irreversible electrochemical, bias-induced, and thermal transformations in nanoscale systems.

Effect of titania addition on yttria-stabilised tetragonal zirconia ceramics sintered at high temperatures

In order to combine the mechanical properties of yttria-stabilised zirconia (ZrO2-3 mol% Y2O3; code Y-ZrO2) with the bioactivity of titania (TiO2), Y-ZrO2-TiO2, green compacts with 0-40vol.% TiO2 were sintered at 1300, 1400, and 1500degreesC for 4h, respectively. The microstructural features such as grains, pores, and phases were examined using scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy dispersive spectroscopy (EDX). The mechanical properties such as hardness and toughness were also determined using the methods of Vickers indentation and Knoop indentation. All the composites showed the major tetragonal Y-ZrO2 phase regardless of the content of the added TiO2. However, rutile TiO2 phase was obtained at 1300degreesC, whereas zirconium titanate (ZrTi04) phase was found at 1400 and 1500degreesC. The Y-ZrO2-ZrTiO4 Composites sintered at 1500degreesC showed relatively high hardness (860-1000 kg/mm(2)) and toughness (4.0-4.5 MPa m(0.5)), whereas the Y-ZrO2-TiO2 composites sintered at 1300degreesC had slightly lower hardness (720-950kg/mm(2)) and fracture toughness (3.1-3.3 MPa m(0.5)). (C) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Static and dynamic degradation of sintered calcium phosphate ceramics

The chemical compositions of calcium phosphate materials are similar to that of bone making them very attractive for use in the repair of critical size bone defects. The bioresorption of calcium phosphate occurs principally by dissolution. To determine the impact of composition and flow conditions on dissolution rates, calcium phosphate tablets were prepared by slip casting of ceramic slips with different ratios of hydroxyapatite (HA) and ß-tricalcium phosphate (ß-TCP). Dissolution was evaluated at pH4 using both a static and dynamic flow regime. Both the composition of the HA:ß-TCP tablet and flow regime noticeably influenced the rate of dissolution; the 50:50 HA:ß-TCP composition demonstrating the greatest level of dissolution, and, exposure of the ceramic specimens to dynamic conditions producing the highest rate of dissolution. Understanding the impact of phase composition and flow condition with respect to the dissolution of calcium phosphate will aid in the development and improvement of materials for bone substitution.

Interlaboratory studies on in vitro test methods for estimating in vivo resorption of calcium phosphate ceramics

A potential standard method for measuring the relative dissolution rate to estimate the resorbability of calcium-phosphate-based ceramics is proposed. Tricalcium phosphate (TCP), magnesium-substituted TCP (MgTCP) and zinc-substituted TCP (ZnTCP) were dissolved in a buffer solution free of calcium and phosphate ions at pH 4.0, 5.5 or 7.3 at nine research centers. Relative values of the initial dissolution rate (relative dissolution rates) were in good agreement among the centers. The relative dissolution rate coincided with the relative volume of resorption pits of ZnTCP in vitro. The relative dissolution rate coincided with the relative resorbed volume in vivo in the case of comparison between microporous MgTCPs with different Mg contents and similar porosity. However, the relative dissolution rate was in poor agreement with the relative resorbed volume in vivo in the case of comparison between microporous TCP and MgTCP due to the superimposition of the Mg-mediated decrease in TCP solubility on the Mg-mediated increase in the amount of resorption. An unambiguous conclusion could not be made as to whether the relative dissolution rate is predictive of the relative resorbed volume in vivo in the case of comparison between TCPs with different porosity. The relative dissolution rate may be useful for predicting the relative amount of resorption for calcium-phosphate-based ceramics having different solubility under the condition that the differences in the materials compared have little impact on the resorption process such as the number and activity of resorbing cells.