RuxNb1-xO2 catalyst for the oxygen evolution reaction in proton exchange membrane water electrolysers

Bimetallic catalyst system of ruthenium oxide (RuO) and niobium oxide (NbO) was prepared using the Adams method and the hydrolysis method. Physical and electrochemical characterizations of the catalysts were studied using X-ray diffraction (XRD), Scanning electron microscopy (SEM), cyclic voltammogram (CV) and polarization measurements. NbO addition to RuO was found to increase the stability of RuO. In Adams method the sodium nitrate was found to be forming complex with NbO at high temperature reaction. This makes Adams method unsuitable for the synthesis of RuO -NbO bimetallic system. Hydrolysis method on other hand does not have this problem. But a proper mixture of two oxides was not obtained in hydrolysis method. A lower crystallite size for bimetallic system was obtained with Adams method compared to hydrolysis method. RuO prepared by Adams method had higher activity compared to the hydrolysis counterpart in electrolyzer operation with nafion membrane. A cell voltage of 1.62 V was obtained with RuO (A) at 1 A/cm. A higher stability for RuNbO(A) compared to RuO(A) was observed in continuous cyclic voltammogram and electrolyzer cell test. Copyright © 2013, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

Investigation into the effect of molybdenum-site substitution on the performance of Sr2Fe1.5Mo0.5O6-δ for intermediate temperature solid oxide fuel cells

In this paper, niobium doping is evaluated as a means of enhancing the electrochemical performance of a Sr₂Fe_1.5Mo_0.5O_6-δ (SFM) perovskite structure cathode material for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications. As the radius of Nb approximates that of Mo and exhibits +4/+5 mixed valences, its substitution is expected to improve material performance. A series of Sr₂Fe_1.5Mo_0.5-xNb_xO_6-δ (x = 0.05, 0.10, 0.15, 0.20) cathode materials are prepared and the phase structure, chemical compatibility, microstructure, electrical conductivity, polarization resistance and power generation are systematically characterized. Among the series of samples, Sr₂Fe_1.5Mo_0.4Nb_0.10O_6-δ (SFMNb_0.10) exhibits the highest conductivity value of 30 S cm^-1 at 550°C, and the lowest area specific resistance of 0.068 Ω cm² at 800°C. Furthermore, an anode-supported single cell incorporating a SFMNb_0.10 cathode presents a maximum power density of 1102 mW cm^-2 at 800°C. Furthermore no obvious performance degradation is observed over 15 h at 750°C with wet H₂(3% H₂O) as fuel and ambient air as the oxidant. These results demonstrate that SFMNb shows great promise as a novel cathode material for IT-SOFCs.