6 resultados para Nb-doped
em QUB Research Portal - Research Directory and Institutional Repository for Queen's University Belfast
Resumo:
The formation of epitaxial BaTiO3/SrTiO3 multilayers; is studied in terms of the growth mechanism by investigating surface morphologies, crystalline orientations, microstructures, and structures of the interfaces, as well as by determining the dielectric properties. Under specific conditions, the epitaxial BaTiO3 films follow a layer-then-island (Stranski-Krastanov) mechanism on SrTiO3 (001)-oriented substrates. In view of actual efforts made to grow epitaxial superlattices involving very thin individual layers of BaTiO3 and/or SrTiO3, we have determined that the BaTiO3 films Of up to 6,nm thickness do not show any defects and have a sharp BaTiO3-on-SrTiO3 interface. On the contrary, SrTiO3-on-BaTiO3 interfaces within multilayers are rough, probably due to the different growth mechanisms of the two different materials, or due to a difference in the morphological stability of the growth surfaces caused by different surface energies of BaTiO3 and SrTiO3 and by different mobilities of the Ba and Sr atoms reaching the SrTi3 and BaTiO3 layers, respectively.
Resumo:
The growth mechanism of epitaxial BaTiO3 films on vicinal Nb-doped SrTiO3 (srTiO(3):Nb) (001) substrate surfaces was studied in terms of surface morphology, crystalline orientation, microstructure, and film/substrate interface. Well-oriented BaTiO3 thin films were grown on SrTiO3 substrates with well-defined terraces by pulsed laser deposition. The regularly terraced TiO2-terminated surfaces of vicinal SrTiO3:Nb (001) substrates were prepared by a definite chemical and thermal treatment. Under our conditions, BaTiO3 seems to grow with a layer-then-island (Stranski-Krastanov) growth mechanism. In order to investigate the orientation and crystallinity of the BaTiO3 films, x-ray diffraction and high-resolution transmission election microscopy were performed. Ferroelectricity of the BaTiO3 films was proved by electrical measurements performed on Pt/BaTiO3/SrTiO3:Nb heterostructures.
Resumo:
Epitaxial BaTiO3 films and epitaxial BaTiO3/SrTiO3 multilayers were grown by pulsed laser deposition on vicinal surfaces of (001)-oriented Nb-doped SrTiO3 (SrTiO3:Nb) single-crystal substrates. Atomic force microscopy was used to investigate the surface topography of the deposited films. The morphology of the films, of the BaTiO3/SrTiO3 interfaces, and of the column boundaries was investigated by cross-sectional high-resolution transmission electron microscopy. Measurements of the dielectric properties were performed by comparing BaTiO3 films and BaTiO3/SrTiO3 multilayers of different numbers of individual layers, but equal overall thickness. The dielectric loss saturates for a thickness above 300 nm and linearly decreases with decreasing film thickness below a thickness of 75 nm. At the same thickness of 75 nm, the thickness dependence of the dielectric constant also exhibits a change in the linear slope both for BaTiO3 films and BaTiO3/SrTiO3 multilayers. This behaviour is explained by the change observed in the grain morphology at a thickness of 75 nm. For the thickness dependence of the dielectric constant, two phenomenological models are considered, viz. a 'series-capacitor' model and a 'dead-layer' model.
Resumo:
The initial growth mechanism of epitaxial BaTiO3 films is studied by combined application of atomic force microscopy, cross sectional high-resolution transmission electron microscopy, and x-ray diffraction. Epitaxial BaTiO3 thin films were grown by pulsed laser deposition on vicinal Nb-doped SrTiO3 (SrTiO3:Nb) (001) substrates with well-defined terraces. X-ray diffraction and cross sectional high-resolution transmission electron microscopy investigations revealed well-defined epitaxial films and a sharp interface between BaTiO3 films and SrTiO3:Nb substrates. The layer-then-island (Stranski-Krastanov mode) growth mechanism observed by analyzing the morphology of a sequence of films with increasing amount of deposited material has been confirmed by microstructure investigations. (C) 2002 American Institute of Physics.
Resumo:
Epitaxial SrBi2Ta2O9 (SBT) thin films with well-defined (001), (116), and (103) orientations have been grown by pulsed laser deposition on (001)-, (011)-, and (111)-oriented Nb-doped SrTiO3 substrates. X-ray diffraction pole figure and phi -scan measurements revealed that the three-dimensional epitaxial orientation relation SBT(001)parallel to SrTiO3(001), and SBT[1(1) over bar 0]parallel to SrTiO3[100] is valid for all cases of SET thin films on SrTiO3 substrates, irrespective of their orientations. Atomic force microscopy images of the c-axis-oriented SET revealed polyhedron-shaped grains showing spiral growth around screw dislocations. The terrace steps of the c-axis-oriented SET films were integral multiples of a quarter of the lattice parameter c of SBT (similar to 0.6 nm). The grains of (103)-oriented SET films were arranged in a triple-domain configuration consistent with the symmetry of the SrTiO3(111) substrate. The measured remanent polarization (2P(r)) and coercive field (2E(c)) of (116)-oriented SBT films were 9.6 muC/cm(2) and 168 kV/cm, respectively, for a maximum applied electric field of 320 kV/cm. Higher remanent polarization (2P(r)=10.4 muC/cm(2)) and lower coercive field (2E(c)=104 kV/cm) than those of SBT(116) films were observed in (103)-oriented SET thin films, and (001)-oriented SET revealed no ferroelectricity along the [001] axis. The dielectric constants of (001)-, (116)-, and (103)-oriented SBT were 133, 155, and 189, respectively. (C) 2000 American Institute of Physics.
Resumo:
Epitaxial BaTiO3 films and BaTiO3/SrTiO3 multilayers were grown by pulsed laser deposition (PLD) on (001)-oriented Nb-doped SrTiO3 (SrTiO3:Nb) substrates. Measurements of the dielectric properties were performed comparing BaTiO3 films and BaTiO3/SrTiO3 multilayers of different number of individual layers, but equal overall thickness. The dielectric loss saturates for a thickness above 300 nm, and linearly decreases with decreasing film thickness below a thickness of 75 nm, and it is independent on the number of multilayers, pointing to some interface effect. The thickness dependence of the dielectric constant of BaTiO3 films and BaTiO3/SrTiO3 multilayers; exhibits a change in the linear slope at a thickness of 75 nm. This behavior is explained by the change observed in the morphology at a thickness of 75 nm. In order to explain the thickness dependence of the dielectric constant, two approaches are considered in this paper, viz. a "series capacitor" model and a "dead layer" model.