The effect of H-2 and the presence of hot-O-(ads) during the decomposition of N2O on platinum

The decomposition of N2O was studied using a silica-supported Pt catalyst. The catalyst was found to exhibit short-lived activity at low temperatures to yield N-2 and O-(ads), the latter remained adsorbed on the surface and poisoned the active sites. Creation of hot-O-(ads) atoms during N2O decomposition is proposed to allow O-2 desorption at intermediate temperatures. Inclusion of H-2 as a reducing agent greatly enhanced the activity and suppressed low temperature deactivation. Simultaneous and sequential pulsing of N2O and H-2 showed that H-2 inclusion with the N2O gas stream produced the greatest activity. A mechanism involving H-(ads) addition to

Low-temperature catalytic decomposition of N2O on platinum and bismuth-modified platinum: identification of active sites

Classification of the active surface sites of platinum catalysts responsible for low temperature N2O decomposition, in terms of steps, kinks and terraces, has been achieved by controlled addition of bismuth to as-received platinum/graphite catalysts.

Abatement of nitrous oxide over natural and iron modified natural zeolites

The natural zeolite obtained from the Sivas-Yavu region in Turkey and iron modified forms were studied for the decomposition of N2O and selective catalytic reduction of N2O with NH3. The natural and iron modified zeolites were characterised by XRD, SEM, H-2-TPR, NH3-TPD and low temperature nitrogen sorption. The effect iron loading, precursor and valency on the catalytic performance of catalysts were studied. The catalytic activity of the zeolites increased up to about 7.0 wt.% Fe. Above this value, the activity decreased as a result of a reduction in the surface area and pore volume of the zeolite. The highest catalytic activity was observed using catalysts prepared with FeCl2 due to the formation of more reducible iron species in the zeolites. When FeSO4 was used as the iron precursor, sulphate remained on the surface even after extensive washing resulting in a decrease in the N2O decomposition activity and a shift the N2O reduction temperature to higher values. Since the natural and iron exchanged natural zeolites prepared using FeCl2 have comparable activity with synthetic zeolites, the offer a promising alternative catalyst for the abatement of N2O, particularly for the selective reduction of N2O with NH3. (C) 2011 Elsevier B.V. All rights reserved.

Sol-gel-entrapped nano silver catalysts-correlation between active silver species and catalytic behavior

Silver colloids prepared by reducing AgNO3 in aqueous solution with sodium citrate were embedded in alumina following two different preparation procedures resulting in samples containing 3 and 5 wt.% silver. Characterization of these materials using TEM. XPS, XAES, CP/MAS NMR, XRD, and adsorption-desorption isotherms of nitrogen showed that embedding the pre-prepared silver colloids into the alumina via the sol-gel procedure preserved the particle size of silver. However, as XAES demonstrates, the catalysts prepared in a sol-gel with a lower amount of water led to embedded colloids with a higher population of Ag+ species. The catalytic behaviors of the resultant catalysts were well correlated with the concentration of these species. Thus, the active silver species of the catalysts containing more Ag+ species selectively converts NO to N-2. However, subsequent thermal aging leads to an enhancement of the conversion of NO parallel to slight alteration of the selectivity with the appearance of low amounts of N2O despite an increase of Ag+ species. Accordingly, an optimal surface Ag-0/Ag+ ratio is probably needed, independently of the size of silver particles. It was found that this optimal ratio strongly depends on the operating conditions during the synthesis route. (C) 2010 Elsevier Inc. All rights reserved.

Cobalt-doped ZnO nanowires on quartz: Synthesis by simple chemical method and characterization

The synthesis of cobalt-doped ZnO nanowires is achieved using a simple, metal salt decomposition growth technique. A sequence of drop casting on a quartz substrate held at 100 degrees C and annealing results in the growth of nanowires of average (modal) length similar to 200 nm and diameter of 15 +/- 4 nm and consequently an aspect ratio of similar to 13. A variation in the synthesis process, where the solution of mixed salts is deposited on the substrate at 25 degrees C, yields a grainy film structure which constitutes a useful comparator case. X-ray diffraction shows a preferred [0001] growth direction for the nanowires while a small unit cell volume contraction for Co-doped samples and data from Raman spectroscopy indicate incorporation of the Co dopant into the lattice; neither technique shows explicit evidence of cobalt oxides. Also the nanowire samples display excellent optical transmission across the entire visible range, as well as strong photoluminescence (exciton emission) in the near UV, centered at 3.25 eV. (C) 2012 Elsevier B.V. All rights reserved.