Reactive dye adsorption onto a novel mesoporous carbon

A new mesoporous carbon (MCSG60) was developed using an inexpensive commercial mesoporous silica gel as a template and sucrose as the carbon source. The surface area, porosity and density of the carbon were determined. The material possesses a high specific surface area and pore volume accessible for most typical aqueous pollutants. The adsorbent material was tested in a batch dye adsorption system. The behaviour of three reactive dyes adsorbed onto MCSG60 was evaluated (Naphthol Blue Black, NBB; Reactive Black 5, RB5; and Remazol Brilliant Blue R, RBBR). The maximum adsorption capacities obtained for the dyes were: 270. mg/g for NBB; 270. mg/g for RB5; and 280. mg/g for RBBR. Kinetic studies indicated that the adsorption process onto the mesoporous carbon was rapid and that equilibrium was reached in less than 1. h for all the dye systems investigated. Further batch experiments showed MCSG60 successfully adsorbed the dyes over a wide pH range and at low adsorbate concentration. The adsorption potential of MCSG60 for dye removal was further evaluated using a fixed-bed adsorption column. © 2013 Elsevier B.V.

Dye adsorption onto mesoporous materials: PH influence, kinetics and equilibrium in buffered and saline media

Mesoporous materials were used as adsorbents for dye removal in different media: non-ionic, buffered and saline. The mesoporous materials used were commercial (silica gel) as well as as-synthesised materials (SBA-15 and a novel mesoporous carbon). Dye adsorption onto all the materials was very fast and the equilibrium was reached before 1h. The pH has a significant influence on the adsorption capacity for the siliceous materials since the electrostatic interactions are the driving forces. However, the influence of the pH on the adsorption capacity of the carbonaceous material was lower, since the van der Waals interactions are the driving forces. The ionic strength has a great impact on the siliceous materials adsorption capacity, being their adsorption capacity in a buffered medium six times higher than the corresponding to a non-ionic medium. Nevertheless, ionic strength does not influence on the dye adsorption on the mesoporous carbon. Overall, the as-synthesised carbon material presents a clear potential to treat dye effluents, showing high adsorption capacity (q_e≈200mg/g) in all the pH range studied (from 3 to 11); even at low concentrations (C_e≈10mg/L) and at short contact times (t_e<30min).

2D Monolayer MoS2–Carbon Interoverlapped Superstructure: Engineering Ideal Atomic Interface for Lithium Ion Storage: Engineering Ideal Atomic Interface for Lithium Ion Storage

A novel strategy for the controlled synthesis of 2D MoS<inf>2</inf>/C hybrid nanosheets consisting of the alternative layer-by-layer interoverlapped single-layer MoS<inf>2</inf> and mesoporous carbon (m-C) is demonstrated. Such special hybrid nanosheets with a maximized MoS<inf>2</inf>/m-C interface contact show very good performance for lithium-ion batteries in terms of high reversible capacity, excellent rate capability, and outstanding cycling stability.

An effective three-dimensional ordered mesoporous ZnCo2O4 as electrocatalyst for Li-O2 batteries

Three-dimensional ordered mesoporous (3DOM) ZnCo₂O₄ materials have been synthesized via a hard template and used as bifunctional electrocatalysts for rechargeable Li-O₂ batteries. The as-prepared ZnCo₂O₄ nanoparticles possess a high specific surface area of 127.2 m² g^-1 and a spinel crystalline structure. The Li-O₂ battery utilizing 3DOM ZnCo₂O₄ shows a higher specific capacity of 6024 mAh g^-1 than that with pure Ketjen black (KB). Moreover, the ZnCo₂O₄-based electrode enables much enhanced cyclability with a smaller discharge-recharge voltage gap than that of the carbon-only cathode. Such excellent catalytic performance of ZnCo₂O₄ could be associated with its larger surface area and 3D ordered mesoporous structure

An effective three-dimensional ordered mesoporous CuCo2O4 as electrocatalyst for Li-O2 batteries

Three-dimensional ordered mesoporous (3DOM) CuCo₂O₄ materials have been synthesized via a hard template and used as bifunctional electrocatalysts for rechargeable Li-O₂ batteries. The characterization of the catalyst by X-ray diffractometry and transmission electron microscopy confirms the formation of a single-phase, 3-dimensional, ordered mesoporous CuCo₂O₄ structure. The as-prepared CuCo₂O₄ nanoparticles possess a high specific surface area of 97.1 m² g^{- 1} and a spinel crystalline structure. Cyclic voltammetry demonstrates that mesoporous CuCo₂O₄ catalyst enhances the kinetics for either oxygen reduction reaction (ORR) or oxygen evolution reaction (OER). The Li-O₂ battery utilizing 3DOM CuCo₂O₄ shows a higher specific capacity of 7456 mAh g^{- 1} than that with pure Ketjen black (KB). Moreover, the CuCo₂O₄-based electrode enables much enhanced cyclability with a 610 mV smaller discharge-recharge voltage gap than that of the carbon-only cathode at a current rate of 100 mA g^{- 1}. Such excellent catalytic performance of CuCo₂O₄ could be associated with its larger surface area and 3D ordered mesoporous structure. The excellent electrochemical performances coupled with its facile and cost-effective way will render the 3D mesoporous CuCo₂O₄ nanostructures as attractive electrode materials for promising application in Li-O₂ batteries.