Fabrication of Ti-Al coatings by mechanical alloying method

By means of the mechanical alloying (MA) method, Al and Ti + Al coatings were deposited on Ti alloy substrates. During the mechano-activation processing, the substrate surface was impacted by a large number of flying balls along with particles of powder. The repeated ball collisions with the substrate resulted in the deposition of powder on its surface. MA technique produced Ti + Al coating with a thickness of 200 µm and Al one with a thickness of 50 µm after 2 h milling at room temperature. The as-synthesized coatings showed structures with high apparent density and free of porosity. The surface morphology of the MA-coatings was very rough. Annealing treatment led to the leveling of this uneven morphology. Annealing at temperatures ranging between 600 °C and 1100 °C gave different aluminide phases on the samples. In the case of Al coating, Al3Ti and Ti3Al compound were observed upon heating up to 1100 °C. In the case of Ti + Al coating, Al3Ti, Al2Ti, TiAl and Ti3Al were formed on the surface.

Microstructure, properties and application of YAl2 intermetallic compound as particle reinforcements

An yttrium aluminum (YAl2) intermetallic compound ingot was prepared in an induction furnace under vacuum. The microstructure of YAl2 ingot was characterized by optical microscopy, scanning electron microscopy, and X-ray diffraction. The load bearing response of YAl2 intermetallic was investigated and compared with SiC ceramic by indentation combined with optical microscopy and scanning electron microscopy. Additionally, the tensile properties of the Mg–Li matrix composites reinforced with ultrafine YAl2 particles fabricated by planet ball milling were tested. The results show that the intermetallic compound ingot in this experiment is composed of a main face-centered-cubic structure YAl2 phase, a small amount of YAl phase, and minor Y and Al-rich phases. YAl2 intermetallic compound has excellent stability and shows better capability in crack resistance than SiC ceramic. The YAl2 intermetallic compound has better deformation compatibility with the Mg–14Li–3Al matrix than SiC reinforcement with the matrix, which leads to the superior resistance to crack for YAl2p/Mg–14Li–3Al composite compared to SiCp/Mg–14Li–3Al composite.