Investigation into the effect of molybdenum-site substitution on the performance of Sr2Fe1.5Mo0.5O6-δ for intermediate temperature solid oxide fuel cells

In this paper, niobium doping is evaluated as a means of enhancing the electrochemical performance of a Sr₂Fe_1.5Mo_0.5O_6-δ (SFM) perovskite structure cathode material for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications. As the radius of Nb approximates that of Mo and exhibits +4/+5 mixed valences, its substitution is expected to improve material performance. A series of Sr₂Fe_1.5Mo_0.5-xNb_xO_6-δ (x = 0.05, 0.10, 0.15, 0.20) cathode materials are prepared and the phase structure, chemical compatibility, microstructure, electrical conductivity, polarization resistance and power generation are systematically characterized. Among the series of samples, Sr₂Fe_1.5Mo_0.4Nb_0.10O_6-δ (SFMNb_0.10) exhibits the highest conductivity value of 30 S cm^-1 at 550°C, and the lowest area specific resistance of 0.068 Ω cm² at 800°C. Furthermore, an anode-supported single cell incorporating a SFMNb_0.10 cathode presents a maximum power density of 1102 mW cm^-2 at 800°C. Furthermore no obvious performance degradation is observed over 15 h at 750°C with wet H₂(3% H₂O) as fuel and ambient air as the oxidant. These results demonstrate that SFMNb shows great promise as a novel cathode material for IT-SOFCs.

High performance cobalt-free Cu1.4Mn1.6O4 spinel oxide as an intermediate temperature solid oxide fuel cell cathode

In this work Cu_1.4Mn_1.6O₄ (CMO) spinel oxide is prepared and evaluated as a novel cobalt-free cathode for intermediate temperature solid oxide fuel cells (IT-SOFCs). Single phase CMO powder with cubic structure is identified using XRD. XPS results confirm that mixed Cu⁺/Cu²⁺ and Mn³⁺/Mn⁴⁺ couples exist in the CMO sample, and a maximum conductivity of 78 S cm⁻¹ is achieved at 800 °C. Meanwhile, CMO oxide shows good thermal and chemical compatibility with a 10 mol% Sc₂O₃ stabilized ZrO₂ (ScSZ) electrolyte material. Impedance spectroscopy measurements reveals that CMO exhibits a low polarization resistance of 0.143 Ω cm² at 800 °C. Furthermore, a Ni-ScSZ/ScSZ/CMO single cell demonstrates a maximum power density of 1076 mW cm⁻² at 800 °C under H₂ (3% H₂O) as the fuel and ambient air as the oxidant. These results indicate that Cu_1.4Mn_1.6O₄ is a superior and promising cathode material for IT-SOFCs.