The synthesis and characterization of nanophase hydroxyapatite using a novel dispersant-aided precipitation method

The synthesis of nanophase hydroxyapatite (nHA) is of importance in the field of biomaterials and bone tissue engineering. The bioactive and osteoconductive properties of nHA are of much benefit to a wide range of biomedical applications such as producing bone tissue engineered constructs, coating medical implants, or as a carrier for plasmid DNA in gene delivery. This study aimed to develop a novel low-temperature dispersant-aided precipitation reaction to produce nHA particles (

Preparation and characterization of Pr0.6Sr0.4FeO3-δ-Ce0.9Pr0.1O2-δ nanofiber structured composite cathode for IT-SOFCs

In this work, Pr_0.6Sr_0.4FeO_3-δ -Ce_0.9Pr_0.1O_2-δ (PSFO-CPO) nanofibers were synthesized by a one-step electrospin technique for use in intermediate-temperature solid oxide fuel cell (IT-SOFC) applications. PSFO-CPO nanofibers were produced with a diameter of about 100nm and lengths exceeding tens of microns. The thermal expansion coefficient (TEC) matches with standard GDC electrolytes and the resulting conductivity also satisfies the needs of IT-SOFCs cathodes. EIS analysis of the nanofiber structured electrode gives a polarization resistance of 0.072Ωcm² at 800°C, smaller than that from the powdered cathode with the same composition. The excellent electrochemical performance can be attributed to the well-constructed microstructure of the nanofiber structured cathode, which promotes surface oxygen diffusion and charge transfer processes. All the results imply that the one-step electrospin method is a facile and practical way of improving the cathode properties and that PSFO-CPO is a promising cathode material for IT-SOFCs.

Fabrication and characterization of SSZ tape cast electrolyte-supported solid oxide fuel cells

A 10 mol%Sc₂O₃, 1 mol%CeO₂ stabilized-ZrO₂ (SSZ) powder was successfully prepared using the sol-gel method. Subsequent SSZ electrolyte pellets were prepared by tape casting technique and sintered at 1400 °C, 1450 °C, 1500 °C, 1550 °C and 1600 °C. These were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS). SSZ showed a pure cubic phase after sintering, the grain size of SSZ increased with the increase of sintering temperature. The SSZ sintered at 1550 °C showed the highest ion conductivity. The maximum power densities of Ni-SSZ/SSZ/La_0.8Sr_0.2MnO_3-δ (LSM)-SSZ single cells sintered at 1550 °C were 0.18, 0.36, 0.51 and 0.72 W cm^-2 at 650, 700, 750 and 800 °C, respectively. The polarization resistance (R_p) of the single cell attained 0.201 Ω cm² at 800 °C.