A low temperature, isothermal gas-phase system for conversion of methane to methanol over Cu-ZSM-5

A low temperature, isothermal, gas-phase, recyclable process is described for the partial oxidation of methane to methanol over Cu–ZSM-5. Activation in NO at 150 °C followed by methane reaction and steam extraction (both at 150 °C) allowed direct observation of methanol at the reactor outlet.

Characterisation and evaluation of novel surfactant bacterial anti-adherent coatings for endotracheal tubes designed for the prevention of ventilator-associated pneumonia.

It is accepted that ventilator-associated pneumonia is a frequent cause of morbidity and mortality in intensive care patients. This study describes the physicochemical properties of novel surfactant coatings of the endotracheal tube and the resistance to microbial adherence of surfactant coated endotracheal tube polyvinylchloride (PVC). Organic solutions of surfactants containing a range of ratios of cholesterol and lecithin (0:100, 25:75, 50:50, 75:25, dissolved in dichloromethane) were prepared and coated onto endotracheal tube PVC using a multiple dip-coating process. Using modulated temperature differential scanning calorimetry it was confirmed that the binary surfactant systems existed as physical mixtures. The surface properties of both surfactant-coated and uncoated PVC, following treatment with either pooled human saliva or phosphate-buffered saline (PBS), were characterised using dynamic contact angle analysis. Following treatment with saliva, the contact angles of PVC decreased; however, those of the coated biomaterials were unaffected, indicating different rates and extents of macromolecular adsorption from saliva onto the coated and uncoated PVC. The advancing and receding contact angles of the surfactant-coated PVC were unaffected by sonication, thereby providing evidence of the durability of the coatings. The cell surface hydrophobicity and zeta potentials of isolates of Staphylococcus aureus and Pseudomonas aeruginosa, following treatment with either saliva or PBS, and their adherence to uncoated and surfactant-coated PVC (that had been pre-treated with saliva) were examined. Adherence of S. aureus and Ps. aeruginosa to surfactant-coated PVC at each successive time period (0.5, 1, 2, 4, 8 h) was significantly lower than to uncoated PVC, the extent of the reduction frequently exceeding 90%. Interestingly, the microbial anti-adherent properties of the coatings were dependent on the lecithin content. Based on the impressive microbial anti-adherence properties and durability of the surfactant coating on PVC following dip coatings, it is proposed that these systems may usefully reduce the incidence of ventilator-associated pneumonia when employed as luminal coatings of the endotracheal tube.

Reduction in gingival overgrowth associated with conversion from cyclosporin A to tacrolimus

Background: Unsightly gingival overgrowth affects many individuals immunosuppressed with cyclosporin A (CsA), Current management involves repeated periodontal surgery and intensive hygienist support. Tacrolimus is an effective alternative immunosuppressive agent for renal transplantation which does not appear to produce gingival enlargement.

Electron/positron collisions with positronium

We report results for e(+/-)-Ps(Is) scattering in the energy range up to 80 eV calculated in 9-state and 30-state coupled pseudostate approximations. Cross-sections are presented for elastic scattering, ortho-para conversion, discrete excitation, ionization and total scattering. Resonances associated with the Ps(n = 2) threshold are also examined and their positions and widths determined. Very good agreement is obtained with the variational calculations of Ward et al. [J. Phys. B 20 (1987) 127] below 5.1 eV. (C) 2004 Elsevier B.V. All rights reserved.

Fabrication of Ti-Al coatings by mechanical alloying method

By means of the mechanical alloying (MA) method, Al and Ti + Al coatings were deposited on Ti alloy substrates. During the mechano-activation processing, the substrate surface was impacted by a large number of flying balls along with particles of powder. The repeated ball collisions with the substrate resulted in the deposition of powder on its surface. MA technique produced Ti + Al coating with a thickness of 200 µm and Al one with a thickness of 50 µm after 2 h milling at room temperature. The as-synthesized coatings showed structures with high apparent density and free of porosity. The surface morphology of the MA-coatings was very rough. Annealing treatment led to the leveling of this uneven morphology. Annealing at temperatures ranging between 600 °C and 1100 °C gave different aluminide phases on the samples. In the case of Al coating, Al3Ti and Ti3Al compound were observed upon heating up to 1100 °C. In the case of Ti + Al coating, Al3Ti, Al2Ti, TiAl and Ti3Al were formed on the surface.